New Model for Estimating the Time-Variant Seismic Performance of Corroding RC Bridge Columns
Publication: Journal of Structural Engineering
Volume 141, Issue 6
Abstract
Corrosion of reinforcement is a predominant reason for reduced service lives of reinforced concrete (RC) structures exposed to aggressive environments. This deterioration process can lead to damage resulting in capacity loss or even structural failure, especially in coastal marine environments or where deicing or antiicing applications occur. Based on data from the National Bridge Inventory in 2010, the average bridge age in the country is 40 years old. Thirty percent of the bridges have exceeded 50 years, 7% have exceeded 75 years, and 25% are deemed deficient. For bridges exposed to chlorides (coastal areas or deicing or antiicing exposure), these older bridges often experience corrosion of the reinforcement. When reinforcement corrodes, the capacity of the structure is likely reduced, although little work has been reported on quantifying the reduction in performance and reliability. In seismic areas, this reduction in capacity may be magnified due to the loading demands during a seismic event. Therefore, understanding the time-variant risks associated with corroding structures will assist engineers and decision makers in making sound decisions with respect to optimization of design, inspection, repair, strengthening, and/or replacement of RC structures. This paper develops a new deterministic corrosion rate model and then uses the new model to assess the time-variant reliability of a corroding column subjected to a seismic event. The results indicate that corrosion can significantly reduce the reliability of an existing bridge column over relatively short durations.
Get full access to this article
View all available purchase options and get full access to this article.
References
Ahmad, S. (2003). “Reinforcement corrosion in concrete structures, its monitoring and service life prediction—A review.” Cem. Concr. Compos., 25(4–5), 459–471.
Ahmad, S., and B., Bhattacharjee (2000). “Empirical modeling of indicators of chloride-induced rebar corrosion.” J. Struct. Eng., 27(3), 195–207.
Alonso, C., Andrade, C., and González, J. A. (1988). “Relation between resistivity and corrosion rate of reinforcements in carbonated mortar made with several cement types.” Cem. Concr. Res., 18(5), 687–698.
Alonso, C., Andrade, C., Rodriguez, J., and Diez, J. M. (1998). “Factors controlling cracking of concrete affected by reinforcement corrosion.” Mater. Struct., 31(7), 435–441.
Andrade, C., Alonso, C., and Molina, F. J. (1993). “Cover cracking as a function of rebar corrosion: Part I—Experimental test.” Mater. Struct., 26(8), 453–464.
Andrade, C., et al. (2004). “Test methods for on-site corrosion rate measurement of steel reinforcement in concrete by means of the polarization resistance method.” Mater. Struct., 37(273), 623–643.
Balabanic, G., Bicanic, N., and Đureković, A. (1996). “The influence of ratio, concrete cover thickness and degree of water saturation on the corrosion rate of reinforcing steel in concrete.” Cem. Concr. Res., 26(5), 761–769.
Balafas, I., and Burgoyne, C. J. (2010). “Environmental effects on cover cracking due to corrosion.” Cem. Concr. Res., 40(9), 1429–1440.
Bazant, Z. P. (1979). “Physical model for steel corrosion in concrete sea structures—Application.” J. Struct. Div., 105(6), 1155–1166.
Bazant, Z. P., and Planas, J. (1998). Fracture and size effect in concrete and other quasibrittle materials, CRC Press, Boca Raton, FL.
Bertolini, L., Elsener, B., Pedeferri, P., Redaelli, E., and Polder, R. B. (2004). Corrosion of steel in concrete: Prevention, diagnosis, repair, Wiley-VCH, Weinheim, Germany.
Böhni, H. (2005). Corrosion in reinforced concrete structures, CRC Press, Boca Raton, FL.
Broomfield, J. P. (1997). Corrosion of steel in concrete: Understanding, investigation, and repair, E & FN Spon, London, New York.
Choe, D. E., Gardoni, P., Rosowsky, D., and Haukaas, T. (2009). “Seismic fragility estimates for reinforced concrete bridges subject to corrosion.” Struct. Saf., 31(4), 275–283.
DuraCrete. (2000). “Brite EuRam: DuraCrete—Final technical report. DuraCrete—Probabilistic performance based durability design of concrete structures.”, Brussels, Belgium.
Fang, C. Q., Lundgren, K., Chen, L., and Zhu, C. (2004). “Corrosion influence on bond in reinforced concrete.” Cem. Concr. Res., 34(11), 2159–2167.
Hussain, S. E., Rasheeduzzafar, X., Al-Musallam, A., and Al-Gahtani, A. S. (1995). “Factors affecting threshold chloride for reinforcement corrosion in concrete.” Cem. Concr. Res., 25(7), 1543–1555.
Jones, D. A. (1996). Principles and prevention of corrosion, Prentice Hall, Upper Saddle River, NJ.
Kent, D. C., and Park, R. (1971). “Flexural members with confined concrete.” J. Struct. Div., 97(ST7), 1969–1990.
Kirkpatrick, T. J., Weyers, R. E., Anderson-Cook, C. M., and Sprinkel, M. M. (2002). “Probabilistic model for the chloride-induced corrosion service life of bridge decks.” Cem. Concr. Res., 32, 1943–1960.
Kobayashi, K., and Shuttoh, K. (1991). “Oxygen diffusivity of various cementitious materials.” Cem. Concr. Res., 21(2–3), 273–284.
Li, C. Q. (2004). “Reliability based service life prediction of corrosion affected concrete structures.” J. Struct. Eng., 1570–1577.
Li, C. Q., Melchers, R. E., and Zheng, J. J. (2006). “Analytical model for corrosion-induced crack width in reinforced concrete structures.” ACI Struct. J., 103(4), 479–487.
Liu, T., and Weyers, R. W. (1998a). “Modeling the dynamic corrosion process in chloride contaminated concrete structures.” Cem. Concr. Res., 28(3), 365–379.
Liu, Y. P., and Weyers, R. E. (1998b). “Modeling the time-to-corrosion cracking in chloride contaminated reinforced concrete structures.” ACI Mater. J., 95(6), 675–681.
Lopez, W., and Gonzalez, J. A. (1993). “Influence of the degree of pore saturation on the resistivity of concrete and the corrosion rate of steel reinforcement.” Cem. Concr. Res., 23(2), 368–376.
Martinez, I., and Andrade, C. (2009). “Examples of reinforcement corrosion monitoring by embedded sensors in concrete structures.” Cem. Concr. Compos., 31(8), 545–554.
Mirza, S. A., MacGregor, J. G., and Hatzinikolas, M. (1979). “Statistical descriptions of strength of concrete.” J. Struct. Div., 105(6), 1021–1037.
Morris, W., Vico, A., and Vázquez, M. (2004). “Chloride induced corrosion of reinforcing steel evaluated by concrete resistivity measurements.” Electrochim. Acta, 49(25), 4447–4453.
Neville, A. M. (1996). Properties of concrete, 4th Ed., Wiley, New York, NY.
Otieno, M. B., Beushausen, H. D., and Alexander, M. G. (2011). “Modelling corrosion propagation in reinforced concrete structures—A critical review.” Cem. Concr. Compos., 33(2), 240–245.
Pour-Ghaz, M., Isgor, O. B., and Ghods, P. (2009). “The effect of temperature on the corrosion of steel in concrete. Part 1: Simulated polarization resistance tests and model development.” Corros. Sci., 51(2), 415–425.
Simon, J., Bracci, J. M., and Gardoni, P. (2010). “Seismic response and fragility of deteriorated reinforced concrete bridges.” J. Struct. Eng., 136(10), 1273–1281.
Song, H. W., and V., Saraswathy (2007). “Corrosion monitoring of reinforced concrete structures—A review.” Int. J. Electrochem. Sci., 2(1), 1–28.
Stewart, M. G., and Rosowsky, D. (1998). “Structural safety and serviceability of concrete bridges subject to corrosion.” J. Infrastruct. Syst., 146–155.
Torres-Acosta, A. A., and Sagues, A. A. (2004). “Concrete cracking by localized steel corrosion—Geometric effects.” ACI Mater. J., 101(6), 501–507.
Trejo, D., and Monteiro, P. J. (2005). “Corrosion performance of conventional (ASTM A615) and low-alloy (ASTM A706) reinforcing bars embedded in concrete and exposed to chloride environments.” Cem. Concr. Res., 35(3), 562–571.
Vu, K., Stewart, M. G., and Mullard, J. (2005). “Corrosion-induced cracking: Experimental data and predictive models.” ACI Struct. J., 102(5), 719–726.
Vu, K. A. T., and Stewart, M. G. (2000). “Structural reliability of concrete bridges including improved chloride-induced corrosion models.” Struct. Saf., 22(4), 313–333.
Wang, X. H., and Liu, X. L. (2004). “Modeling bond strength of corroded reinforcement without stirrups.” Cem. Concr. Res., 34(8), 1331–1339.
Yalçyn, H., and Ergun, M. (1996). “The prediction of corrosion rates of reinforcing steels in concrete.” Cem. Concr. Res., 26(10), 1593–1599.
Zhong, J. Q., Gardoni, P., and Rosowsky, D. (2010). “Stiffness degradation and time to cracking of cover concrete in reinforced concrete structures subject to corrosion.” J. Eng. Mech., 136(2), 209–219.
Information & Authors
Information
Published In
Journal of Structural Engineering
Volume 141 • Issue 6 • June 2015
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Aug 31, 2012
Accepted: Dec 2, 2013
Published online: Aug 1, 2014
Discussion open until: Jan 1, 2015
Published in print: Jun 1, 2015
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.