Preparation of Magnesium Oxysulfate Cement with Calcined Phosphate Tailings
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 12
Abstract
Recycling of phosphate tailings (PT) in cement production can reduce the amount of this solid waste and its consequent pollution. This paper used high content of calcined PT as an alternative to light-burned magnesia to prepare magnesium oxysulfate (MOS) cement. Thermal decomposition properties of PT at calcination temperature of 600°C–900°C were studied with X-ray diffraction (XRD) and scanning electron microscopy (SEM). Compressive strength, XRD, Fourier-transform infrared spectroscopy (FT-IR), and SEM were conducted to study the effects of the calcination temperature of PT (600°C–800°C) and the dosage of calcined PT (50%–100%) on the strength development and hydration mechanism of MOS cement. Results showed that the main component of PT, dolomite, partially decomposed into magnesium calcite, periclase, and calcite at 700°C; decomposed further into calcite, periclase, and lime at 800°C; and finally decomposed into lime and periclase at 900°C. The periclase sourced from calcined PT reacted with the MOS system to form brucite and (517 phase). Gypsum also was formed in the reaction. Brucite, 517 phase, and gypsum worked with the unreacted PT to build the structure and provide the source of strength. MOS paste prepared with 60% PT calcined at 700°C had the highest compressive strength, 63 MPa, at 28 days of all the mixtures. The paste prepared with 50% PT calcined at 700°C had the highest strength retention value, about 68%, after 56 days of water immersion. This study provides a method for the efficient use of PT by incorporating it into MOS cement after calcination.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
This research work was financially supported by the National Natural Science Foundation of China, Grant No. 51972209; and Shanghai “Science, Technology and Innovation Action Plan 2020” “The Belt and Road Initiative” (Grant No. 20520741200).
References
Chen, Q., Q. Zhang, A. Fourie, and C. Xin. 2017. “Utilization of phosphogypsum and phosphate tailings for cemented paste backfill.” J. Environ. Manage. 201 (Oct): 19–27. https://doi.org/10.1016/j.jenvman.2017.06.027.
Chen, Y., C. Wu, H. Yu, W. Chen, C. Chen, S. Zheng, and F. Chen. 2018. “Study of using light-burned dolomite ores as raw material to produce magnesium oxysulfate cement.” Adv. Cem. Res. 30 (10): 437–450. https://doi.org/10.1680/jadcr.17.00165.
Dang, L., X. Nai, Y. Dong, and W. Li. 2017. “Functional group effect on flame retardancy, thermal, and mechanical properties of organophosphorus-based magnesium oxysulfate whiskers as a flame retardant in polypropylene.” RSC Adv. 7 (35): 21655–21665. https://doi.org/10.1039/C7RA02863F.
Dinnebier, R. E., M. Pannach, and D. Freyer. 2013. “: A metastable phase in the system .” Z. Anorg. Allg. Chem. 639 (10): 1827–1833. https://doi.org/10.1002/zaac.201300128.
Dung, N. T., and C. Unluer. 2018. “Development of MgO concrete with enhanced hydration and carbonation mechanisms.” Cem. Concr. Res. 103 (Oct): 160–169. https://doi.org/10.1016/j.cemconres.2017.10.011.
Frost, R. L., and S. J. Palmer. 2011. “Infrared and infrared emission spectroscopy of nesquehonite for the formula of nesquehonite.” Spectrochim. Acta, Part A 78 (4): 1255–1260. https://doi.org/10.1016/j.saa.2010.12.059.
Fu, S., P. Li, Q. Feng, X. Li, P. Li, Y. Sun, and Y. Chen. 2011. “Soil quality degradation in a magnesite mining area.” Pedosphere 21 (1): 98–106. https://doi.org/10.1016/S1002-0160(10)60084-7.
Gu, K., and B. Chen. 2020. “Loess stabilization using cement, waste phosphogypsum, fly ash and quicklime for self-compacting rammed earth construction.” Constr. Build. Mater. 231 (Jan): 117195. https://doi.org/10.1016/j.conbuildmat.2019.117195.
Gu, K., Y. Maierdan, and B. Chen. 2022. “Effects of ethylenediamine tetra-acetic acid (EDTA) and its disodium salt derivative (EDTA-Na) on the characteristics of magnesium oxysulfate (MOS) cement.” Composites, Part B 14 (Jan): 109654. https://doi.org/10.1016/j.compositesb.2022.109654.
Guan, Y., Z. Hu, Z. Zhang, J. Chang, W. Bi, C. R. Cheeseman, and T. Zhang. 2021. “Effect of hydromagnesite addition on the properties and water resistance of magnesium oxysulfate (MOS) cement.” Cem. Concr. Res. 143 (Feb): 106387. https://doi.org/10.1016/j.cemconres.2021.106387.
Gunasekaran, S., and G. Anbalagan. 2007. “Thermal decomposition of natural dolomite.” Bull. Mater. Sci. 30 (4): 339–344. https://doi.org/10.1007/s12034-007-0056-z.
Kristóf-Makó, E., and A. Z. Juhász. 1999. “The effect of mechanical treatment on the crystal structure and thermal decomposition of dolomite.” Thermochim. Acta 342 (Dec): 105–114. https://doi.org/10.1016/S0040-6031(99)00290-7.
Kumar, A., T. Oey, S. Kim, D. Thomas, S. Badran, J. Li, F. Fernandes, N. Neithalath, and G. Sant. 2013. “Simple methods to estimate the influence of limestone fillers on reaction and property evolution in cementitious materials.” Cem. Concr. Compos. 42 (Sep): 20–29. https://doi.org/10.1016/j.cemconcomp.2013.05.002.
Li, D., B. Chen, X. Chen, B. Fu, H. Wei, and X. Xiang. 2020a. “Synergetic effect of superabsorbent polymer (SAP) and crystalline admixture (CA) on mortar macro-crack healing.” Constr. Build. Mater. 247 (Jun): 118521. https://doi.org/10.1016/j.conbuildmat.2020.118521.
Li, K., Y. Wang, N. Yao, and A. Zhang. 2020b. “Recent progress of magnesium oxychloride cement: Manufacture, curing, structure and performance.” Constr. Build. Mater. 255 (Sep): 119381. https://doi.org/10.1016/j.conbuildmat.2020.119381.
Lim, D. J., N. A. Marks, and M. R. Rowles. 2020. “Universal Scherrer equation for graphene fragments.” Carbon 162 (Jun): 475–480. https://doi.org/10.1016/j.carbon.2020.02.064.
Liu, Z., S. Wang, J. Huang, Z. Wei, B. Guan, and J. Fang. 2015. “Experimental investigation on the properties and microstructure of magnesium oxychloride cement prepared with caustic magnesite and dolomite.” Constr. Build. Mater. 85 (Jun): 247–255. https://doi.org/10.1016/j.conbuildmat.2015.01.056.
Miao, M., C. Wu, Y. Tan, and H. Yu. 2020. “Mechanistic study of the effects of magnesia reactivity on setting and hardening of basic magnesium sulfate cement.” J. Adv. Concr. Technol. 18 (11): 678–688. https://doi.org/10.3151/jact.18.678.
Power, I. M., G. M. Dipple, and P. S. Francis. 2017. “Assessing the carbon sequestration potential of magnesium oxychloride cement building materials.” Cem. Concr. Compos. 78 (2017): 97–107. https://doi.org/10.1016/j.cemconcomp.2017.01.003.
Qin, L., X. Gao, and T. Chen. 2018a. “Recycling of raw rice husk to manufacture magnesium oxysulfate cement based lightweight building materials.” J. Cleaner Prod. 191 (Aug): 220–232. https://doi.org/10.1016/j.jclepro.2018.04.238.
Qin, L., X. Gao, W. Li, and H. Ye. 2018b. “Modification of magnesium oxysulfate cement by incorporating weak acids.” J. Mater. Civ. Eng. 30 (9): 04018209. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002418.
Runčevski, T., C. Wu, H. Yu, B. Yang, and R. E. Dinnebier. 2013. “Structural characterization of a new magnesium oxysulfate hydrate cement phase and its surface reactions with atmospheric carbon dioxide.” J. Am. Ceram. Soc. 96 (11): 3609–3616. https://doi.org/10.1111/jace.12556.
Teague, A. J., and M. C. Lollback. 2012. “The beneficiation of ultrafine phosphate.” Miner. Eng. 27–28 (Feb): 52–59. https://doi.org/10.1016/j.mineng.2011.12.007.
Walling, S. A., and J. L. Provis. 2016. “Magnesia-based cements: A journey of 150 years, and cements for the future?” Chem. Rev. 116 (7): 4170–4204. https://doi.org/10.1021/acs.chemrev.5b00463.
Wang, N., H. Yu, W. Bi, Y. Tan, N. Zhang, C. Wu, H. Ma, and S. Hua. 2018. “Effects of sodium citrate and citric acid on the properties of magnesium oxysulfate cement.” Constr. Build. Mater. 169 (Apr): 697–704. https://doi.org/10.1016/j.conbuildmat.2018.02.208.
Wang, R., L. Qin, and X. Gao. 2020. “Mechanical strength and water resistance of magnesium oxysulfate cement based lightweight materials.” Cem. Concr. Compos. 109 (Jun): 103554. https://doi.org/10.1016/j.cemconcomp.2020.103554.
Wu, C., W. Chen, H. Zhang, H. Yu, W. Zhang, N. Jiang, and L. Liu. 2017. “The hydration mechanism and performance of Modified magnesium oxysulfate cement by tartaric acid.” Constr. Build. Mater. 144 (Jul): 516–524. https://doi.org/10.1016/j.conbuildmat.2017.03.222.
Wu, C., H. Yu, J. Dong, and L. Zheng. 2014. “Effects of material ratio, fly ash, and citric acid on magnesium oxysulfate cement.” ACI Mater. J. 111 (3): 291–297. https://doi.org/10.14359/51686723.
Wu, C., H. Yu, H. Zhang, J. Dong, J. Wen, and Y. Tan. 2015. “Effects of phosphoric acid and phosphates on magnesium oxysulfate cement.” Mater. Struct./Mater. et Constr. 48 (4): 907–917. https://doi.org/10.1617/s11527-013-0202-6.
Wu, J., J. Li, F. Rao, and W. Yin. 2020. “Mechanical property and structural evolution of alkali-activated slag-phosphate mine tailings mortars.” Chemosphere 251 (Jul): 126367. https://doi.org/10.1016/j.chemosphere.2020.126367.
Yan, X., D. Xu, and D. Xue. 2007. “ ions direct the one-dimensional growth of · · .” Acta Mater. 55 (17): 5747–5757. https://doi.org/10.1016/j.actamat.2007.06.023.
Yang, Y., Z. Wei, Y.-L. Chen, Y. Li, and X. Li. 2017. “Utilizing phosphate mine tailings to produce ceramisite.” Constr. Build. Mater. 155 (Nov): 1081–1090. https://doi.org/10.1016/j.conbuildmat.2017.08.070.
Yu, J., J. Qian, F. Wang, Z. Li, and X. Jia. 2020a. “Preparation and properties of a magnesium phosphate cement with dolomite.” Cem. Concr. Res. 138 (Dec): 106235. https://doi.org/10.1016/j.cemconres.2020.106235.
Yu, J., J. Qian, F. Wang, J. Qin, X. Dai, C. You, and X. Jia. 2020b. “Study of using dolomite ores as raw materials to produce magnesium phosphate cement.” Constr. Build. Mater. 253 (Aug): 119147. https://doi.org/10.1016/j.conbuildmat.2020.119147.
Zeng, X., H. Yu, and C. Wu. 2019. “An overview of study on basic magnesium sulfate cement and concrete in China (2012–2019).” KSCE J. Civ. Eng. 23 (10): 4445–4453. https://doi.org/10.1007/s12205-019-0199-7.
Zhang, N., H. Yu, H. Ma, Y. Diao, T. Liu, and C. Wu. 2021. “Effect of ammonium citrate tribasic on the hydration reaction and properties of magnesium oxysulfate cement.” J. Mater. Civ. Eng. 33 (11): 04021296. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003882.
Zheng, K., J. Zhou, and M. Gbozee. 2015. “Influences of phosphate tailings on hydration and properties of Portland cement.” Constr. Build. Mater. 98 (Nov): 593–601. https://doi.org/10.1016/j.conbuildmat.2015.08.115.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Nov 13, 2021
Accepted: Apr 20, 2022
Published online: Oct 12, 2022
Published in print: Dec 1, 2022
Discussion open until: Mar 12, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Yue Xiao, Xinjiang Ju, Chao Li, Tianlei Wang, Rui Wu, Research on Recycling of Phosphorus Tailings Powder in Open-Graded Friction Course Asphalt Concrete, Materials, 10.3390/ma16052000, 16, 5, (2000), (2023).
- Kairong Jin, Wanli Bi, Yan Guan, Xiaoyang Chen, Xiangming Zhou, Dezhi Wang, Performance of magnesium oxysulfate (MOS) cement with granite powders after combined sulfate and chloride attacks, Construction and Building Materials, 10.1016/j.conbuildmat.2022.130141, 366, (130141), (2023).