Severely Corroded RC with Cover Cracking
Publication: Journal of Structural Engineering
Volume 139, Issue 2
Abstract
It is not uncommon that cover cracking, spalling, and delamination occur in many corroding RC structures. Previous research has mainly been concerned with corrosion levels leading to cover cracking along the main reinforcement, whereas corrosion of stirrups is often overlooked. Corrosion phenomena, including stirrup corrosion, were studied in an experimental investigation presented in this paper. High levels of corrosion were reached, up to 20% of the main bars and 34% of the stirrups legs. The occurrence of crack initiation, propagation, and cover delamination were examined. The specimens had the shape of a beam end and were corroded with an accelerated method; an imposed current was used, taking care to keep the current density as low as practically possible for the duration of the laboratory testing. The effects of this process were compared with those of natural corrosion using models from the literature. The location of the bar, middle and corner placement, the amount of transverse reinforcement, and the corrosion level of longitudinal reinforcement and of transverse reinforcement were studied. The results concerning the concrete cracking in the experimental campaign are presented. The crack patterns and widths were analyzed, showing differences between specimens with or without stirrups and whether stirrups were corroding. Finally, the effect of corrosion was simulated as the expansion of corrosion products in a finite-element (FE) model, and the results, mainly the crack pattern and width, were compared with the test results. The conclusions addressed the importance of taking into consideration both high corrosion levels and corrosion of stirrups for the assessment of deteriorated structures.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The technical support for the specimen preparation and casting by Ing. Stefano Vacis and Geom. Giorgio Ghia – AVstrutture is gratefully acknowledged.
References
Al-Sulaimani, G. J., Kaleemulaah, M., Basunbul, I. A., and Rasheeduzzafar. (1990). “Influence of corrosion and cracking on bond behavior and strength of reinforced concrete members.” ACI Struct. J., 87(2), 220–231.
Almusallam, A. A., Al-Gahtani, A. S., and Rasheeduzzafar, A. R. A. (1996). “Effect of reinforcement corrosion on bond strength.” Constr. Build. Mater., 10(2), 123–129.
Alonso, C., Andrade, C., Rodriguez, J., and Diez, J. M. (1998). “Factors controlling cracking of concrete affected by reinforcement corrosion.” Mat. Struct./Matériaux et Constructions, 31(211), 435–441.
Auyeung, Y., Balaguru, P., and Chung, L. (2000). “Bond behavior of corroded reinforcement bars.” ACI Mater. J., 97(2), 214–221.
Berra, M., Castellani, A., Coronelli, D., Zanni, S., and Zhang, G. (2003). “Steel-concrete bond deterioration due to corrosion: FE analysis for different confinement levels.” Mag. Concr. Res., 55(3), 237–247.
Bhargava, K., Ghosh, A. K., Mori, Y., and Ramanujam, S. (2006). “Model for cover cracking due to rebar corrosion in RC structures.” Eng. Structures, 28(8), 1093–1109.
Clark, L. A., and Saifullah, M. (1993) “Effect of corrosion on reinforcement bond strength.” Proc., 5th Int. Conf. Structural Faults and Repair, V.3, M. Forde, ed., Engineering Technical Press, Edinburgh, Scotland, 113–119.
Coronelli, D., and Gambarova, P. (2004). “Structural assessment of corroded reinforced concrete beams: Modeling guidelines.” J. Struct. Eng., 130(8), 1214–1224.
DIANA [Computer software] Delft, Netherlands, TNO Building and Construction Research.
Féderation Internationale du béton (Fib). (2000). “Bond in reinforced concrete.” State-of-the-Art Rep. 10, Fib Féderation Internationale du béton, Lausanne, Switzerland.
Grassl, P., and Rempling, R. (2007). “Influence of volumetric–deviatoric coupling on crack prediction in concrete fracture tests.” Eng. Fract. Mech., 74(100), 1683–1693.
Higgins, C., and Farrow, W. C., III. (2006). “Tests of reinforced concrete beams with corrosion-damaged stirrups.” ACI Struct. J., 103(1), 133–141.
Hordijk, D. A. (1991) “Local approach to fatigue of concrete.” Ph.D. thesis, Delft Univ. of Technology, Delft, Netherlands.
ISO. (2009). “Corrosion of metals and alloys–Removal of corrosion products from corrosion test specimens.” ISO 8407, Geneva.
Liu, Y., and Weyers, R. E. (1998). “Modeling the time-to-corrosion cracking in chloride contaminated reinforced concrete structures.” ACI Mater. J., 95(6), 675–681.
Lundgren, K. (2005a). “Bond between ribbed bars and concrete. Part 1: Modified model.” Mag. Concr. Res., 57(7), 371–382.
Lundgren, K. (2005b). “Bond between ribbed bars and concrete. Part 2: The effect of corrosion.” Mag. Concr. Res., 57(7), 383–395.
Lundgren, K., Roman, S. A. S., Schlune, H., Hanjari, K. Z., and Kettil, P. (2007). “Effects on bond of reinforcement corrosion.” Int. RILEM Workshop on Integral Service Life Modeling of Concrete Structures, RILEM Publications S.A.R.L., Bagneux, France, 231–238.
Molina, F. J., Alonso, C., and Andrade, C. (1993). “Cover cracking as a function of rebar corrosion. 2. Numerical- model.” Mater. Struct., 26(9), 532–548.
Mullard, J. A., and Stewart, M. G. (2011). “Corrosion-induced cover cracking: New test data and predictive models.” ACI Struct. J., 108(1), 71–79.
Sæther, I. (2011). “Bond deterioration of corroded steel bars in concrete.” Struct. Infrastruct, Eng:, 7(6), 415–429.
Thorenfeldt, E., Tomaszewicz, A., and Jensen, J. J. (1987). “Mechanical properties of high-strength concrete and applications in design.” Proc., Symp. Utilization of High-Strength Concrete, Stavanger, Norway.
Val, D. V., Chernin, L., and Stewart, M. G. (2009). “Experimental and numerical investigation of corrosion-induced cover cracking in reinforced concrete structures.” J. Struct. Eng., 135(4), 376–385.
Vidal, T., Castel, A., and François, R. (2004). “Analyzing crack width to predict corrosion in reinforced concrete.” Cement Concr. Res., 34(1), 165–174.
Yuan, Y., Ji, Y., and Shah, S. P. (2007). “Comparison of two accelerated corrosion techniques for concrete structures.” ACI Struct. J., 104(3), 344–347.
Zandi Hanjari, K., Coronelli, D., and Lundgren, K. (2011a). “Bond capacity of severely corroded bars with corroded stirrups.” Mag. Concr. Res., 63(12), 953–968.
Zandi Hanjari, K., Kettil, P., and Lundgren, K. (2011b). “Analysis of the mechanical behavior of corroded reinforced concrete structures.” ACI Struct. J., 108(5), 532–541.
Zandi Hanjari, K., Lundgren, K., Plos, M., Coronelli, D. (2011c). “Three-dimensional modelling of structural effects of corroding steel reinforcement in concrete,” Structure and Infrastructure Engineering, Taylor & Francis, London.
Information & Authors
Information
Published In
Journal of Structural Engineering
Volume 139 • Issue 2 • February 2013
Pages: 221 - 232
Copyright
© 2013 American Society of Civil Engineers.
History
Received: Jul 23, 2011
Accepted: Apr 24, 2012
Published online: Apr 26, 2012
Published in print: Feb 1, 2013
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.