Aggregate Effects on Pervious Portland Cement Concrete Static Modulus of Elasticity
Publication: Journal of Materials in Civil Engineering
Volume 19, Issue 7
Abstract
The effects of aggregate gradation, amount, and size on pervious portland cement concrete (PCC) static modulus of elasticity were compared using four different mixtures. A standard mix and three variable mixes using a uniform gradation, increased aggregate amount, and increased aggregate size were used. The effective air void content was determined for each mixture. The compressive strengths and static elastic moduli were determined and compared at equal void contents. For a uniform gradation, the compressive strengths and static elastic moduli appeared to be higher within an optimal range of voids; however, there was no statistically significant difference between the results from the different gradations. An increased aggregate amount resulted in a statistically significant decrease in both compressive strength and static elastic moduli due to the subsequent decrease in paste amount. While the compressive strengths were higher for mixtures containing smaller aggregate sizes, there was no significant difference between the static elastic moduli when different aggregate sizes were used. Further research is needed to understand the effects of aggregate size on the static modulus of elasticity of pervious PCC.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The writers gratefully acknowledge the financial support of the Tennessee Concrete Association. The research team appreciates material donations from Rogers Group, Inc., MBT Degussa, Irving Materials Inc., Builder’s Supply of Cookeville, Tenn., and the TTU Department of Civil and Environmental Engineering. The writers also appreciate the technical assistance of Jeff Holmes, Tim Dunn, Wes Mittlesteadt, and Ben Byard of TTU. The writers would like to thank the TTU Center for Energy Systems Research for administering the project and providing financial assistance.
References
AASHTO. (1998). “Resistance to plastic flow of bituminous mixtures using Marshall apparatus.” AASHTO T 245-97, Standard specifications for transportation materials and methods of sampling and testing Part II tests, 19th Ed., Washington, D.C.
American Concrete Institute (ACI). (2004). “Guide for selecting proportions for no slump concrete.” ACI 211.3-R02, manual of concrete practice (CD-ROM), Farmington Hills, Mich., Appendix 6, 25.
ASTM. (2002a). “Standard practice for capping concrete specimens.” Annual book of ASTM standards, ASTM C 617-98, Vol. 04.02, 314–318.
ASTM. (2002b). “Standard test method for compressive strength of cylindrical concrete specimens.” Annual book of ASTM standards, ASTM C 39-01, Vol. 04.02, West Conshohocken, Pa., 21–25.
ASTM. (2004a). “Standard practice for making and curing concrete test specimens in the laboratory.” Annual book of ASTM standards, ASTM C 192-98, Vol. 04.02, 126–133.
ASTM. (2004b). “Standard specification for fly ash and raw or calcined natural pozzolan for use as a mineral admixture in Portland cement concrete.” Annual book of ASTM standards, ASTM C 618-03, Vol. 04.02, West Conshohocken, Pa., 319–321.
ASTM. (2004c). “Standard specifications for chemical admixtures for concrete.” Annual book of ASTM standards, ASTM C 494-04, Vol. 04.02, West Conshohocken, Pa., 271–279.
ASTM. (2004d). “Standard specifications for concrete aggregates.” Annual book of ASTM standards, ASTM C 33-03, Vol. 04.02, West Conshohocken, Pa., 10–20.
ASTM. (2004e). “Standard test method for sieve analysis of fine and coarse aggregates.” Annual book of ASTM standards, ASTM C 136-01, Vol. 04.02, West Conshohocken, Pa., 84–88.
ASTM. (2004f). “Standard test method for static modulus of elasticity and Poisson’s ratio of concrete in compression.” Annual book of ASTM standards, ASTM C 469-94, Vol. 04.02, West Conshohocken, Pa., 256–260.
ASTM. (2005a). “Standard specification for portland cement.” Annual book of ASTM standards, ASTM C 150-04a, Vol. 04.01, West Conshohocken, Pa., 144–151.
ASTM. (2005b). “Standard test method for effective porosity and effective air voids of compacted bituminous paving mixture samples.” ASTM D 7063-05, West Conshohocken, Pa., 1–4.
Cetin, A., and Carrasquillo, R. (1998). “High-performance concrete: Influence of coarse aggregates on mechanical properties.” ACI Mater. J., 95(3), 252–261.
Ghafoori, N., and Dutta, S. (1995). “Laboratory investigation of compacted no-fines concrete for paving materials.” J. Mater. Civ. Eng., 7(3), 183–191.
Kevern, J., Wang, K., Suleimam, M., and Schaefer, V. (2005). “Mix design development for pervious concrete in cold weather climates.” 2005 Mid-Continent Transportation Research Symp., Iowa State Univ., Ames, Iowa.
Marolf, A., Neithalath, N., Sell, E., Wegner, K., Weiss, W. J., and Olek, J. O. (2004). “The influence of aggregate size and gradation on acoustic absorption of enhanced porosity concrete.” ACI Mater. J., 101(1), 82–91.
Marotta, T. (2005). “Aggregates.” Basic construction materials, 7th Ed., Pearson, Upper Saddle River, N.J., Chap. 2, 65.
Meininger, R. C. (1988). “No-fines pervious concrete for paving.” Concr. Int., 10(8), 20–27.
Mindess, S., Young, J., and Darwin, D. (2003). “Aggregates.” Concrete, 2nd Ed., Pearson, Upper Saddle River, N.J., Chap. 7, 125.
Neville, A. (1997). “Aggregate and bond modulus of elasticity of concrete.” ACI Mater. J., 94(1), 71–74.
Oluokon, F., Burdette, E., and Deatherage, J. (1991). “Elastic modulus, Poisson’s ratio, and compressive strength relationships at early ages.” ACI Mater. J., 88(1), 3–10.
Pasko, T., Jr. (1998). “Concrete pavements—Past, present, and future.” Public Roads, 62(1), 7–15.
Sideris, K., and Manita, P. (2004). “Estimation of ultimate modulus of elasticity and Poisson ratio of normal concrete.” Cem. Concr. Compos., 26(6), 623–631.
Wu, K., Chen, B., Yao, W., and Zhang, D. (2001). “Effect of coarse aggregate type on mechanical properties of high-performance concrete.” Cem. Concr. Res., 31(10), 1421–1425.
Yang, J., and Jiang, G. (2003). “Experimental study on properties of pervious concrete pavement materials.” Cem. Concr. Res., 33(3), 381–386.
Information & Authors
Information
Published In
Copyright
© 2007 ASCE.
History
Received: Jan 11, 2006
Accepted: Dec 28, 2006
Published online: Jul 1, 2007
Published in print: Jul 2007
Notes
Note. Associate Editor: Baoshan Huang
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.