Repairing Distortion-Induced Fatigue Cracks in Steel Bridge Girders Using Angles-with-Plate Retrofit Technique. I: Physical Simulations
This article has a reply.
VIEW THE REPLYPublication: Journal of Structural Engineering
Volume 140, Issue 5
Abstract
Physical simulations of 914 mm (36 in.) deep girder-cross frame subassemblies subjected to cyclic loading were carried out to study the effects of distortion-induced fatigue and to evaluate the effectiveness of a new retrofit measure. The new repair method consists of adding steel angles connecting the girder web to the cross frame transverse connection plate (CP), and a steel plate on the opposite side of the girder web. Parameters of the experimental study included the retrofit configuration and length of the fatigue cracks. Test results showed that the new angles-with-plate retrofit measure was effective in preventing fatigue crack reinitiation for both horseshoe-shaped cracks around the CP-to-web weld and cracks along the flange-to-web weld. When the retrofit measure was implemented, specimens were able to exceed the number of cycles equivalent to infinite fatigue life for AASHTO Fatigue Category A details without any measureable fatigue crack growth, regardless of crack configuration. A test trial was also carried out to measure fatigue crack reinitiation life of the web-gap region with undersized crack-arrest holes. Experimental results showed that, for the stress range imposed at the web-gap region of the specimens and the crack-arrest hole diameter evaluated, fatigue cracks reinitiated at 40,000 cycles, which was below the limit for AASHTO Fatigue Category details.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors are grateful for support from the Kansas Department of Transportation (KDOT) and the University of Kansas Transportation Research Institute (KU TRI). The authors would also like to acknowledge support provided through Pooled Fund Study TPF-5(189), which includes the following participating state DOTs: Kansas, California, Iowa, Illinois, Louisiana, New Jersey, New York, Oregon, Pennsylvania, Tennessee, Washington, Wisconsin, and Wyoming, as well as the Federal Highway Administration.
References
AASHTO. (2010). AASHTO LRFD bridge design specifications, 5th Ed., Washington, DC.
Alemdar, F., Overman, T., Matamoros, A., Bennett, C., and Rolfe, S. (2014). “Repairing distortion-induced fatigue cracks in steel bridge girders using angles-with-plate retrofit technique. II: Computer simulations.” J. Struct. Eng., 04014004.
ASTM. (2009). “Standard test methods for tension testing of metallic materials.” E8/E8M, West Conshohoken, PA.
Cousins, T., and Stallings, T. (1998). “Laboratory tests of bolted diaphragm-girder connections.” J. Bridge Eng., 56–63.
Fisher, J., Jin, J., Wagner, D., and Yen, B. (1990). “Distortion-induced fatigue cracking in steel bridges.”, Transportation Research Board, Washington, DC.
Fisher, J. W., Barthelemy, B. M., Mertz, D. R., and Edinger, J. A. (1980). “Fatigue behavior of full-scale welded bridge attachments.”, Transportation Research Board, Washington, DC.
Hassel, H., Bennett, C., Matamoros, A., and Rolfe, S. (2012). “Parametric analysis of cross-frame layout on distortion-induced fatigue in skewed steel bridges.” J. Bridge Eng., 601–611.
Keating, P., and Fisher, J. (1987). “Fatigue behavior of variable loaded bridge details near the fatigue limit.”, Transportation Research Board, Washington, DC, 56–64.
Keating, P. B. (1994). “Focusing on fatigue.” Civ. Eng., 64(11), 54–57.
Lindberg, A., and Schultz, A. (2007). “Incorporation of fatigue detail classification of steel bridges into the Minnesota Department of Transportation database: Final report.”, Minnesota Dept. of Transportation: Research Services Section, St. Paul, MN.
Richardson, T. (2012). “Analytical investigation of repair methods for fatigue cracks in steel bridges.” M.S. thesis, Dept. of Civil Engineering, Univ. of Kansas, Lawrence, KS.
Rolfe, S. T., and Barsom, J. M. (1977). Fracture and fatigue control in structures: Applications of fracture mechanics, 1st Ed., Prentice Hall, Englewood Cliffs, NJ.
Information & Authors
Information
Published In
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Jul 31, 2012
Accepted: May 13, 2013
Published online: May 15, 2013
Published in print: May 1, 2014
Discussion open until: Jun 6, 2014
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.