Effect of Cement and Fly Ash Dosages on the Characteristics and Performance of Microsurfacing Mix
Publication: Journal of Materials in Civil Engineering
Volume 34, Issue 2
Abstract
In this study, the role of mineral fillers on the microsurfacing mix characteristics and performance was assessed for 10 different combinations of mineral filler type (cement and fly ash) and dosages (0%–3%). The mixes were initially characterized in terms of compatibility, cohesion, and adhesion using Schulze-Breuer and Ruck test, cohesion test, and boiling water test, respectively. Subsequently, the performance of microsurfacing mixes, that is, raveling and rutting resistance, was determined using wet track abrasion test and loaded wheel test, respectively. Results indicated that the filler–emulsion system’s compatibility improved significantly with the addition of cement at the proper dosage. In contrast, mixes with only fly ash as mineral filler had inferior filler–emulsion compatibility. Also, the rate of strength development and adhesion was higher with cement than fly ash. The performance, that is, raveling and rutting resistance, positively correlates with the 60-min cohesion, adhesion, and compatibility (abrasion loss). Interestingly, the combination with 2% cement and 1% fly ash as mineral filler had the best mix characteristic and performance, indicating that the careful selection of the type and the dosage of mineral filler could maximize the durability of the microsurfacing mix.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
Acknowledgments
The authors acknowledge the support provided by IIT Guwahati for experiments and analysis. The authors are grateful to Om Infracon Pvt. Ltd. and Hincol Pvt. Ltd. for providing the material support required for the study. Also, the authors highly appreciate the laboratory support provided by IRMS Lab, IIT Kanpur, for sample testing using XRF.
References
American Coal Ash Association. 2003. Fly ash facts for highway engineers. Washington, DC: USDOT, Federal Highway Administration.
ASTM. 2019a. Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete. ASTM C618. West Conshohocken, PA: ASTM.
ASTM. 2019b. Standard specification for mineral filler for asphalt mixtures. ASTM D242/D242M. West Conshohocken, PA: ASTM.
Bhargava, N., A. K. Siddagangaiah, and T. L. Ryntathiang. 2019. “State of the art review on design and performance of microsurfacing.” Road Mater. Pavement Des. 21 (8): 2091–2125. https://doi.org/10.1080/14680629.2019.1607771.
Broughton, B., and S.-J. Lee. 2012. Microsurfacing in Texas. FHWA/TX-12/0-6668-1. Austin, TX: Texas DOR.
Du, S. 2014a. “Effect of different fillers on performance properties of asphalt emulsion mixture.” J. Test. Eval. 42 (1): 126–134. https://doi.org/10.1520/JTE20130020.
Du, S. 2014b. “Interaction mechanism of cement and asphalt emulsion in asphalt emulsion mixtures.” Mater. Struct. 47 (7): 1149–1159. https://doi.org/10.1617/s11527-013-0118-1.
Fang, X., A. Garcia-Hernandez, and P. Lura. 2016. “Overview on cold cement bitumen emulsion asphalt.” RILEM Tech. Lett. 1: 116–121. https://doi.org/10.21809/rilemtechlett.2016.23.
Fooladi, A., and S. Hesami. 2021. “Experimental investigation of the effect of types of fillers on the performance of microsurfacing asphalt mixture.” J. Mater. Civ. Eng. 33 (7): 04021139. https://doi.org/10.1061/(ASCE)MT.1943-5533.0003512.
García, A., P. Lura, M. N. Partl, and I. Jerjen. 2013. “Influence of cement content and environmental humidity on asphalt emulsion and cement composites performance.” Mater. Struct. 46 (8): 1275–1289. https://doi.org/10.1617/s11527-012-9971-6.
Gransberg, D. D. 2010. NCHRP Synthesis 411: Microsurfacing; a synthesis of highway practices. Washington, DC: Transportation Research Board of the National Academies.
Hixon, C. D., and D. A. Ooten. 1993. “Nine years of microsurfacing in Oklahoma.” In vol. 1392 of Proc., Transportation Research Board, National Research Council, 13–19. Washington, DC: TRB.
InstroTek. n.d. “ACT: Asphalt compatibility tester.” Accessed July 24, 2019. https://web.archive.org/web/20190724125928/https://cdn.shopify.com/s/files/1/1245/4913/files/ACT_Manual_ver_3.pdf?20.
IRC (Indian Roads Congress). 2008. Tentative specifications for slurry seal and microsurfacing. New Delhi, India: IRC.
ISSA (International Slurry Surfacing Association). 2010. Recommended performance guideline for micro surfacing. Glen Ellyn, IL: ISSA.
ISSA TB (International Slurry Surfacing Association). 2005. Test method for boiling compatibility of slurry seal mixes. Glen Ellyn, IL: ISSA.
ISSA TB (International Slurry Surfacing Association). 2013. Test method for classification of slurry surfacing materials compatibility by Schulze-Breuer and Ruck procedures. Glen Ellyn, IL: ISSA.
ISSA TB (International Slurry Surfacing Association). 2017. Test method to determine set and cure development of slurry surfacing systems by cohesion tester. Glen Ellyn, IL: ISSA.
Li, Y., Y. Lyv, L. Fan, and Y. Zhang. 2019. “Effects of cement and emulsified asphalt on properties of mastics and 100% cold recycled asphalt mixtures.” Materials 12 (5): 754. https://doi.org/10.3390/ma12050754.
Little, D. N., and J. C. Petersen. 2005. “Unique effects of hydrated lime filler on the performance-related properties of asphalt cements: Physical and chemical interactions revisited.” J. Mater. Civ. Eng. 17 (2): 207–218. https://doi.org/10.1061/(ASCE)0899-1561(2005)17:2(207).
Nikolaides, A., and N. Oikonomou. 2000. “The use of fly ash as a substitute of cement in microsurfacing.” Waste Mater. Constr. 1: 234–240. https://doi.org/10.1016/S0713-2743(00)80035-5.
Patel, N., and R. Gujar. 2017. “Evaluation of performance of high calcium fly ash as a mineral filler in mix design of microsurfacing of road pavement.” Civ. Eng. Urban Plann. Int. J. 4 (2): 49–58. https://doi.org/10.5121/civej.2017.4204.
Pederson, C. M., and C. D. Hixon. 1988. “Microsurfacing with natural latex-modified asphalt emulsion: A field evaluation.” Transp. Res. Rec. 1171: 108–112.
Raza, H. 1994. State-of-the-practice: Design, construction, and performance of micro-surfacing. Washington, DC: FHWA.
Robati, M., A. Carter, and D. Perraton. 2015. “New conceptual model for filler stiffening effect on asphalt mastic of microsurfacing.” J. Mater. Civ. Eng. 27 (11): 04015033. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001264.
Syed, I. M., T. J. Freeman, and R. E. Smith. 1998. “Effectiveness of highway maintenance treatments used in Texas.” Flexible pavement rehabilitation and maintenance, ASTM STP 1348, 136–150. West Conshohocken, PA: ASTM.
Takamura, K., and A. James. 2015. “Paving with asphalt emulsions.” In Advances in asphalt materials, 393–426. Amsterdam, Netherlands: Elsevier.
Thomas, M. D. A. 2007. Vol. 5420 of Optimizing the use of fly ash in concrete. Skokie, IL: Portland Cement Association.
Yang, Y., Y. Yang, and B. Qian. 2019. “Performance and microstructure of cold recycled mixes using asphalt emulsion with different contents of cement.” Materials 12 (16): 2548. https://doi.org/10.3390/ma12162548.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: Jan 29, 2021
Accepted: Jun 17, 2021
Published online: Nov 25, 2021
Published in print: Feb 1, 2022
Discussion open until: Apr 25, 2022
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.
Cited by
- Ramin Khafajeh, Mohsen Shamsaei, Ali Latifi, Babak Amin Javaheri, Michel Vaillancourt, Comprehensive Investigation of Influential Mix-Design Factors on the Microsurfacing Mixture Performance, Journal of Materials in Civil Engineering, 10.1061/JMCEE7.MTENG-15212, 35, 7, (2023).