Performance of Repair Materials Exposed to Fluctuation of Temperature
This article has a reply.
VIEW THE REPLYPublication: Journal of Materials in Civil Engineering
Volume 7, Issue 1
Abstract
The repair performance of resinous and cementitious materials exposed to static and fluctuating temperature conditions has been evaluated in this study, which is of importance for the repair of concrete structures in the Arabian Gulf region. Specimens were exposed to a total of 90 thermal cycles between 25°C and 70°C, simulating the temperature variation of concrete surfaces on typical summer days in the Arabian Gulf region. The slant shear bond strengths as well as failure characteristics have been observed at 0, 60, and 90 cycles. The results show that the shear slant bond strength undergoes significant reduction with thermal fluctuations due to the thermal incompatibility between the concrete and the repair materials. It is found that for resinous materials the reduction varied from 9.3–20.47% for 60 cycles, and from 18.98–36.43% for 90 thermal cycles. For the cementitious materials, the corresponding values were 3.2–17.46% for 60 cycles, and 8.07–34.80% for 90 cycles. It is also seen, in general, that the mode of failure of the test specimens changed from crushing of concrete to combined crushing-joint failure at 60 cycles, and then to a distinct joint failure at 90 thermal cycles.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Chou, G. K.(1984). “Cathodic protection: an emerging solution to the rebar corrosion problem.”Concrete Const., 29(6), 561.
2.
Durability of concrete bridge decks. (1979). NCHRP 57, Transportation Research Board, Washington, D.C.
3.
Halstead, S., and Woodworth, L. A. (1955). “The deterioration of reinforced concrete structures under coastal conditions.”Trans., South African Instn. of Civ. Engrs., 115–134.
4.
Harboe, E. M. (1982). “Long-time studies and field experiences with sulfate attack.” Sufate Resistance of Concrete, SP-77, American Concrete Institute (ACI), 1–20.
5.
Hobbs, S. W. (1984). “Expansion of concrete due to alkali-silica reaction.”The Struct. Engr., London, England, 62A(1), 26.
6.
Hamilton, J. J., and Handegord, G. O. (1968). “The performance of ordinary portland cement concrete in prairie soils of high sulfate content.”Performance of Concrete, E. G. Swenson, ed., Univ. of Toronto Press, Toronto, Canada, 135–158.
7.
Jaegermann, C. H., Ravina, D., and Pundak, B. (1971). “Accelerated curing of concrete by solar radiation.”Concrete and Reinforced Concrete in Hot Countries: Proc., Int. RILEM Symp., Vol. II, 339–362.
8.
Kliger, P., Monfore, G., Stark, D., and Teske, W. (1974). “D-cracking of concrete pavements in Ohio.”Final Rep., Portland Cement Assoc., Skokie, Ill.
9.
Macmillan, G. L. (1984). “Concrete specifications—development by investigation and research.” Al-Mohandis, Bahrain Soc. of Engrg., Bahrain, 36.
10.
Mironov, S. A., Malinskyi, E. N., and Vakhitov, M. M. (1982). “Durability assessment criterion for concrete exposed to dry hot climate conditions.”Durability of building materials. Elsevier Scientific Publishing Co., Amsterdam, The Netherlands, No. 1, 3–14.
11.
Monson, J. F.(1984). “Parking garage repaired using thin polymer concrete overlay.”Concrete Int., 6(7), 7.
12.
O'Brien, T. P. (1980). “Concrete deterioration and repair.”Proc., The Instn. of Civ. Engrs., Part 1, London, England, Vol. 68, 399.
13.
Rasheeduzzafar, Al-Saadoun, S. S., Al-Gahtani, A. S., Dakhil, F. H., and Bader, M. A. (1989). “A repair strategy for corrosion damaged concrete.”Proc., 3rd Int. Conf. on Deterioration and Repair of Reinforced Concrete in the Arabian Gulf, Bahrain Soc. of Engrg., Bahrain, Vol. 1, 35–57.
14.
Rasheeduzzafar, Dakhil, and F. H., and Al-Gahtani(1984). “The deterioration of concrete structures in the environment of the Middle East.”ACI J., 81(1), 13–20.
15.
Rasheeduzzafar, Dakhil, and F. H., and Al-Gahtani(1985). “Corrosion of reinforcement in concrete structures in the Middle East.”Concrete Int., 7(9), 48–55.
16.
“Repairing a parking structure.” (1985). Concrete Int., 7(10), 43.
17.
Seki, H. (1975). “Deterioration of concrete of coastal structures in Japan.”SP 47-13, American Concrete Institute (ACI), 293–316.
18.
Tabor, L. J.(1978). “The evaluation of resin systems for concrete repair.”Mag. of Concrete Res., 30(15), 221–225.
Information & Authors
Information
Published In
Copyright
Copyright © 1995 American Society of Civil Engineers.
History
Published online: Feb 1, 1995
Published in print: Feb 1995
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.