Deformation in Concrete with External CFRP Sheet Reinforcement
Publication: Journal of Composites for Construction
Volume 4, Issue 2
Abstract
A detailed experimental investigation of local and global deformations of tensile-loaded, cracked, rectangular, concrete prisms reinforced with externally bonded carbon fiber reinforced polymer (CFRP) sheets was carried out. High and low modulus sheets were applied using three different thicknesses of epoxy interlayer between the sheet and concrete. It was found that the stiffness of the CFRP sheet had a dominant effect on global tension stiffening, whereas interlayer thickness had a dominant effect on local load transfer and damage formation. Thicker interlayers transferred load into through-cracked concrete over longer transfer zones, thereby increasing the spacing of subsequent cracks in the concrete. The combined effect on global stiffness of changes in transfer zones and crack spacing due to interlayer thickness was negligible. Increasing the stiffness of the CFRP sheet resulted in considerably increased global tension stiffening. Full field strain measurements by moiré interferometry revealed detailed information about local load transfer in the CFRP sheet, epoxy interlayer, and concrete in the vicinity of cracks.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Arduini, M., and Nanni, A. (1997). “Behavior of precracked RC beams strengthened with carbon FRP sheets.”J. Compos. for Constr., ASCE, 1(2), 63–70.
2.
Bakis, C. E., Boothby, T. E., Tripi, J. M., and Nanni, A. (1999). “An optical investigation of damage and load transfer mechanisms in concrete with external FRP sheet reinforcement.” Proc., 8th Int. Symp., Struct. Faults and Repair '99, Engineering Technics Press, Edinburgh, Scotland.
3.
Brosens, K., and Van Gemert, D. (1997). “Anchoring stresses between concrete and carbon fibre reinforced laminates.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 271–278.
4.
“Forca tow sheet technical notes.” (1995). Tonen Corporation. Tokyo, Japan.
5.
Fukuzawa, K., Numao, T., Wu, Z., Yoshizawa, H., and Mitsui, M. (1997). “Critical strain energy release rate of interface debonding between carbon fiber sheet and mortar.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 295–302.
6.
Garden, H. N., and Hollaway, L. C. (1998). “An experimental study of the failure modes of reinforced concrete beams strengthened with prestressed composite plates.” Compos., 29B, 411–424.
7.
Horiguchi, T., and Saeki, N. (1997). “Effect of test methods and quality of concrete on bond strength of CFRP sheet.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 265–270.
8.
Izumo, K., Saeki, N., Asamizu, T., and Shimura, K. (1997). “Strengthening reinforced concrete beams by using prestressed fiber sheets.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 379–386.
9.
Lee, Y. J., Boothby, T. E., Bakis, C. E., and Nanni, A. (1999). “Slip modulus of FRP sheets bonded to concrete.”J. Compos. for Constr., ASCE, 3(4), 161–167.
10.
Maeda, T., Asano, Y., Sato, Y., Ueda, T., and Kakuta, Y. (1997). “A study on bond mechanism of carbon fiber sheet.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 279–286.
11.
Malek, A., Saadatmanesh, H., and Ehsani, M. (1998). “Prediction of failure of R/C beams strengthened with FRP plate due to stress concentration at the plate end.” ACI Struct. J., 95(1), 142–152.
12.
Meier, U. (1997). “Post-strengthening by continuous fiber laminates in Europe.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 41–56.
13.
Parvizi, A., Garrett, K. W., and Bailey, J. E. (1978). “Constrained cracking in glass fibre-reinforced epoxy cross-ply laminates.” J. Mat. Sci., 13, 195–201.
14.
Post, D., Han, B., and Ifju, P. (1994). High sensitivity Moiré, experimental analysis for mechanics and materials. Springer, New York.
15.
Reifsnider, K. L. (1977). “Some fundamental aspects of fatigue and fracture response of composite materials.” Proc., 14th Annu. Meeting of the Soc. of Engrg., Sci., Lehigh University, Bethlehem, Pa., 373–384.
16.
Swamy, R. N., Jones, R., and Bloxham, J. W. ( 1986). “Shear adhesion properties of epoxy resin adhesives.” Adhesion between polymers and concrete, Chapman & Hall, London, 741–755.
17.
Takahashi, Y., Sato, Y., Ueda, T., Maeda, T., and Kobayashi, A. (1997). “Flexural behavior of RC beams with externally bonded carbon fiber sheet.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 327–334.
18.
Van Gemert, D. (1980). “Force transfer in epoxy-bonded steel-concrete joints.” Int. J. Adhesion and Adhesives, 1, 67–72.
19.
Wu, Z., Matsuzaki, T., and Tanabe, K. (1997). “Interface crack propagation in FRP-strengthened concrete structures.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 319–326.
20.
Wu, Z., and Yoshizawa, H. (1998). “Analytical/experimental study on composite behavior in strengthening structures with bonded carbon fiber sheets.” Proc., 8th Japan-U.S. Conf. On Compos. Mat., G. M. Newaz and R. F. Gibson, eds., Technomic Publishing Co., Lancaster, Pa. 907–918.
21.
Yoshizawa, H., and Wu, Z. (1997). “Analysis of debonding fracture properties of CFS strengthened RC member subject to tension.” Proc., 3rd Int. Symp., Non-Metallic (FRP) Reinforcement for Concrete Struct., Vol. 1, Japan Concrete Institute, Tokyo, 287–294.
Information & Authors
Information
Published In
History
Received: Dec 22, 1998
Published online: May 1, 2000
Published in print: May 2000
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.