Early-Age Properties of Cement-Based Materials. I: Influence of Cement Fineness
This article has a reply.
VIEW THE REPLYPublication: Journal of Materials in Civil Engineering
Volume 20, Issue 7
Abstract
The influence of cement fineness on early-age properties of cement-based materials is investigated using a variety of experimental techniques. Properties that are critical to the early-age performance of these materials are tested, including heat release, temperature rise, chemical shrinkage, and autogenous deformation. Measurements of these properties for two cements of widely different fineness are supplemented with other performance measures, specifically acoustic emission measurements to listen for microcracking occurring in high performance mortars and dual-ring paste shrinkage measurements conducted under sealed conditions to assess residual stress development. The measured properties are observed to be quite different for the coarse and the fine cement. The current emphasis on high early-age strength within the construction industry may result in the specification of cements that are more prone to early-age cracking.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The writers would like to thank the Lehigh Portland Cement Co. for providing the two cements used in this study.
References
American Concrete Institute (ACI). (1999). “Hot weather concreting.” ACI 305R-99, Farmington Hills, Mich.
American Concrete Institute (ACI). (2005). “Guide to mass concrete.” ACI 207.IR-05, Farmington Hills, Mich.
American Concrete Institute (ACI). (2008). “Early-age cracking: Causes, measurements, and mitigation.” State-of-the-Art Rep. of ACI Committee 231.
ASTM. (1999a). “Standard practice for mechanical mixing of hydraulic cement pastes and mortars of plastic consistency.” C 305-99, West Conshohocken, Pa.
ASTM. (1999b). “Standard test method for time of setting of hydraulic cement by Vicat Needle.” C 191-99, West Conshohocken, Pa.
ASTM. (1999c). “Standard test method for compressive strength of hydraulic cement mortars (using . or cube specimens).” C 109/C, 109/M-99, West Conshohocken, Pa.
ASTM. (2004a). “Standard practice for estimating concrete strength by the maturity method.” C 1074-04, West Conshohocken, Pa.
ASTM. (2004b). “Standard test method for determining age at cracking and induced tensile stress characteristics of mortar and concrete under restrained shrinkage.” C 1581-04, West Conshohocken, Pa.
ASTM. (2005a). “Standard specification for standard sand.” C 778-05, West Conshohocken, Pa.
ASTM. (2005b). “Standard test method for chemical shrinkage of hydraulic cement paste.” C 1608-05, West Conshohocken, Pa.
ASTM. (2007). “Standard specification for portland cement.” C 150-07, West Conshohocken, Pa.
Baroghel-Bouny, V., Mounanga, P., Khelidj, A., Loukili, A., and Rafai, N. (2006). “Autogenous deformation of cement pastes. Part II. W/C effects, micro-macro correlations, and threshold values.” Cem. Concr. Res., 36, 123–136.
Bentz, D. P. (1997). “Three-dimensional computer simulation of cement hydration and microstructure development.” J. Am. Ceram. Soc., 80(1), 3–21.
Bentz, D. P., Garboczi, E. J., Haecker, C. J., and Jensen, O. M. (1999). “Effects of cement particle size distribution on performance properties of portland cement-based materials.” Cem. Concr. Res., 29, 1663–1671.
Bentz, D. P., and Haecker, C. J. (1999). “An argument for using coarse cements in high performance concretes.” Cem. Concr. Res., 29(4), 615–618.
Bentz, D. P., Jensen, O. M., Hansen, K. K., Olesen, J. F., Stang, H., and Haecker, C. J. (2001). “Influence of cement particle-size distribution on early age autogenous strains and stresses in cement-based materials.” J. Am. Ceram. Soc., 84(1), 129–135.
Bentz, D. P., Lura, P., and Roberts, J. W. (2005). “Mixture proportioning for internal curing.” Concr. Int., 27(2), 35–40.
Bentz, D. P., Peltz, M., and Winpigler, J. (2008). “Early-age properties of cement-based materials: II. Influence of water-to-cement ratio.” J. Mater. Civ. Eng., in review.
Bentz, D. P., and Turpin, R. (2007). “Potential applications of phase change materials in concrete technology.” Cem. Concr. Compos., 29(7), 527–532.
Brewer, H. W., and Burrows, R. W. (1951). “Coarse-ground cement makes more durable concrete.” J. Am. Concr. Inst., 22(5), 353–360.
Burrows, R. W. (1998). “The visible and invisible cracking of concrete.” Monograph No. 11, American Concrete Institute, Farmington Hills, Mich.
Burrows, R. W., Kepler, W. F., Hurcomb, D., Schaffer, J., and Sellers, G. (2004). “Three simple tests for selecting low-crack cement.” Cem. Concr. Compos., 26(5), 509–519.
Cement and Concrete Reference Laboratory. (2007). ⟨http://www.ccrl.us⟩ (June 2007).
Chariton, T., Kim, B., and Weiss, W. J. (2002). “Using passive acoustic energy to quantify cracking in volumetrically restrained cementitious systems.” Proc., 15th EMD Conf. (CD-ROM), ASCE, Restov, Va.
Chariton, T., and Weiss, W. J. (2002). “Using acoustic emission to monitor damage development in mortars restrained from volumetric changes.” Proc., Concrete: Material Science to Application, A Tribute to Surendra P. Shah, P. Balaguru, A. Namaan, and W. J. Weiss, eds., ACI SP-206, 205–218.
Day, R. L. (1992). “The effect of secondary ettringite formation on the durability of concrete: A literature analysis.” Rep. No. RD108, Portland Cement Association, Skokie, Ill.
Geiker, M., and Knudsen, T. (1982). ”Chemical shrinkage of portland cement pastes.” Cem. Concr. Res., 12, 603–610.
Houk, I. E., Jr., Borge, O. E., and Houghton, D. R. (1969). “Studies of autogenous volume change in concrete for Dworshak Dam.” ACI J., 66(45), 560–568.
Jensen, O. M., and Hansen, P. F. (1995). “A dilatometer for measuring autogenous deformation in hardening portland cement paste.” Mater. Struct., 28, 406–409.
Kim, B., and Weiss, W. J. (2003). “Using acoustic emission to quantify damage in restrained fiber reinforced cement mortars.” Cem. Concr. Res., 33(2), 207–214.
Landis, E., and Ballion, L. (2002). “Experiments to relate acoustic energy to fracture energy of concrete.” J. Eng. Mech., 128(6), 698–702.
Pease, B., Neuwald, A., and Weiss, W. J. (2003). “The influence of cement fineness on early age shrinkage in fresh cementitious systems.” Proc., Celebrating Concrete, 329–338.
Powers, T. C. (1935). “Adsorption of water by portland cement paste during the hardening process.” Ind. Eng. Chem., 27, 790–794.
Sant, G., Lura, P., and Weiss, W. J. (2006). “Measurement of volume change in cementitious materials at early ages: Review of testing protocols and interpretation of results.” Transportation Research Record. 1979, Transportation Research Board, Washington, D.C.
Sant, G., Rajabipour, F., Lura, P., and Weiss, J. (2007). “Examining residual stress development in cementitious materials experiencing an early-age expansion.” Proc., 9th CANMET-ACI Int. Conf.—T.C. Holland Symp., 21–29.
Tennis, P. D., and Bhatty, J. I. (2005). “Portland cement characteristics—2004.” Concr. Tech. Today, 26(3), 1–3.
Weiss, J., Lura, P., Rajabipour, F., and Sant, G. (2006). “Performance of shrinkage reducing admixtures at different humidities and at early ages.” ACI Mater. J., accepted for publication.
Information & Authors
Information
Published In
Copyright
© 2008 ASCE.
History
Received: Aug 31, 2007
Accepted: Nov 28, 2007
Published online: Jul 1, 2008
Published in print: Jul 2008
Notes
Note. Associate Editor: Chiara F. Ferraris
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.