Multi-Index Evaluation for Anticracking Performance of Epoxy Porous Asphalt Mixtures Based on Overlay Test
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 12
Abstract
Porous asphalt pavement have been widely employed for various functions. However, due to its large voids and small contact area between particles, the reflective cracks results from semirigid base layer shrinkage cracking and buttom-up fatigue cracking are easy to occur, under long-term multifield coupling influenced by load, temperature, water, light and other factors of natural conditions. Therefore, improving asphalt crack resistance is a key issue. Using an overlay test with a high-viscosity porous asphalt mixture (HPA-13) as a control object, a multi-index evaluation was performed to test the anticracking performance of an epoxy porous asphalt mixture (EPA-13) under different temperatures and aging conditions. Results showed that epoxy asphalt binders can considerably improve the anticracking performance of porous asphalt mixtures; under the standard condition of 25°C, the number of loading cycles () of EPA-13 was 7.5 times higher than that of HPA-13. However, EPA-13 was greatly affected by low temperature and aging conditions; in particular, under the low temperature condition of 10°C, decreased by 93.5%. In the multi-index evaluation of crack resistance, the gray correlation degree of each evaluation index followed the order of the allowable failure times with () > cumulative fracture energy () > displacement at the maximum load of the first cycle () > fracture energy of the first cycle () > average fracture energy () > maximum load of the first cycle (). It is recommended to use , , and to evaluate the crack resistance of porous asphalt mixtures.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and codes generated or used during the study appear in the published article.
Acknowledgments
All authors reviewed the results and approved the final version of the manuscript. The authors gratefully acknowledge the financial support from the Yunnan Research Institute of Highway Science and Technology.
References
Alvarez, A. E., A. Epps-Martin, C. Estakhri, and R. Izzo. 2010. “Evaluation of durability tests for permeable friction course mixtures.” Int. J. Pavement Eng. 11 (1): 49–60. https://doi.org/10.1080/10298430902730539.
Deng, J. 1987. The basic method of grey system. Wuhan, China: Huazhong Institute of Technology Press.
Du, J., A. Rahman, Z. Zhou, C. Ai, and Y. Qiu. 2021. “Enhancement effect of the aggregate particles on the low-temperature cracking resistance of the asphalt mortar.” Constr. Build. Mater. 290 (Jul): 123225. https://doi.org/10.1016/j.conbuildmat.2021.123225.
Garcia, V., J. Garibay, I. Abdalah, and S. Nazarian. 2016. “Performance of the overlay tester in monotonic and cyclic loading modes.” In Proc., Int. Conf. on Transportation and Development 2016, 181–191. Austin, TX: Oklahoma State Univ. https://doi.org/10.1061/9780784479926.017.
Germann, F. P., and R. L. Lyttton. 1979. Methodology for predicting the reflective cracking life of asphalt concrete overlays. Interim Report. College Station, TX: Texas A&M Univ.
Gu, F., X. Luo, Y. Zhang, and R. L. Lyttton. 2015. “Using overlay test to evaluate fracture properties of field-aged asphalt concrete.” Constr. Build. Mater. 101 (Dec): 1059–1068. https://doi.org/10.1016/j.conbuildmat.2015.10.159.
He, Q., H. Zhang, J. Li, and H. Duan. 2021. “Performance evaluation of polyurethane/epoxy resin modified asphalt as adhesive layer material for steel-UHPC composite bridge deck pavements.” Constr. Build. Mater. 291 (Jul): 123364. https://doi.org/10.1016/j.conbuildmat.2021.123364.
Herrington, P., and D. Alabaster. 2008. “Epoxy modified open-graded porous asphalt.” Road Mater. Pavement Des. 9 (3): 481–498. https://doi.org/10.1080/14680629.2008.9690129.
Hu, X., Z. Wang, F. Zhou, and Y. Wu. 2014. “Rapid evaluation method for reflective crack of asphalt mixture.” [In Chinese.] J. China Foreign Highway 34 (2): 221–225. https://doi.org/10.14048/j.issn.1671-2579.2014.02.054.
Jabonero, C., J.-W. Park, S. Ryu, W. Lin, and Y.-h. Cho. 2020. “Development of a multi-modal overlay tester for the evaluation of asphalt overlay cracking behaviors.” Can. J. Civ. Eng. 47 (11): 1258–1266. https://doi.org/10.1139/cjce-2019-0227.
Li, X., W. Huang, and Z. Qian. 2013. “Fracture test based on improved overlay tester asphalt mixture.” J. Southeast Univ. (Engl. Ed.). 29 (3): 294–299. https://doi.org/10.3969/j.issn.1003-7985.2013.03.012.
Li, X., J. Shen, T. Ling, and F. Yuan. 2022. “Fatigue properties of aged porous asphalt mixtures with an epoxy asphalt binder.” J. Mater. Civ. Eng. 34 (3): 04021488. https://doi.org/10.1061/(ASCE)MT.1943-5533.0004130.
Lu, Q., C. Xin, M. Alamri, and M. Alharthai. 2021. “Development of porous asphalt mixture with bio-based epoxy asphalt.” J. Cleaner Prod. 317 (Oct): 128404. https://doi.org/10.1016/J.JCLEPRO.2021.128404.
Luo, S., Q. Lu, and Z. Qian. 2015. “Performance evaluation of epoxy modified open-graded porous asphalt concrete.” Constr. Build. Mater. 76 (Feb): 97–102. https://doi.org/10.1016/j.conbuildmat.2014.11.057.
MTPRC (Ministry of Transport of the People’s Republic of China). 2004. Technical specification for construction of highway asphalt pavements. Beijing: Ministry of Communications.
Qian, Z., and Q. Lu. 2015. “Design and laboratory evaluation of small particle porous epoxy asphalt surface mixture for roadway pavements.” Constr. Build. Mater. 77 (Feb): 110–116. https://doi.org/10.1016/j.conbuildmat.2014.12.056.
TxDOT (Texas Department of Transportation). 2021. Overlay test. Austin, TX: TxDOT.
Walubita, L. F., A. N. M. Faruk, J. Zhang, and X. Hu. 2015. “Characterizing the cracking and fracture properties of geosynthetic interlayer reinforced HMA samples using the Overlay Tester (OT).” Constr. Build. Mater. 93 (Sep): 695–702. https://doi.org/10.1016/j.conbuildmat.2015.06.028.
Walubita, L. F., L. Fuentes, S. I. Lee, O. Guerrero, E. Mahmoud, B. Naik, and G. S. Simate. 2021. “Correlations and preliminary validation of the laboratory monotonic overlay test (OT) data to reflective cracking performance of in-service field highway sections.” Constr. Build. Mater. 267 (Jan): 121029. https://doi.org/10.1016/j.conbuildmat.2020.121029.
Wei, J., T. Fu, and J. Liang. 2021. “Fracture performance of a large-stone asphalt mixture based on a monotonic tensile overlay test.” Adv. Civ. Eng. 6622024 (Jan): 1–11. https://doi.org/10.1155/2021/6622024.
Wei, J., J. Shi, and J. Liang. 2020. “Overlay test to investigate the crack propagation of a large-size asphalt mixture.” J. Mater. Civ. Eng. 32 (5): 04020097. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003164.
Wu, X. 2016. “Research on the fracture resistance of different types of asphalt mixture based on the overlay tester.” In Proc., 4th Int. Conf. on Sustainable Energy & Environmental Engineering. Amsterdam, Netherlands: Atlantis Press.
Xu, W., X. Wei, J. Wei, and Z. Chen. 2020. “Experimental evaluation of the influence of aggregate strength on the flexural cracking behavior of epoxy asphalt mixtures.” Materials (Basel) 13 (8): 1876. https://doi.org/10.3390/ma13081876.
Yan, K., S. Wang, S. Tian, J. Chen, and H. Sun. 2020. “Research on anti-reflective cracking performance of stress-absorption interlayer based on overlay test.” [In Chinese.] J. Hunan Univ. (Nat. Sci.). 47 (1): 108–115. https://doi.org/10.16339/j.cnki.hdxbzkb.2020.01.013.
Yang, D., H. R. Karimi, and M. R. M. Aliha. 2021. “Comparison of testing method effects on cracking resistance of asphalt concrete mixtures.” Appl. Sci. 11 (11): 5094. https://doi.org/10.3390/app11115094.
Zhai, R., Y. Chen, Q. Yu, W. Yuan, and Z. Zeng. 2017. “Evaluation of cracking-resistance potential of large stone permeable of asphalt mixture based on overlay tester.” [In Chinese.] J. Funct. Mater. 48 (9): 9129–9135. https://doi.org/10.3969/j.issn.1001-9731.2017.09.023.
Zhai, R., P. Hao, G. Li, Z. Zeng, and W. Li. 2018. “Anti-reflection cracking performance of asphalt mixture under freeze-thaw cycles.” [In Chinese.] J. Build. Mater. 2018 (6): 150–154. https://doi.org/10.3969/j.issn.1007-9629.2018.06.022.
Zhang, H., Z. Chen, G. Xu, and C. Shi. 2018. “Evaluation of aging behaviors of asphalt binders through different rheological indices.” Fuel 221 (Jun): 78–88. https://doi.org/10.1016/j.fuel.2018.02.087.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Nov 19, 2021
Accepted: Apr 1, 2022
Published online: Sep 28, 2022
Published in print: Dec 1, 2022
Discussion open until: Feb 28, 2023
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.