Crack Growth and Lifetime of Concrete under Long Time Loading
Publication: Journal of Engineering Mechanics
Volume 123, Issue 4
Abstract
Edge-notched eccentrically compressed fracture specimens made of aggregate of reduced size are loaded in standard creep test frames. Measurements of the time rate of crack mouth opening in notched concrete specimens subjected to constant load of almost one month duration are reported and analyzed. To reveal the size effect, geometrically similar specimens of four sizes in the ratio 1:2:4:8 are tested. The results are successfully described by a previously proposed time-dependent generalization of the R-curve model, in which the rate of crack growth is a function of the ratio of the stress intensity factor to the R-curve, and linear aging viscoelastic creep in the bulk of the specimen is treated according to the operator method. Good predictions are also obtained with a simplified method in which the R-curve is replaced by a constant asymptotic value of the critical stress intensity factor and creep is handled in similarity to the effective modulus method, neglecting the history effect. The time curves of crack opening terminate with an infinite slope, indicating the lifetime. The finiteness of the lifetime is not caused by creep, but by time-dependent crack growth, which dominates the final stage of crack opening. The initial stage of crack opening, on the other hand, is dominated by creep. Tests are conducted both for concretes of normal strength of 33.4 MPa (4,847 psi) in compression and relatively high strength of 46.4 MPa (6,442 psi). For the stronger concrete, the lifetimes are found to be longer. An increase of specimen size is found to decrease the lifetime. Since the same type of model was previously shown capable of describing all other known time-dependent fracture phenomena in concrete, a rather general applicability may be expected.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Barenblatt, G. I.(1959). “The formation of equilibrium cracks during brittle fracture—general ideas and hypothesis, axially symmetric cracks.”Prikl. Math. Mekh., 23(3), 434–444.
2.
Barsoum, R.(1976). “On the use of isotropic finite elements in linear fracture mechanics.”Int. J. Numer. Methods in Engrg., 10, 25–37.
3.
Bažant, Z. P. (1995). “Creep and damage in concrete.”Materials Science of Concrete IV, J. Skalny and S. Mindess, eds., Am. Ceramic. Soc., Westerville, Ohio, 355–389.
4.
Bažant, Z. P. (1983). “Fracture in concrete and reinforced concrete.”Preprint, IUTAM Prager Symp. on Mech. of Geomat.: Rocks, Concrete, Soil, Z. P. Bažant, ed., Int. Union on Theoretical and Appl. Mech., 281–316.
5.
Bažant, Z. P.(1984). “Size effect in blunt fracture: Concrete, rock and metal.”J. Engrg. Mech., ASCE, 110(4), 518–535.
6.
Bažant, Z. P. (1993). “Current status and advances in the theory of creep and interaction with fracture.”Proc., 5th Int. RILEM Symp. on Creep and Shrinkage of Concrete (ConCreep 5), Z. P. Bažant and I. Carol, eds., E & FN Spon, London, U.K., 291–307.
7.
Bažant, Z. P., Bai, S.-P., and Gettu, R.(1993). “Fracture of rock: Effect of loading rate.”Engrg. Fracture Mech., 45(3), 393–398.
8.
Bažant, Z. P., and Cedolin, L. (1991). Stability of structures: Elastic, inelastic, fracture and damage theories. Oxford University Press, New York, N.Y.
9.
Bažant, Z. P., and Gettu, R. (1989). “Determination of nonlinear fracture characteristics and time dependence from size effect.”Fracture of concrete and rock: Recent developments, S. P. Shah, S. E. Swartz, and B. Barr, eds., Elsevier, London, U.K., 549–565.
10.
Bažant, Z. P., and Gettu, R. (1992). “Rate effects and load relaxation in static fracture of concrete.”ACI Mat. J., 89(Sept.), 456–467.
11.
Bažant, Z. P., Gu, W.-H., and Faber, K. T.(1995). “Softening reversal and other effects of a change in loading rate on fracture of concrete.”ACI Mat. J., 92, 3–9.
12.
Bažant, Z. P., and Jirásek, M.(1993). “R-curve modeling of rate and size effects in quasibrittle fracture.”Int. J. Fracture, 62, 355–373.
13.
Bažant, Z. P., and Kazemi, M. T.(1990). “Determination of fracture energy, process zone length and brittleness number from size effect, with application to rock and concrete.”Int. J. Fracture, 44, 111–131.
14.
Bažant, Z. P., and Li, Y.-N. (1995a). “Stability of cohesive crack model: Part I—Energy principles.”J. Appl. Mech., 62(Dec.), 959–964.
15.
Bažant, Z. P., and Li, Y.-N. (1995b). “Stability of cohesive crack model: Part II—Eigenvalue analysis of size effect on strength and ductility of structures.”J. Appl. Mech., 62(Dec.), 965–969.
16.
Bažant, Z. P., and Li, Y.-N. (1996). “Cohesive crack model with rate-dependent opening and viscoelasticity.”Rep., Dept. of Civ. Engrg., Northwestern Univ., Evanston (submitted to Int. J. of Fracture).
17.
Bažant, Z. P., and Oh, B.-H.(1982). “Strain-rate effect in rapid triaxial loading of concrete.”J. Engrg. Mech. Div., ASCE, 108(5), 764–782.
18.
Bažant, Z. P., and Pfeiffer, P. A.(1987). “Determination of fracture energy from size effect and brittleness number.”ACI Mat. J., 84(6), 463–480.
19.
Darwin, D., and Attiogbe, E. K. (1986). “Effects of loading rate on cracking of cement paste in compression.”Cement based composites: Strain rate effects on fracture, S. Mindess and S. P. Shah, eds., 167–180.
20.
Evans, A. G., and Fu, Y. (1984). “The mechanical behavior of alumina.”Fracture of ceramic materials, Noyes Publications, Park Ridge, N.J., 56–88.
21.
Harsh, S., Shen, Z., and Darwin, D.(1990). “Strain-rate sensitive behavior of cement paste and mortar in compression.”ACI Mat. J., 87(5), 508–516.
22.
He, S., Plesha, M. E., Rowlands, R. E., and Bažant, Z. P.(1992). “Fracture energy tests of dam concrete with rate and size effects.”Dam Engrg., 3(2), 139–159.
23.
Hillerborg, A., Modéer, M., and Peterson, P. E.(1976). “Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements.”Cement and Concrete Res., 6, 773–782.
24.
Hughes, B. P., and Watson, A. J.(1978). “Compressive strength ultimate strain of concrete under impact loading.”Magazine of Concrete Res., 30, 189–199.
25.
Li, Y.-N., and Bažant, Z. P.(1994). “Eigenvalue analysis of size effect for cohesive crack model.”Int. J. Fracture, 66, 213–226.
26.
Liu, Z.-G., Swartz, S. E., Hu, K. K., and Kan, Y.-C. (1989). “Time dependent response and fracture of plain concrete beam.”Fracture of concrete and rock: Recent developments, S. P. Shah, S. E. Swartz, and B. Barr, eds., Elsevier, London, U.K., 577–586.
27.
Mindess, S. (1985). “Rate of loading effects on the fracture of cementitious materials.”Application of fracture mechanics to cementitious composites, S. P. Shah, ed., Martinus Nijhoff Publishers, Dordrecht, The Netherlands, 617–638.
28.
Moran, B., and Shih, C. F.(1987). “Crack tip and associated domain integrals from momentum and energy balance.”Engrg. Fracture Mech., 27, 615–642.
29.
Neville, A. M., Dilger, W. H., and Brooks, J. J. (1983). Creep of plain and structural concrete. Construction Press, London, U.K.
30.
Reinhardt, H. W. (1985). “Tensile fracture of concrete at high rates of loading.”Application of fracture mechanics to cementitious composites, S. P. Shah, ed., Martinus Nijhoff Publishers, Dordrecht, The Netherlands, 559–592.
31.
Ross, C. A., and Kuennen, S. T. (1989). “Fracture of concrete at high strain rates.”Fracture of concrete and rock: Recent developments, S. P. Shah, S. E. Swartz, and B. Barr, eds., Elsevier, London, U.K., 152–161.
32.
Shah, S. P., and Chandra, S. (1970). “Fracture of concrete subjected to cyclic and sustained loading.”Am. Concrete Inst., J., 67, 816– 825.
33.
Tandon, S., Faber, K. T., Bažant, Z. P., and Li, Y.-N. (1997). “Cohesive crack modeling of influence of sudden changes in loading rate on concrete fracture.”Engrg. Fracture Mech., in press.
34.
Thouless, M. D., Hsueh, C. H., and Evans, A. G.(1983). “A damage model of creep crack growth in polycrystals.”Acta Metallurgica, 31(10), 1675–1687.
35.
Wittman, F. H. (1985). “Influence of time on crack formation and failure of concrete.”Application of fracture mechanics to cementitious composites, S. P. Shah, ed., Martinus Nijhoff Publishers, Dordrecht, The Netherlands, 593–616.
36.
Wittmann, F. H., and Zaitsev, Y. (1972). “Behavior of hardened element paste and concrete under high sustained load.”Mechanical Behavior of Mat., Proc., 1971 Int. Conf. Soc. of Mat. Sci., Japan, 84–95.
37.
Wu, Z.-S., and Bažant, Z. P. (1993). “Finite element modeling of rate effect in concrete fracture with influence of creep.”Proc., 5th Int. RILEM Symp. on Creep and Shrinkage of Concrete, Z. P. Bažant and I. Carol, eds., E & FN Spon, London, U.K., 427–432.
Information & Authors
Information
Published In
Journal of Engineering Mechanics
Volume 123 • Issue 4 • April 1997
Pages: 350 - 358
Copyright
Copyright © 1997 American Society of Civil Engineers.
History
Published online: Apr 1, 1997
Published in print: Apr 1997
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.