Effect of Seawater on Hydration and Sulfate Resistance of Noncement Mortars
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 8
Abstract
Modern concrete construction consumes significant amounts of freshwater, which is a valuable natural resource. Using seawater can be an alternative solution to reduce freshwater consumption for sustainable development. The durability of seawater construction materials should be studied for better understanding of their long-term behavior. This study investigated the effect of seawater on the hydration and the sulfate resistance of noncement mortars prepared by mixing ground granulated blast furnace slag (BFS), carbide slag (CS), and silica fume (SF) to understand the feasibility of using seawater and solid waste materials to develop low-carbon construction materials. CS in the mix acted as an alkali activator for the hydration and strength development of the solid wastes. Two batch specimens were prepared, one batch mixed with seawater and the other mixed with freshwater for comparison. A compressive test investigated the effect of seawater on the mechanical properties. Heat flow, X-ray diffractometry (XRD), and thermogravimetry tests were used to understand the hydration. The results suggest that the seawater could accelerate the hydration by producing a large amount of hydrocalumite, which improves the compressive strength at early ages. Durability testing was carried out by immersing specimens in a sulfate solution for various durations. Sulfate resistance was characterized by XRD, and ettringite and Friedel’s salt were the main corrosion products when the specimens were immersed in sulfate solution. Corrosion could be reduced by seawater in the specimens. Scanning electron microscopy was used to characterize the microstructure of the hydration products, which showed that the corrosion was a progressive process. A loose and porous microstructure of the specimen surface accelerated corrosion of the noncement specimens.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
The third author gratefully acknowledges the financial support provided by the National Natural Science Foundation of China (51911530208 and 51978025) and the Thousand Talents Plan (Young Professionals).
References
Angulo-Ramírez, D. E., R. Mejía de Gutiérrez, and F. Puertas. 2017. “Alkali-activated Portland blast-furnace slag cement: Mechanical properties and hydration.” Constr. Build. Mater. 140 (Jun): 119–128. https://doi.org/10.1016/j.conbuildmat.2017.02.092.
Blanco, F., M. P. Garcia, J. Ayala, G. Mayoral, and M. A. Garcia. 2006. “The effect of mechanically and chemically activated fly ashes on mortar properties.” Fuel 85 (14–15): 2018–2026. https://doi.org/10.1016/j.fuel.2006.03.031.
Cabrera, J., and M. F. A. Rojas. 2001. “Mechanism of hydration of the metakaolin–lime–water system.” Cem. Concr. Res. 31 (2): 177–182. https://doi.org/10.1016/S0008-8846(00)00456-7.
Dehghani, A., F. Aslani, and N. Ghaebi Panah. 2021. “Effects of initial molar ratio and slag on fly ash-based ambient cured geopolymer properties.” Constr. Build. Mater. 293 (Jul): 123527. https://doi.org/10.1016/j.conbuildmat.2021.123527.
Fernandez, A., G. Calvo, and M. C. Alonso. 2018. “Ordinary Portland cement composition for the optimization of the synergies of supplementary cementitious materials of ternary binders in hydration processes.” Cem. Concr. Compos. 89 (May): 238–250. https://doi.org/10.1016/j.cemconcomp.2017.12.016.
Gijbels, A., Y. Pontikes, P. Samyn, S. Schreurs, and W. Schroeyers. 2020. “Effect of NaOH content on hydration, mineralogy, porosity and strength in alkali/sulfate-activated binders from ground granulated blast furnace slag and phosphogypsum.” Cem. Concr. Res. 132 (Jun): 106054. https://doi.org/10.1016/j.cemconres.2020.106054.
Jansen, D., F. Goetz-Neunhoeffer, C. Stabler, and J. Neubauer. 2011. “A remastered external standard method applied to the quantification of early OPC hydration.” Cem. Concr. Res. 41 (6): 602–608. https://doi.org/10.1016/j.cemconres.2011.03.004.
Jeon, D., Y. Jun, Y. Jeong, and J. S. Oh. 2015. “Microstructural and strength improvements through the use of in a cementless -activated Class F fly ash system.” Cem. Concr. Res. 67 (Jan): 215–225. https://doi.org/10.1016/j.cemconres.2014.10.001.
Jeon, D., W. S. Yum, Y. Jeong, and J. E. Oh. 2018. “Properties of quicklime (CaO)-activated Class F fly ash with the use of .” Cem. Concr. Res. 111 (Sep): 147–156. https://doi.org/10.1016/j.cemconres.2018.05.019.
Juenger, M. C. G., F. Winnefeld, J. L. Provis, and J. H. Ideker. 2011. “Advances in alternative cementitious binders.” Cem. Concr. Res. 41 (12): 1232–1243. https://doi.org/10.1016/j.cemconres.2010.11.012.
Kim, M. S., Y. Jun, C. Lee, and J. E. Oh. 2013. “Use of CaO as an activator for producing a price-competitive non-cement structural binder using ground granulated blast furnace slag.” Cem. Concr. Res. 54 (Dec): 208–214. https://doi.org/10.1016/j.cemconres.2013.09.011.
Li, H., N. Farzadnia, and C. J. Shi. 2018. “The role of seawater in interaction of slag and silica fume with cement in low water-to-binder ratio pastes at the early age of hydration.” Constr. Build. Mater. 185 (Oct): 508–518. https://doi.org/10.1016/j.conbuildmat.2018.07.091.
Olivier, J. G. J., G. Janssens-Maenhout, M. Muntean, and J. A. H. Peters. 2016. “Trends in global emissions.” Accessed December 6, 2016. https://www.pbl.nl/en/publications/trends-in-global-co2-emissions-2016-report.
Paris, J. M., J. G. Roessler, C. C. Ferraro, H. D. DeFord, and T. G. Townsend. 2016. “A review of waste products utilized as supplements to Portland cement in concrete.” J. Cleaner Prod. 121 (May): 1–18. https://doi.org/10.1016/j.jclepro.2016.02.013.
Provis, J. L., A. Palomo, and C. J. Shi. 2015. “Advances in understanding alkali-activated materials.” Cem. Concr. Res. 78 (Dec): 110–125. https://doi.org/10.1016/j.cemconres.2015.04.013.
Qian, J. S., C. J. Shi, and Z. Wang. 2001. “Activation of blended cements containing fly ash.” Cem. Concr. Res. 31 (8): 1121–1127. https://doi.org/10.1016/S0008-8846(01)00526-9.
Ragoug, R., O. O. Metalssi, F. Barberon, J.-M. Torrenti, N. Roussel, L. Divet, and J.-B. d’Espinose de Lacaillerieg. 2019. “Durability of cement pastes exposed to external sulfate attack and leaching: Physical and chemical aspects.” Cem. Concr. Res. 116 (Feb): 134–145. https://doi.org/10.1016/j.cemconres.2018.11.006.
SAC (Standardization Administration of the People’s Republic of China). 1999. Method of testing cements-Determination of strength. Beijing: SAC.
SAC (Standardization Administration of the People’s Republic of China). 2017. China ISO standard sand. Beijing: SAC.
Shi, C. J. 1996. “Early microstructure development of activated lime-fly ash pastes.” Cem. Concr. Res. 26 (9): 1351–1359. https://doi.org/10.1016/0008-8846(96)00123-8.
Shi, C. J., and R. L. Day. 1995. “Acceleration of the reactivity of fly ash by chemical activation.” Cem. Concr. Res. 25 (1): 15–21. https://doi.org/10.1016/0008-8846(94)00107-A.
Shi, C. J., and R. L. Day. 2000. “Pozzolanic reaction in the presence of chemical activators: Part I. Reaction kinetics.” Cem. Concr. Res. 30 (1): 51–58. https://doi.org/10.1016/S0008-8846(99)00205-7.
Shi, C. J., and R. L. Day. 2001. “Comparison of different methods for enhancing reactivity of pozzolans.” Cem. Concr. Res. 31 (5): 813–818. https://doi.org/10.1016/S0008-8846(01)00481-1.
Shi, C. J., A. F. Jiménez, and A. Palomo. 2011. “New cements for the 21st century: The pursuit of an alternative to Portland cement.” Cem. Concr. Res. 41 (7): 750–763. https://doi.org/10.1016/j.cemconres.2011.03.016.
Thomas, J. J., H. M. Jennings, and J. J. Chen. 2009. “Influence of nucleation seeding on the hydration mechanisms of tricalcium silicate and cement.” J. Phys. Chem. C 113 (11): 4327–4334. https://doi.org/10.1021/jp809811w.
Xiao, J., C. Qiang, A. Nanni, and K. Zhang. 2017. “Use of sea-sand and seawater in concrete construction: Current status and future opportunities.” Constr. Build. Mater. 155 (Nov): 1101–1111. https://doi.org/10.1016/j.conbuildmat.2017.08.130.
Yang, K.-H., A.-R. Cho, J.-K. Song, and S.-H. Nam. 2012. “Hydration products and strength development of calcium hydroxide-based alkali-activated slag mortars.” Constr. Build. Mater. 29 (Apr): 410–419. https://doi.org/10.1016/j.conbuildmat.2011.10.063.
Yuan, J., L. Li, P. He, Z. Chen, C. Lao, D. Jia, and Y. Zhou. 2021. “Effects of kinds of alkali-activated ions on geopolymerization process of geopolymer cement pastes.” Constr. Build. Mater. 293 (Jul): 123536. https://doi.org/10.1016/j.conbuildmat.2021.123536.
Zhang, S., Z. Li, B. Ghiassi, S. Yin, and G. Ye. 2021. “Fracture properties and microstructure formation of hardened alkali-activated slag/fly ash pastes.” Cem. Concr. Res. 144 (Jun): 106447. https://doi.org/10.1016/j.cemconres.2021.106447.
Zhao, G., J. Li, and W. Shao. 2018. “Effect of mixed chlorides on the degradation and sulfate diffusion of cast-in-situ concrete due to sulfate attack.” Constr. Build. Mater. 181 (Aug): 49–58. https://doi.org/10.1016/j.conbuildmat.2018.05.251.
Information & Authors
Information
Published In
Copyright
© 2022 American Society of Civil Engineers.
History
Received: Aug 26, 2021
Accepted: Dec 9, 2021
Published online: May 25, 2022
Published in print: Aug 1, 2022
Discussion open until: Oct 25, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.