Use of Zeolite as Both Internal Curing Agent and Supplementary Binder in Mortar
Publication: Journal of Materials in Civil Engineering
Volume 35, Issue 9
Abstract
Internal curing with sand-like zeolite particles is effective in reducing shrinkage of cement-based materials, but it decreases the compressive strength. In order to obtain cement-based materials with lower shrinkage and higher strength, zeolite can be used as both internal curing agent and supplementary binder, due to its pozzolanic activity. In this study, the effects of particle size and calcination treatment on internal curing performance and supplementary binding performance of zeolite in cement mortar were experimentally investigated. The pore structure, chemical bond characteristics, water absorption/release behaviors, and pozzolanic activity of zeolite particles were investigated. Cement hydration products, interior relative humidity, and drying moisture loss of mortar specimens containing zeolite were also investigated. The results show that (1) fine zeolite particles can improve the compressive strength, relative humidity, water retention property, and pore structure of cement mortar more obviously than coarse zeolite particles, because they have larger pore size and higher pozzolanic activity; (2) calcination treatment can improve the internal curing performance of coarse zeolite particles, because coarse particles can lose more combined water after calcined; and (3) calcination decreases the pozzolanic activity of zeolite, especially for fine particles.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
Support from National Natural Science Foundation of China (52108203), Natural Science Foundation of Hebei Province (E2021201038), Science and Technology Project of Hebei Education Department (BJK2022048), Foundation of President of Hebei University (XZJJ202001), and Startup Funding of Hebei University (521100221069) are gratefully acknowledged.
References
Ahmadi, B., and M. Shekarchi. 2009. “Use of natural zeolite as a supplementary cementitious material.” Cem. Concr. Compos. 32 (2): 134–141. https://doi.org/10.1016/j.cemconcomp.2009.10.006.
ASTM. 2020. Standard test methods for measuring the reactivity of supplementary cementitious materials by isothermal calorimetry and bound water measurements. ASTM C1897. West Conshohocken, PA: ASTM.
Bílek, V., Z. Keršner, P. Schmid, and T. Mosler. 2002. “The possibility of self-curing concrete.” In Innovations and developments in concrete materials and construction, edited by R. K. Dhir, P. C. Hewlett, and L. J. Csetenyi, 51–60. Scotland, UK: Dundee.
Burris, L. E., and M. C. G. Juenger. 2020. “Effect of calcination on the reactivity of natural clinoptilolite zeolites used as supplementary cementitious materials.” Constr. Build. Mater. 258 (Oct): 119988. https://doi.org/10.1016/j.conbuildmat.2020.119988.
Chan, S. Y. N., and X. Ji. 1999. “Comparative study of the initial surface absorption and chloride diffusion of high performance zeolite, silica fume and PFA concretes.” Cem. Concr. Compos. 21 (4): 293–300. https://doi.org/10.1016/S0958-9465(99)00010-4.
China National Standard. 2005. Test method for fluidity of cement mortar. GB/T 2419-2005. Beijing: China National Standard.
China National Standard. 2008. Methods of dust character test. GB/T 16913-2008. Beijing: China National Standard.
China National Standard. 2009. Standard for test methods performance on building mortar. JGJ/T 70-2009. Beijing: China National Standard.
Ding X. 2019. “Mixture design and properties study of low shrinkage concrete by internal curing with porous particles.” Ph.D. thesis, Dept. of Civil Engineering, Tsinghua Univ.
Dong, Y., Y. Zhang, and H. Lin. 2017. “Effects of calcination temperature on physicochemical properties of natural zeolite.” J. Nonferrous Metals 27 (7): 1520–1526. https://doi.org/10.19476/j.ysxb.1004.0609.
Florez, C., O. Restrepo-Baena, and J. I. Tobon. 2021. “Effects of calcination and milling pre-treatments on natural zeolites as a supplementary cementitious material.” Constr. Build. Mater. 310 (Dec): 125220. https://doi.org/10.1016/j.conbuildmat.2021.125220.
Ghourchian, S., M. Wyrzykowski, P. Lura, M. Shekarchi, and B. Ahmadi. 2013. “An investigation on the use of zeolite aggregates for internal curing of concrete.” Constr. Build. Mater. 40 (Mar): 135–144. https://doi.org/10.1016/j.conbuildmat.2012.10.009.
Küçükyıldırım, E., and B. Uzal. 2014. “Characteristics of calcined natural zeolites for use in high-performance pozzolan blended cements.” Constr. Build. Mater. 73 (Dec): 229–234. https://doi.org/10.1016/j.conbuildmat.2014.09.081.
Kukobat, R., R. Škrbić, P. Massiani, K. Baghdad, F. Launay, M. Sarno, C. Cirillo, A. Senatore, E. Salčin, and S. G. Atlagić. 2022. “Thermal and structural stability of microporous natural clinoptilolite zeolite.” Microporous Mesoporous Mater. 341 (Aug): 112101. https://doi.org/10.1016/j.micromeso.2022.112101.
Kupwade-Patil, K., S. D. Palkovic, A. Bumajdad, C. Soriano, and O. Büyüköztürk. 2017. “Use of silica fume and natural volcanic ash as a replacement to Portland cement: Micro and pore structural investigation using NMR, XRD, FTIR and X-ray microtomography.” Constr. Build. Mater. 158 (Jan): 574–590. https://doi.org/10.1016/j.conbuildmat.2017.09.165.
Lee, J. 2012. “Grinding effects on the change of particle properties in cupric sulfide, CuS.” Adv. Powder Technol. 23 (6): 731–735. https://doi.org/10.1016/j.apt.2011.09.004.
Liu, Y., W. Wang, and A. Wang. 2012. “Effect of dry grinding on the microstructure of palygorskite and adsorption efficiency for methylene blue.” Powder Technol. 225 (Jul): 124–129. https://doi.org/10.1016/j.powtec.2012.03.049.
Markiv, T., K. Sobol, M. Franus, and W. Franus. 2016. “Mechanical and durability properties of concretes incorporating natural zeolite.” Arch. Civ. Mech. Eng. 16 (4): 554–562. https://doi.org/10.1016/j.acme.2016.03.013.
Nagrockienė, D., G. Girskas, and G. Skripkiūnas. 2017. “Properties of concrete modified with mineral additives.” Constr. Build. Mater. 135 (Mar): 37–42. https://doi.org/10.1016/j.conbuildmat.2016.12.215.
Najimi, M., J. Sobhani, B. Ahmadi, and M. Shekarchi. 2012. “An experimental study on durability properties of concrete containing zeolite as a highly reactive natural pozzolan.” Constr. Build. Mater. 35 (Oct): 1023–1033. https://doi.org/10.1016/j.conbuildmat.2012.04.038.
Poon, C., L. Lam, S. Kou, and Z. Lin. 1999. “A study on the hydration rate of natural zeolite blended cement pastes.” Constr. Build. Mater. 13 (8): 427–432. https://doi.org/10.1016/S0950-0618(99)00048-3.
Raggiotti, B. B., M. J. Positieri, and Á. Oshiro. 2018. “Natural zeolite, a pozzolan for structural concrete.” Proc. Struct. Integrity 11 (Jan): 36–43. https://doi.org/10.1016/j.prostr.2018.11.006.
Ramezanianpour, A. A., R. Mousavi, M. Kalhori, J. Sobhani, and M. Najimi. 2015. “Micro and macro level properties of natural zeolite contained concretes.” Constr. Build. Mater. 101 (Dec): 347–358. https://doi.org/10.1016/j.conbuildmat.2015.10.101.
Sadrara, M., M. K. Khorrami, J. T. Darian, and A. B. Garmarudi. 2021. “Rapid determination and classification of zeolites based on Si/Al ratio using FTIR spectroscopy and chemometrics.” Infrared Phys. Technol. 116 (Aug): 103797. https://doi.org/10.1016/j.infrared.2021.103797.
Su, Y. F., C. Huang, H. G. Jeong, T. Nantung, J. Olek, P. Baah, and N. Lu. 2020. “Autogenous healing performance of internal curing agent-based self-healing cementitious composite.” Cem. Concr. Compos. 114 (Nov): 103825. https://doi.org/10.1016/j.cemconcomp.2020.103825.
Ulmanu, M., and I. Anger. 2012. “Physical and chemical properties.” In Handbook of natural zeolites, edited by V. J. Inglezakis and A. A. Zorpas, 70–102. Sharjah, United Arab Emirates: Bentham Science Publishers.
Uzal, B., L. Turanlı, H. Yücel, M. C. Göncüoğlu, and A. Çulfaz. 2010. “Pozzolanic activity of clinoptilolite: A comparative study with silica fume, fly ash and a non-zeolitic natural pozzolan.” Cem. Concr. Res. 40 (3): 398–404. https://doi.org/10.1016/j.cemconres.2009.10.016.
Villa, R. V. D. L., R. Fernández, O. Rodríguez, R. García, E. Villar-Cociña, and M. Frías. 2013. “Evolution of the pozzolanic activity of a thermally treated zeolite.” J. Mater. Sci. 48 (8): 3213–3224. https://doi.org/10.1007/s10853-012-7101-z.
Wang, J., Y. Wang, J. Yu, L. Xu, M. Li, J. Cheng, and Z. Li. 2022. “Effects of sodium sulfate and potassium sulfate on the properties of calcium sulfoaluminate (CSA) cement based grouting materials.” Constr. Build. Mater. 353 (Oct): 129045. https://doi.org/10.1016/j.conbuildmat.2022.129045.
Wang, Q. 2018. “Design and application of high and ultra-high strength engineered cementitious composites.” Ph.D. thesis, Dept. of Civil Engineering, Tsinghua Univ.
Wang, Q., J. Zhang, and J. C. M. Ho. 2020. “Zeolite to improve strength-shrinkage performance of high-strength engineered cementitious composite.” Constr. Build. Mater. 234 (Feb): 117335. https://doi.org/10.1016/j.conbuildmat.2019.117335.
Yang, L., Y. Guang, and D. S. Geert. 2019. “Investigation on the potential utilization of zeolite as an internal curing agent for autogenous shrinkage mitigation and the effect of modification.” Constr. Build. Mater. 198 (Feb): 669–676. https://doi.org/10.1016/j.conbuildmat.2018.12.001.
Yang, Y., Y. Yao, X. Gao, H. Deng, and P. Yu. 2008. “Shrinkage reducing measures for engineering cementitious composites.” J. Wuhan Univ. Technol. 23 (6): 907–911. https://doi.org/10.1007/s11595-007-6907-z.
Yu, Z., W. Yang, P. Zhan, X. Liu, and D. Chen. 2020. “Strengths, microstructure and nanomechanical properties of concrete containing high volume of zeolite powder.” Materials 13 (18): 4191. https://doi.org/10.3390/ma13184191.
Zaichenko, N. M. 2011. “Internal curing and autogenous shrinkage of high-strength concrete.” [In Russian.] Build. Mater. Constr. J. Ukrainian State Acad. Railway Transp. 122: 236–244.
Zeng, Q., K. Li, and T. Fen-Chong. 2011. “Pore structure characterization of cement pastes blended with high-volume fly-ash.” Cem. Concr. Res. 42 (1): 194–204. https://doi.org/10.1016/j.cemconres.2011.09.012.
Zhang, G., and X. Wang. 2020. “Effect of pre-wetted zeolite sands on the autogenous shrinkage and strength of ultra-high-performance concrete.” Materials 13 (10): 2356. https://doi.org/10.3390/ma13102356.
Zhang, J., X. Ding, and Q. Wang. 2018. “Effective solution for low shrinkage and low permeability of normal strength concrete using calcined zeolite particles.” Constr. Build. Mater. 160 (Jan): 57–65. https://doi.org/10.1016/j.conbuildmat.2017.11.029.
Zhang, J., X. Ding, Q. Wang, and X. Zheng. 2019. “High-strength concrete mixture with calcined zeolite particles for shrinkage reduction.” Mag. Concr. Res. 71 (13): 690–699. https://doi.org/10.1680/jmacr.17.00181.
Zhang, J., Y. Han, and J. Zhang. 2016. “Evaluation of shrinkage induced cracking in concrete with impact of internal curing and water to cement ratio.” J. Adv. Concr. Technol. 14 (7): 324–334. https://doi.org/10.3151/jact.14.324.
Zhang, J., Q. Wang, and J. Zhang. 2017. “Shrinkage of internal cured high strength engineered cementitious composite with pre-wetted sand-like zeolite.” Constr. Build. Mater. 134 (Mar): 664–672. https://doi.org/10.1016/j.conbuildmat.2016.12.182.
Zhao, H., J. Li, G. Sun, J. Jiang, W. Xuan, Y. Chen, Q. Tian, and J. Liu. 2020. “Effects of pre-soaked zeolite and CaO-based expansive agent on mechanical properties and autogenous deformation of early-age concrete.” Constr. Build. Mater. 261 (Nov): 120370. https://doi.org/10.1016/j.conbuildmat.2020.120370.
Zheng, X., K. F. Liu, S. Z. Gao, F. Z. Wang, and Z. Z. Wu. 2023. “Effect of pozzolanic reaction of zeolite on its internal curing performance in cement-based materials.” J Build. Eng. 63 (Feb): 105503. https://doi.org/10.1016/j.jobe.2022.105503.
Zheng, X., and J. Zhang. 2020. “Influence of zeolite addition on mechanical performance and shrinkage of high strength engineered cementitious composites.” J. Build. Eng. 36 (Apr): 102124. https://doi.org/10.1016/J.JOBE.2020.102124.
Zhou, Y., Z. Wang, Z. Zhu, Y. Chen, K. Wu, H. Huang, K. G. Anvarovna, and L. Xu. 2022. “Influence of metakaolin and calcined montmorillonite on the hydration of calcium sulphoaluminate cement.” Case Stud. Constr. Mater. 16 (Jun): e01104. https://doi.org/10.1016/J.CSCM.2022.E01104.
Information & Authors
Information
Published In
Copyright
© 2023 American Society of Civil Engineers.
History
Received: Jun 13, 2022
Accepted: Feb 15, 2023
Published online: Jun 22, 2023
Published in print: Sep 1, 2023
Discussion open until: Nov 22, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.