Plasticity Model for Concrete under Triaxial Compression
Publication: Journal of Engineering Mechanics
Volume 127, Issue 3
Abstract
Using the experimental background of 130 triaxial tests conducted on cylindrical specimens, a plasticity-based constitutive model of concrete behavior is developed. Parameters of the reference experimental database include the water:cement ratio (i.e., , degree of saturation at testing, and load path used in the tests. In the model, damage is quantified by the volumetric expansion that builds up progressively in the material as it approaches failure and is caused by propagation of microcracks. This behavioral index is calibrated with reference to the available tests and subsequently used as the primary state variable in the model, determining for any stress state the degree of stiffness and strength degradation and the ductility in the response. Because failure is modeled as a damage-driven continuous process rather than a distinct event, the characteristic failure envelope is expanding (hardening) or contracting (softening) as a function of a scalar measure of plastic deformation. A nonassociated plastic flow rule calibrated against the experiments is used to describe the direction of plastic deformation. The model was tested against published triaxial test series and empirical confinement models. It was also used in the context of a finite-element formulation to study the mechanical behavior of reinforced-concrete circular columns. This particular test problem was selected because it is a real-life example of the experimental conditions used to derive the model.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Ansari, F., and Li, Q. ( 1998). “High-strength concrete subjected to triaxial compression.” ACI Mat. J., 95(6), 747–755.
2.
Chen, W. F. ( 1982). Plasticity in reinforced concrete, McGraw-Hill, New York.
3.
Elwi, A. A., and Murray, D. W. (1979). “Constitutive model for concrete structures.”J. Engrg. Mech. Div., ASCE, 105(4), 623–641.
4.
Finite element analysis of reinforced concrete: State-of-the-art report. (1982). ASCE, New York.
5.
Hsieh, S. S., Ting, E. C., and Chen, W. F. ( 1988). “Applications of a plastic-fracture model to concrete structures.” Comp. and Struct., 28(3), 373–393.
6.
Imran, I. ( 1994). “Applications of non-associated plasticity in modeling the mechanical response of concrete.” PhD thesis, Dept. of Civ. Engrg., University of Toronto, Toronto.
7.
Imran, I., and Pantazopoulou, S. ( 1996). “Experimental study of plain concrete under triaxial stress.” ACI Mat. J., 93(6), 589–601.
8.
Jansen, D. C., and Shah, S. P. (1997). “Effect of length on compressive strain softening of concrete.”J. Engrg. Mech., ASCE, 123(1), 25–35.
9.
Lade, P. V. ( 1988). “Effects of voids and volume changes on the behavior of frictional materials.” Int. J. Numer. and Analytical Methods in Geomech., 12, 351–370.
10.
Launay, P., and Gachon, H. ( 1972). “Strain and ultimate strength of concrete under triaxial stress.” ACI SP 34-13, American Concrete Institute, Detroit, 269–282.
11.
Li, Q., and Ansari, F. (1999). “Mechanics of damage and constitutive relationships for high strength concrete in triaxial compression.”J. Engrg. Mech., ASCE, 125(1), 1), 1–10.
12.
Mander, J. B., Priestley, M. J. N., and Park, R. (1988). “Theoretical stress-strain model for confined concrete.”J. Struct. Engrg., ASCE, 114(8), 1804–1826.
13.
Mirmiran, A., and Shahawy, M. (1997). “Behavior of concrete columns confined by fiber composites.”J. Struct. Engrg., ASCE, 123(5), 583–590.
14.
Mitchell, G. P., and Owen, D. R. J. ( 1988). “Numerical solutions for elastic-plastic problems.” Eng. Comput., 5(4), 274–284.
15.
Mizuno, E., and Hatanaka, S. (1992). “Compressive softening model for concrete.”J. Engrg. Mech., ASCE, 118(8), 1546–1563.
16.
Ohtani, Y., and Chen, W. F. ( 1989). “A plastic-softening model for concrete materials.” Comp. and Struct., 33(4), 1047–1055.
17.
Pantazopoulou, S. J., and Mills, R. ( 1995). “Microstructural aspects of the mechanical response of plain concrete.” ACI Mat. J., 92(6), 605–616.
18.
Peterson, P. E. ( 1981). “Crack growth and development of fracture zones in plain concrete and similar materials.” Rep. No. TVBM-1106, Div. of Build. Mat., University of Lund, Lund, Sweden.
19.
Reinhardt, H. W. ( 1984). “Fracture mechanics of an elastic softening material like concrete.” Heron, TNO Building and Construction Research, Delft, The Netherlands, 29(2), 1–42.
20.
Richart, F. E., Brandtzaeg, A., and Brown, R. L. ( 1928). “A study of the failure of concrete under combined compressive stresses.” Engrg. Experiment Station Bull. No. 185, University of Illinois, Urbana, Ill.
21.
Sheikh, S. A., and Toklucu, M. T. ( 1993). “Reinforced concrete columns confined by circular spirals and hoops.” ACI Struct. J., 90(5), 542–553.
22.
Smith, S. S., William, K. J., Gerstle, K. H., and Sture, S. ( 1989). “Concrete over the top, or: Is there life after peak?” ACI Mat. J., 86(5), 491–497.
23.
Toutanji, H. A. ( 1999). “Stress-strain characteristics of concrete columns externally confined with advanced fiber composite sheets.” ACI Mat. J., 96(3), 397–404.
24.
Van Mier, J. G. M. ( 1986). “Fracture of concrete under complex stress.” Heron, 31(3), 1–90.
25.
Xie, J., Elwi, A. E., and MacGregor, J. G. ( 1995). “Mechanical properties of three high-strength concretes containing silica fume.” ACI Mat. J., 92(2), 135–145.
26.
Zienkiewicz, O. C., and Taylor, R. L. ( 1989). The finite element method, Vol. 1, McGraw-Hill, New York.
Information & Authors
Information
Published In
Journal of Engineering Mechanics
Volume 127 • Issue 3 • March 2001
Pages: 281 - 290
History
Received: Jan 3, 2000
Published online: Mar 1, 2001
Published in print: Mar 2001
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.