Multiple Cracking and Fiber Bridging Characteristics of Engineered Cementitious Composites under Fatigue Flexure
Publication: Journal of Materials in Civil Engineering
Volume 16, Issue 5
Abstract
The flexural fatigue characteristics of two different shotcreted engineered cementitious composites (ECCs) containing polyvinyl alcohol (PVA) and polyethylene (PE) fibers respectively were tested under four-point bending. The failure mechanisms and characteristics were investigated in comparison with a shotcreted steel fiber reinforced cement. The results showed that both ECCs exhibited a unique fatigue stress–life relationship that is represented by a bilinear function on a semilogarithmic scale. The failure mechanism of ECCs involved the development of multiple cracks, and the number of cracks was higher when the fatigue stress level was higher. The difference in crack opening displacement results from their different fiber bridging characteristics. PVA fibers tended to break under fatigue, while PE fibers tended to pullout. Although PE-ECC provided more cracks at the same fatigue stress, level, PVA-ECC showed larger deformation than PE-ECC because each crack width of PE-ECC was smaller than that of PVA-ECC. The deformation is shown to be governed by the number of cracks as well as the crack width, where the fiber bridging characteristics are related to either fiber rupture or fiber pullout.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Bannantine, J.A., Comer, J.J., and Handrock, J.L. ( 1990). Fundamentals of metal fatigue analysis. Prentice–Hall, Englewood Cliffs, N.J.
2.
Balaguru, P.N., and Shah, S.P. ( 1992). “Fiber-reinforced cement composites.” McGraw–Hill, New York.
3.
Franzen, T. (1992). “Shotcrete for underground support-A state of the art report with focus on steel-fiber reinforcement.” Tunn. Undergr. Space Technol., 7(4), 383–391.
4.
Horii, H., Nanakorn, P., and Kabele, P. ( 1995). “Application of fracture mechanics to design of SFRC tunnel linings and development of strain-hardening cementitious composites.” Fracture Mechanics of Concrete Structures, Proc., FRAMCOS, F. H. Wittmanned. AEDIFICATIO. 2(2), 1345–1360.
5.
Japan Concrete Institute (JCI). ( 1984). “JCI standards for test methods of fiber reinforced concrete.” Tokyo. 45–48.
6.
Kanda, T., and Li, V. C. (1999). “New micromechanics design theory for pseudostrain hardening cementitious composite.” J. Eng. Mech., 125(4), 373–381.
7.
Kanda, T., and Li, V. C., (2001). “Practical design guidelines for pseudostrain hardening cementitious composites reinforced with short random fibers.-I: Micromechanics theory for predicting first cracking strength.” J. Struct. Construct. Eng., AIJ, 539, 13–21 (in Japanese).
8.
Kanda, T., Saito, T., Sakata, N., and Hiraishi, M. ( 2001). “Fundamental properties of direct sprayed retrofit material utilizing fiber reinforced pseudostrain hardening cementitious composites.” Proc., Japan Concrete Institute, JCI, Hokkaido, Japan, 23(1), 475–480 (in Japanese).
9.
Li, V. C. (1993). “From micromechanics to structural engineering-The design of cementitious composites for civil engineering application.” J. Struct. Mech. Earthquake Eng., JSCE, Tokyo. 10(2), 37–48.
10.
Li, V. C. (2002). “Large volume, high-performance applications of fibers in civil engineering.” J. Appl. Polym. Sci., 83(3), 660–686.
11.
Li, V. C., and Wu, H. C. (1992). “Conditions for pseudostrain hardening in fiber reinforced brittle matrix composites.” Appl. Mech. Rev., 45(8), 390–398.
12.
Li, V. C., and Matsumoto, T. (1998). “Fatigue crack growth analysis of fiber reinforced concrete with effect of interfacial bond degradation.” J. Cem. Concr. Compos., 20(5), 339–351.
13.
Maalej, M., and Li, V. C. (1995). “Effect of fiber rupture on tensile properties of short fiber composites.” J. Eng. Mech., 121(8), 903–913.
14.
Matsumoto, T. ( 1998). “Fracture mechanics approach to fatigue life of discontinuous fiber reinforced composites.” PhD thesis, Dept. of Civil and Environmental Engineering, Univ. of Michigan, Ann Arbor, Mich.
15.
Matsumoto, T., and Li, V. C. (1999). “Fatigue life analysis of fiber reinforced concrete with a fracture mechanics based model.” J. Cem. Concr. Compos., 21(4), 249–261.
16.
Matsumoto, T., Suthiwarapirak, P., and Asamoto, S. ( 2002). “Model development of ECC fatigue analysis.” Proc., Japan Concrete Institute, JCI, Ibaraki, Japan, 24(1), 237–242 (in Japanese).
17.
Morgan, D.R. ( 1994). “New developments in shotcrete for repairs and rehabilitation.” Advances in concrete technology, 2nd Ed., CANMET, 675–719.
18.
Shah, S. P., and Rangan, B. V. (1971). “Fiber reinforced concrete properties.” ACI J., 68(2), 126–135.
19.
Suthiwarapirak, P., Matsumoto, T., and Kanda, T. (2002). “Flexural fatigue failure characteristics of an engineered cementitious composite and polymer cement mortar.” J. Mater. Concrete Struct. Pave., JSCE, Tokyo, 718(57), 121–134.
Information & Authors
Information
Published In
Copyright
Copyright © 2004 ASCE.
History
Received: Dec 23, 2002
Accepted: Nov 14, 2003
Published online: Oct 1, 2004
Published in print: Oct 2004
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.