Compressive Strength and Microstructural Development of Cementitious Mixtures Incorporating Ultrafine Granulated Blast Furnace Slag
Publication: Journal of Materials in Civil Engineering
Volume 36, Issue 2
Abstract
Utilization of ultrafine supplementary cementitious materials (SCMs) instead of ordinary ones has shown great potential to enhance the strength development of concrete mixtures. Replacing large amounts of portland cement with ultrafine SCMs, however, may not be feasible due to their negative effect on the water demand of concrete, and extra cost and energy consumption associated with the ultrafine grinding of SCMs. It is therefore important to explore practical methods for efficient use of ultrafine SCMs in producing low portland cement content concretes. To achieve this goal, the current study focused on the use of ultrafine granulated blast furnace slag (GBFS) in combination with a commercial one to replace 30%, 40%, and 50% by weight of portland cement in preparing mortar samples. The compressive strength of the mortars was measured at different ages ranging from 1 to 91 days. Cement paste samples with modified (combination of ultrafine and commercial) and commercial GBFS were also prepared and tested by the isothermal calorimetry, thermogravimetric analysis (TGA), X-ray diffraction (XRD), and scanning electron microscopy equipped with energy dispersive X-ray spectroscopy (SEM/EDS) techniques. The results showed that the samples with 30% and 40% by weight modified GBFS as portland cement replacement had higher compressive strength compared with those made with the same amount of commercial GBFS or 100% by weight portland cement at all the testing ages. The microstructural analyses indicated increased calcium hydroxide consumption and higher reaction degree of clinker phases after 1 day of hydration for the sample incorporating 40% by weight modified GBFS compared with that with the same amount of commercial one, resulting in the superior compressive strength of this sample at such an early age of hydration.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code that support the findings of this study are available from the corresponding author upon reasonable request.
Acknowledgments
The authors would like to thank Mr. Diandian Zhao, Ph.D. Candidate at Columbia University, for his assistance in quantitative X-ray diffraction analysis. The financial support provided by the Natural Sciences and Engineering Research Council of Canada (NSERC), Canadian Concrete Masonry Producers Association (CCMPA), and Canada Masonry Design Centre (CMDC) is also greatly acknowledged.
References
Adu-Amankwah, S., M. Zajac, C. Stabler, B. Lothenbach, and L. Black. 2017. “Influence of limestone on the hydration of ternary slag cements.” Cem. Concr. Res. 100 (Oct): 96–109. https://doi.org/10.1016/j.cemconres.2017.05.013.
Alzaza, A., K. Ohenoja, I. Langås, B. Arntsen, M. Poikelispää, and M. Illikainen. 2022. “Low-temperature () curing of portland cement paste—Synergetic effects of chloride-free antifreeze admixture, C–S–H seeds, and room-temperature pre-curing.” Cem. Concr. Compos. 125 (Jan): 104319. https://doi.org/10.1016/j.cemconcomp.2021.104319.
ASTM. 2017. Standard test method for measurement of heat of hydration of hydraulic cementitious materials using isothermal conduction calorimetry. ASTM C1702. West Conshohocken, PA: ASTM.
ASTM. 2020a. Standard performance specification for hydraulic cement. ASTM C1157/C1157M-20a. West Conshohocken, PA: ASTM.
ASTM. 2020b. Standard practice for mechanical mixing of hydraulic cement pastes and mortars of plastic consistency. ASTM C305-20. West Conshohocken, PA: ASTM.
ASTM. 2021. Standard test method for compressive strength of hydraulic cement mortars (using 2-in. or cube specimens). ASTM C109/109M-21. West Conshohocken, PA: ASTM.
Avet, F., E. Boehm-Courjault, and K. Scrivener. 2019. “Investigation of CASH composition, morphology and density in limestone calcined clay cement (LC3).” Cem. Concr. Res. 115 (Jan): 70–79. https://doi.org/10.1016/j.cemconres.2018.10.011.
Avet, F., X. Li, M. Ben Haha, S. A. Bernal, S. Bishnoi, Ö. Cizer, M. Cyr, S. Dolenec, P. Durdzinski, and J. Haufe. 2022. “Report of RILEM TC 267-TRM phase 2: Optimization and testing of the robustness of the R3 reactivity tests for supplementary cementitious materials.” Mater. Struct. 55 (3): 92. https://doi.org/10.1617/s11527-022-01928-6.
Baki, V. A., X. Ke, A. Heath, J. Calabria-Holley, C. Terzi, and M. Sirin. 2022. “The impact of mechanochemical activation on the physicochemical properties and pozzolanic reactivity of kaolinite, muscovite and montmorillonite.” Cem. Concr. Res. 162 (Dec): 106962. https://doi.org/10.1016/j.cemconres.2022.106962.
Berodier, E., and K. Scrivener. 2014. “Understanding the filler effect on the nucleation and growth of C-S-H.” J. Am. Ceram. Soc. 97 (12): 3764–3773. https://doi.org/10.1111/jace.13177.
Blotevogel, S., A. Ehrenberg, L. Steger, L. Doussang, J. Kaknics, C. Patapy, and M. Cyr. 2020. “Ability of the R3 test to evaluate differences in early age reactivity of 16 industrial ground granulated blast furnace slags (GGBS).” Cem. Concr. Res. 130 (Apr): 105998. https://doi.org/10.1016/j.cemconres.2020.105998.
Bouaziz, A., R. Hamzaoui, S. Guessasma, R. Lakhal, D. Achoura, and N. Leklou. 2017. “Efficiency of high energy over conventional milling of granulated blast furnace slag powder to improve mechanical performance of slag cement paste.” Powder Technol. 308 (Feb): 37–46. https://doi.org/10.1016/j.powtec.2016.12.014.
Burris, L. E., and M. C. G. Juenger. 2016. “Milling as a pretreatment method for increasing the reactivity of natural zeolites for use as supplementary cementitious materials.” Cem. Concr. Compos. 65 (Jan): 163–170. https://doi.org/10.1016/j.cemconcomp.2015.09.008.
CSA (Canadian Standards Association). 2018. Cementitious materials for use in concrete. CSA-A3001-18. Rexdale, ON, Canada: CSA.
De Maeijer, P. K., B. Craeye, R. Snellings, H. Kazemi-Kamyab, M. Loots, K. Janssens, and G. Nuyts. 2020. “Effect of ultra-fine fly ash on concrete performance and durability.” Constr. Build. Mater. 263 (Dec): 120493. https://doi.org/10.1016/j.conbuildmat.2020.120493.
De Weerdt, K., M. B. Haha, G. Le Saout, K. O. Kjellsen, H. Justnes, and B. Lothenbach. 2011. “Hydration mechanisms of ternary portland cements containing limestone powder and fly ash.” Cem. Concr. Res. 41 (3): 279–291. https://doi.org/10.1016/j.cemconres.2010.11.014.
Doebelin, N., and R. Kleeberg. 2015. “Profex: A graphical user interface for the Rietveld refinement program BGMN.” J. Appl. Crystallogr. 48 (5): 1573–1580. https://doi.org/10.1107/S1600576715014685.
Ghasemalizadeh, S., and R. Khoshnazar. 2022. “Effect of ultrafine granulated blast furnace slag on the strength development portland cement mortar.” In Proc., Canadian Society of Civil Engineering Annual Conf. 1–11. Surrey, BC, Canada: Canadian Society for Civil Engineering.
Goto, S., K. Suenaga, T. Kado, and M. Fukuhara. 1995. “Calcium silicate carbonation products.” J. Am. Ceram. Soc. 78 (11): 2867–2872. https://doi.org/10.1111/j.1151-2916.1995.tb09057.x.
Gruskovnjak, A., B. Lothenbach, F. Winnefeld, R. Figi, S.-C. Ko, M. Adler, and U. Mäder. 2008. “Hydration mechanisms of super sulphated slag cement.” Cem. Concr. Res. 38 (7): 983–992. https://doi.org/10.1016/j.cemconres.2008.03.004.
Haha, M. B., B. Lothenbach, G. L. Le Saout, and F. Winnefeld. 2011. “Influence of slag chemistry on the hydration of alkali-activated blast-furnace slag—Part I: Effect of MgO.” Cem. Concr. Res. 41 (9): 955–963. https://doi.org/10.1016/j.cemconres.2011.05.002.
Hamdan, A., T. Kim, A. Hajimohammadi, M. F. Alnahhal, and A. Rawal. 2022. “Synthesis of chemically controlled cementitious materials using organic steric entrapment (OSE) method: Process, advantages, and characterization.” Cem. Concr. Res. 153 (Mar): 106698. https://doi.org/10.1016/j.cemconres.2021.106698.
Han, X., J. Yang, J. Feng, C. Zhou, and X. Wang. 2019. “Research on hydration mechanism of ultrafine fly ash and cement composite.” Constr. Build. Mater. 227 (Dec): 116697. https://doi.org/10.1016/j.conbuildmat.2019.116697.
Hossein, A. H., H. AzariJafari, and R. Khoshnazar. 2022. “The role of performance metrics in comparative LCA of concrete mixtures incorporating solid wastes: A critical review and guideline proposal.” Waste Manage. 140 (Mar): 40–54. https://doi.org/10.1016/j.wasman.2022.01.010.
IEA (International Energy Agency). 2018. Technology roadmap—Low-carbon transition in the cement industry. Paris: IEA.
Ishak, S. A., and H. Hashim. 2015. “Low carbon measures for cement plant—A review.” J. Cleaner Prod. 103 (Feb): 260–274. https://doi.org/10.1016/j.jclepro.2014.11.003.
Juenger, M. C. G., and R. Siddique. 2015. “Recent advances in understanding the role of supplementary cementitious materials in concrete.” Cem. Concr. Res. 78 (Dec): 71–80. https://doi.org/10.1016/j.cemconres.2015.03.018.
Kim, M. S., Y. Jun, C. Lee, and J. E. Oh. 2013. “Use of CaO as an activator for producing a price-competitive non-cement structural binder using ground granulated blast furnace slag.” Cem. Concr. Res. 54 (Dec): 208–214. https://doi.org/10.1016/j.cemconres.2013.09.011.
Kocaba, V. 2009. “Development and evaluation of methods to follow microstructural development of cementitious systems including slags.” Ph.D. thesis, Ecole Polytechnique Federale de Lausanne.
Li, X., J. Bizzozero, and C. Hesse. 2022. “Impact of CSH seeding on hydration and strength of slag blended cement.” Cem. Concr. Res. 161 (Nov): 106935. https://doi.org/10.1016/j.cemconres.2022.106935.
Liu, X., B. Ma, H. Tan, X. He, R. Zhao, P. Chen, Y. Su, and J. Yang. 2020. “Preparation of ultrafine fly ash by wet grinding and its utilization for immobilizing chloride ions in cement paste.” Waste Manage. 113 (Jul): 456–468. https://doi.org/10.1016/j.wasman.2020.06.022.
Liu, Y., Z. Zhang, G. Hou, and P. Yan. 2021. “Preparation of sustainable and green cement-based composite binders with high-volume steel slag powder and ultrafine blast furnace slag powder.” J. Cleaner Prod. 289 (Mar): 125133. https://doi.org/10.1016/j.jclepro.2020.125133.
Lumley, J. S., R. S. Gollop, G. K. Moir, and H. F. W. Taylor. 1996. “Degrees of reaction of the slag in some blends with portland cements.” Cem. Concr. Res. 26 (1): 139–151. https://doi.org/10.1016/0008-8846(95)00190-5.
Matschei, T., B. Lothenbach, and F. P. Glasser. 2007. “The role of calcium carbonate in cement hydration.” Cem. Concr. Res. 37 (4): 551–558. https://doi.org/10.1016/j.cemconres.2006.10.013.
Mejdi, M., W. Wilson, M. Saillio, T. Chaussadent, L. Divet, and A. Tagnit-Hamou. 2022. “Hydration and microstructure of glass powder cement pastes—A multi-technique investigation.” Cem. Concr. Res. 151 (Jan): 106610. https://doi.org/10.1016/j.cemconres.2021.106610.
Monteiro, P. J. M., S. A. Miller, and A. Horvath. 2017. “Towards sustainable concrete.” Nat. Mater. 16 (7): 698–699. https://doi.org/10.1038/nmat4930.
Ogirigbo, O. R., and L. Black. 2016. “Influence of slag composition and temperature on the hydration and microstructure of slag blended cements.” Constr. Build. Mater. 126 (Nov): 496–507. https://doi.org/10.1016/j.conbuildmat.2016.09.057.
Oner, A., and S. Akyuz. 2007. “An experimental study on optimum usage of GGBS for the compressive strength of concrete.” Cem. Concr. Compos. 29 (6): 505–514. https://doi.org/10.1016/j.cemconcomp.2007.01.001.
Rossen, J. E. 2014. “Composition and morphology of C-A-S-H in pastes of alite and cement blended with supplementary cementitious materials.” Ph.D. thesis, Ecole Polytechnique Federale de Lausanne.
Scrivener, K., R. Snellings, and B. Lothenbach. 2016. A practical guide to microstructural analysis of cementitious materials. Boca Raton, FL: CRC Press.
Scrivener, K. L., P. Juilland, and P. J. M. Monteiro. 2015. “Advances in understanding hydration of portland cement.” Cem. Concr. Res. 78 (Dec): 38–56. https://doi.org/10.1016/j.cemconres.2015.05.025.
Sharmila, P., and G. Dhinakaran. 2016. “Compressive strength, porosity and sorptivity of ultra fine slag based high strength concrete.” Constr. Build. Mater. 120 (Sep): 48–53. https://doi.org/10.1016/j.conbuildmat.2016.05.090.
Souri, A., H. Kazemi-Kamyab, R. Snellings, R. Naghizadeh, F. Golestani-Fard, and K. Scrivener. 2015. “Pozzolanic activity of mechanochemically and thermally activated kaolins in cement.” Cem. Concr. Res. 77 (Nov): 47–59. https://doi.org/10.1016/j.cemconres.2015.04.017.
Supit, S. W. M., F. U. A. Shaikh, and P. K. Sarker. 2014. “Effect of ultrafine fly ash on mechanical properties of high volume fly ash mortar.” Constr. Build. Mater. 51 (Jan): 278–286. https://doi.org/10.1016/j.conbuildmat.2013.11.002.
Ting, L., W. Qiang, and Z. Shiyu. 2019. “Effects of ultra-fine ground granulated blast-furnace slag on initial setting time, fluidity and rheological properties of cement pastes.” Powder Technol. 345 (Mar): 54–63. https://doi.org/10.1016/j.powtec.2018.12.094.
UN Environment, K. L. Scrivener, V. M. John, and E. M. Gartner. 2018. “Eco-efficient cements: Potential economically viable solutions for a low- cement-based materials industry.” Cem. Concr. Res. 114 (Mar): 2–26. https://doi.org/10.1016/j.cemconres.2018.03.015.
Vance, K., M. Aguayo, T. Oey, G. Sant, and N. Neithalath. 2013. “Hydration and strength development in ternary portland cement blends containing limestone and fly ash or metakaolin.” Cem. Concr. Compos. 39 (May): 93–103. https://doi.org/10.1016/j.cemconcomp.2013.03.028.
Wang, Y., X. He, Y. Su, J. Yang, B. Strnadel, and X. Wang. 2019. “Efficiency of wet-grinding on the mechano-chemical activation of granulated blast furnace slag (GBFS).” Constr. Build. Mater. 199 (Feb): 185–193. https://doi.org/10.1016/j.conbuildmat.2018.11.245.
Whittaker, M., M. Zajac, M. B. Haha, F. Bullerjahn, and L. Black. 2014. “The role of the alumina content of slag, plus the presence of additional sulfate on the hydration and microstructure of portland cement-slag blends.” Cem. Concr. Res. 66 (Dec): 91–101. https://doi.org/10.1016/j.cemconres.2014.07.018.
Wilson, W., L. Sorelli, and A. Tagnit-Hamou. 2018. “Unveiling micro-chemo-mechanical properties of C–(A)–S–H and other phases in blended-cement pastes.” Cem. Concr. Res. 107 (May): 317–336. https://doi.org/10.1016/j.cemconres.2018.02.010.
Wong, H. S., M. K. Head, and N. R. Buenfeld. 2006. “Pore segmentation of cement-based materials from backscattered electron images.” Cem. Concr. Res. 36 (6): 1083–1090. https://doi.org/10.1016/j.cemconres.2005.10.006.
Yang, J., H. Hu, X. He, Y. Su, Y. Wang, H. Tan, and H. Pan. 2021a. “Effect of steam curing on compressive strength and microstructure of high volume ultrafine fly ash cement mortar.” Constr. Build. Mater. 266 (Jan): 120894. https://doi.org/10.1016/j.conbuildmat.2020.120894.
Yang, J., J. Zeng, X. He, H. Hu, Y. Su, H. Bai, and H. Tan. 2021b. “Eco-friendly UHPC prepared from high volume wet-grinded ultrafine GGBS slurry.” Constr. Build. Mater. 308 (Nov): 125057. https://doi.org/10.1016/j.conbuildmat.2021.125057.
Zhang, J., H. Tan, M. Bao, X. Liu, Z. Luo, and P. Wang. 2021. “Low carbon cementitious materials: Sodium sulfate activated ultra-fine slag/fly ash blends at ambient temperature.” J. Cleaner Prod. 280 (Jan): 124363. https://doi.org/10.1016/j.jclepro.2020.124363.
Zhao, D., and R. Khoshnazar. 2020. “Microstructure of cement paste incorporating high volume of low-grade metakaolin.” Cem. Concr. Compos. 106 (Feb): 103453. https://doi.org/10.1016/j.cemconcomp.2019.103453.
Zhou, Y., and Z. Zhang. 2021. “Effect of fineness on the pozzolanic reaction kinetics of slag in composite binders: Experiment and modeling.” Constr. Build. Mater. 273 (Mar): 121695. https://doi.org/10.1016/j.conbuildmat.2020.121695.
Zunino, F., and K. Scrivener. 2019. “The influence of the filler effect on the sulfate requirement of blended cements.” Cem. Concr. Res. 126 (Dec): 105918. https://doi.org/10.1016/j.cemconres.2019.105918.
Zunino, F., and K. Scrivener. 2022. “Insights on the role of alumina content and the filler effect on the sulfate requirement of PC and blended cements.” Cem. Concr. Res. 160 (Oct): 106929. https://doi.org/10.1016/j.cemconres.2022.106929.
Information & Authors
Information
Published In
Copyright
© 2023 American Society of Civil Engineers.
History
Received: Apr 29, 2023
Accepted: Aug 4, 2023
Published online: Nov 25, 2023
Published in print: Feb 1, 2024
Discussion open until: Apr 25, 2024
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.