Stress‐Cracking Resistance of High‐Density Polyethylene Geomembranes
Publication: Journal of Geotechnical Engineering
Volume 119, Issue 11
Abstract
A new index test method, the notched constant tensile load (NCTL) test, for evaluating high‐density polyethylene (HDPE) geomembranes regarding stress‐cracking resistance is presented in this paper. Eighteen commercially virgin geomembranes and 7 field‐exhumed geomembranes were evaluated using the new test. Results show a wide variation in the onset of the transition time. For the 18 virgin geomembranes, the transition times range from 10 hours to 5,000 hours. In addition, all 7 field‐exhumed geomembranes, where failure actually occurred, show transition times less than 100 hours. An evaluation of the test results leads to a tentative recommendation that the transition time for an acceptable HDPE geomembrane should be 100 hours or longer. A comparison between the results of NCTL test and the currently used ASTM D 1693 bent‐strip test was conducted. It indicates that the bent‐strip test cannot adequately evaluate stress cracking resistance, and that the NCTL test is a more critical test in the assessment of such behavior.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Ayres, R. L. (1987). “Basic structure/property relationship for PE pipe resins.” Tenth Plastic Fuel Gas Pipe Symp., American Gas Association, Arlington, Va., 2–8.
2.
Brown, N., Donofrio, J., and Lu, X. (1987). “The transition between ductile and slow crack‐growth failure in polyethylene.” Polymer, 28(8), 1326–1330.
3.
“Definitions of terms relating to plastics.” (1993). ASTM D 883, Vol. 08.01, ASTM, Philadelphia, Pa.
4.
Fisher, G. E. (1989). “Controlling thermal damage in flexible membrane liners.” Geotech. Fabrics Report, 7(2), 39–41.
5.
“Flexible membrane liners.” (1991). Standard #54, Nat. Sanitation Foundation, Ann Arbor, Mich.
6.
GRI Test Method, GM5, Notched constant tensile load (NCTL) test for polyolefin resins or geomembranes. (1991). Geosynthetic Res. Inst., Drexel Univ., Philadelphia, Pa.
7.
Halse, Y. H., Koerner, R. M., and Lord, A. E. (1990). “Stress cracking morphology of polyethylene (PE) geomembrane seams.” Geosynthetics: Microstructure and Performance, ASTM STP 1076, I.D. Peggs, ed., ASTM, Philadelphia, Pa., 78–89.
8.
Hsuan, Y. G., Lord, A. E., and Koerner, R. M. (1991). “Effect of outdoor exposure on a high density polyethylene geomembrane.” Geosynthetics' 91 Conf., Industrial Fabrics Association Inc., St. Paul, Minn., 287–302.
9.
Hsuan, Y. G., Koerner, R. M., and Lord, A. E. (1992). “Notched constant tensile load (NCTL) test for high density polyethylene geomembranes.” ASTM Geotech. Testing J., submitted.
10.
Jagielski, K. (1990). “Geomembrane market report: A solution that ensures growth.” Geotech. Fabrics Report, 8(6), 27–29.
11.
Lander, L. L. (1960). “Environmental stress rupture of polyethylene.” SPE J., VI, 1329–1332.
12.
Lustiger, A. (1983). “The molecular mechanism of slow crack growth in polyethylene.” Eighth Plastic Fuel Gas Pipe Symp., American Gas Association, Arlington, Va., 54–56.
13.
Lu, X. C., and Brown, N. (1990). “The ductile‐brittle transition in a polyethylene copolymer.” J. Mater. Sci., 25(IA), 29–34.
14.
Lu, X., Qian, R., and Brown, N. (1991). “Notchology—the effect of the notching method on the slow crack growth failure in a tough polyethylene.” J. Mater. Sci., 26(4), 881–888.
15.
Peggs, I. D., and Carlson, D. S. (1989). “Stress cracking of polyethylene geomembrane seams: field experience.” Durability and Aging of Geosynthetics, R. M. Koerner, ed., Elsevier Science Publishers Ltd., London, England, 195–211.
16.
Petermann, J., Miles, M., and Gleiter, H. (1976). “Growth of polymer crystals during annealing.” J. Macromol. Sci. Phys., B12(3), 393–404.
17.
Plastic pipe line. (1982). Gas Res. Inst., 3(2), 3.
18.
Preliminary assessment of stress cracking of polyethylene liners. (1989). Envir. Protection Agency, Cincinnati, Ohio.
19.
Stress crackng behavior of high density polyethylene geomembranes and its minimization. (1992). EPA, Cincinnati, Ohio.
20.
“Test method for environmental stress rupture of type III polyethylenes under constant tensile load.” (1988). ASTM D 2552, Vol. 08.02, ASTM, Philadelphia, Pa.
21.
“Test method for environmental stress‐cracking of ethylene plastics.” (1993a). ASTM D 1693, Vol. 08.02, ASTM, Philadelphia, Pa.
22.
“Test method for tensile‐impact energy to break plastic and electrical insulating materials.” (1993b). ASTM D 1822, Vol. 08.02, ASTM, Philadelphia, Pa.
23.
Williams, J. G. (1987). Fracture mechanics of polymers. John Wiley and Sons, New York, N.Y.
Information & Authors
Information
Published In
Copyright
Copyright © 1993 American Society of Civil Engineers.
History
Received: Oct 27, 1992
Published online: Nov 1, 1993
Published in print: Nov 1993
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.