Galvanic Corrosion of Steel in Contact with Carbon-Polymer Composites. II: Experiments in Concrete
This article is a reply.
VIEW THE ORIGINAL ARTICLEPublication: Journal of Composites for Construction
Volume 6, Issue 2
Abstract
Studies were conducted to understand the galvanic interactions between CFRP and steel in chloride-contaminated concrete. CFRP-pultruded rod samples (6 mm in diameter), #3 deformed plain rebar (PR, uncoated), and #4 epoxy-coated reinforcing (ECR) steel bars were tested. After 350 days, potential measurements of CFRP and steel samples in chloride-contaminated concrete were −200 and −600 mV (versus CSE), respectively. These results confirm that chloride contamination in concrete could allow galvanic corrosion between CFRP and steel. The measured galvanic current densities were up to 0.7 and 100 μA/m2 for the CFRP-PR and CFRP-ECR couples, respectively, raising concerns about the degradation of both CFRP and steel. The results showed that PR steel was unaffected, as the corrosion rates estimated before and after the coupling with CFRP were similar. In contrast, coupling CFRP and ECR steel showed an increase of 10 times of the estimated corrosion rate, suggesting that galvanic interaction might affect the ECR steel.
Get full access to this article
View all available purchase options and get full access to this article.
References
Aguilar, A., Sagüés, A. A., and Powers, R. G. (1990). “In Corrosion rates of steel in concrete.” ASTM STP-1065, N. S. Berke, V. Chacker, and D. Whiting, eds., ASTM, Philadelphia, 66.
Alias, M. N., and Brown, R.(1993). “Corrosion behavior of carbon fiber composites in the marine environment.” Corros. Sci., 35(1–4), 395–402.
Andrade, C., Alonso, M. C., and Gonzalez, J. A. (1990). “An initial effort to use the corrosion rate measurements for estimating rebar durability.” Corrosion rates of steel in concrete, ASTM STP-1065, N. S. Berke, V. Chacker, and D. Whiting, eds., ASTM, Philadelphia, 29–37.
Andrade, C., Alonso, M. C., and Molina, F. J.(1993). “Cover cracking as a function of rebar corrosion: Part I—experimental test.” Mater. Struct., 26, 453–464.
AKZO. (1994). Technical Data Sheet 902A, Fortafil Fibers, Inc., Rockwood, Tenn.
Aylor, D. M. (1993). “The effect of a seawater environment on the galvanic corrosion behavior of graphite/epoxy composites coupled to metals.” High temperature and environmental effects on polymeric composites, ASTM STP-1174, C. E. Harris and T. S. Gates, eds., ASTM, Philadelphia, 81–94.
Fontana, M. G. (1986). Corrosion engineering, 3rd Ed., McGraw-Hill, New York.
Kaushik, D., Alias, M. N., and Brown, R.(1991). “An impedance study of a carbon fiber/vinyl ester composite.” Corrosion, 47(11), 859–867.
Rizkalla, S., and Tadros, G.(1994). “A smart highway bridge in Canada.” Concr. Int., 16(6), 42–44.
Sagüés, A. A. (1994). “Corrosion of epoxy coated rebar in Florida bridges.” Final Rep. to Florida D.O.T., WPI No. 0510603, FDOT Research Center, Tallahassee, Fla.
Taylor, S. R., Wall, F. D., and Cahen, G. L.(1996). “The detection and analysis of electrochemical damage in bismaleimide/graphite fiber composites.” J. Electrochem. Soc., 143(2), 449–458.
Torres-Acosta, A. A., Sagüés, A. A., and Sen, R. (1996). “Experiments in galvanic corrosion of steel in contact with CFRP composites in mortar and concrete.” Proc., 2nd International Conference on Advanced Composite Materials in Bridges and Structures: ACMBS-II, M. El-Badry, ed., Montreal, 141–148.
Torres-Acosta, A. A., Sagüés, A. A., and Sen, R. (1998). “Galvanic interaction between carbon fiber reinforced plastic (CFRP) compositesand steel in chloride contaminated concrete.” Paper No. 98648, CORROSION/98 International Annual Conference and Exposition, NACE International, Houston.
Torres-Acosta, A. A., Castro, P., and Sagüés, A. A. (1999). “Effect of the corrosion rate on the concrete cracking process.” Proc., XIV National Congress of the Mexican Electrochemical Society, Mérida, Mexico (in Spanish).
Torres-Acosta, A. A., and Sagües, A. A. (2000). “Concrete cover cracking with localized corrosion of reinforcing steel.” Proc., 5th CANMET/ACI Int. Conf. on Durability of Concrete, V. Malhotra, ed., American Concrete Institute, Farmington Hills, Mich., 591–611.
Tucker, W. C., Brown, R., and Russell, L.(1990). “Corrosion between a graphite/polymer composite and metals.” J. Composite Mats., 24(1), 92–102.
Information & Authors
Information
Published In
Copyright
Copyright © 2002 American Society of Civil Engineers.
History
Received: Jan 16, 2001
Accepted: Jul 13, 2001
Published online: Apr 15, 2002
Published in print: May 2002
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.