Effect of Carbonation Curing on Portland Cement Attack: Laboratory Characterization at 900 Days
Publication: Journal of Materials in Civil Engineering
Volume 33, Issue 4
Abstract
Sulfate exposure at low temperatures is known to accelerate chemical deterioration in limestone cement concrete by promoting thaumasite formation. Carbonation curing as an emerging sequestration strategy converts gaseous into mineral calcite, a key species that incurs thaumasite formation in conventional limestone cements. To clarify the risk of thaumasite sulfate attack after carbonation curing, this paper presents a laboratory characterization of carbonation-cured mortars stored in a solution at 6°C for up to 900 days. It was found that carbonation curing suppressed mortar swelling and enhanced material mechanical integrity and dimensional stability. The mineral thaumasite and gypsum were significantly lessened after carbonation curing. The maximum longitudinal expansion of mortar bars during exposure was lowered from to less than 0.06% by carbonation curing. The compressive strength of carbonation-cured mortars remained higher than 60 MPa whereas the noncarbonated control decreased to less than 2 MPa. Moreover, mortar critical pore diameter after storage decreased from (noncarbonated) to (carbonation-cured), with the total pore volume lowered by resulting from carbonation curing. The pore densification led by calcium carbonate precipitation tends to limit ingress and prevent mortar interior damage. It was concluded that the calcium carbonate converted from through carbonation curing did not promote thaumasite formation, and material durability with respect to thaumasite sulfate attack could be further enhanced after carbonation curing.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
No data, models, or code were generated or used during the study.
Acknowledgments
Financial support for Dr. Beata Jaworska was provided by the Dr. Anatole S. and Pamela D. Dekaban Fund through the Dekaban Fellowship in 2018–2019.
References
Aguilera, J., S. Martınez-Ramırez, I. Pajares-Colomo, and M. Blanco-Varela. 2003. “Formation of thaumasite in carbonated mortars.” Cem. Concr. Compos. 25 (8): 991–996. https://doi.org/10.1016/S0958-9465(03)00121-5.
ASTM 2017. Standard test method for length change of hardened hydraulic-cement mortar and concrete. ASTM C157. West Conshohocken, PA: ASTM.
ASTM 2020. Standard test method for compressive strength of hydraulic cement mortars [Using 2-in. or (50 mm) cube specimens]. ASTM C109. West Conshohocken, PA: ASTM.
Bellmann, F. 2004. “On the formation of thaumasite : Part II.” Adv. Cem. Res. 16 (3): 89–94. https://doi.org/10.1680/adcr.2004.16.3.89.
Bellmann, F. 2007. “On the formation of thaumasite : Part III.” Adv. Cem. Res. 19 (4): 139–146. https://doi.org/10.1680/adcr.2007.19.4.139.
Bellmann, F., and J. Stark. 2007. “Prevention of thaumasite formation in concrete exposed to sulphate attack.” Cem. Concr. Res. 37 (8): 1215–1222. https://doi.org/10.1016/j.cemconres.2007.04.007.
Bellmann, F., and J. Stark. 2008. “The role of calcium hydroxide in the formation of thaumasite.” Cem. Concr. Res. 38 (10): 1154–1161. https://doi.org/10.1016/j.cemconres.2008.04.005.
Bensted, J. 2003. “Thaumasite––Direct, woodfordite and other possible formation routes.” Cem. Concr. Compos. 25 (8): 873–877. https://doi.org/10.1016/S0958-9465(03)00115-X.
Berger, R., J. Young, and K. Leung. 1972. “Acceleration of hydration of calcium silicates by carbon dioxide treatment.” Nat. Phys. Sci. 240 (97): 16–18. https://doi.org/10.1038/physci240016a0.
Berger, R. L., and W. Klemm. 1972. “Accelerated curing of cementitious systems by carbon dioxide. Part II: Hydraulic calcium silicates and aluminates.” Cem. Concr. Res. 2 (6): 647–652. https://doi.org/10.1016/0008-8846(72)90002-6.
Blanco-Varela, M., J. Aguilera, and S. Martinez-Ramirez. 2006. “Effect of cement content, temperature and storage medium on thaumasite formation in carbonated mortars.” Cem. Concr. Res. 36 (4): 707–715. https://doi.org/10.1016/j.cemconres.2005.11.010.
Bonen, D. 1992. “Composition and appearance of magnesium silicate hydrate and its relation to deterioration of cement-based materials.” J. Am. Ceram. Soc. 75 (10): 2904–2906. https://doi.org/10.1111/j.1151-2916.1992.tb05530.x.
Brown, P., and R. Hooton. 2002. “Ettringite and thaumasite formation in laboratory concretes prepared using sulfate-resisting cements.” Cem. Concr. Compos. 24 (3–4): 361–370. https://doi.org/10.1016/S0958-9465(01)00088-9.
Collett, G., N. Crammond, R. Swamy, and J. Sharp. 2004. “The role of carbon dioxide in the formation of thaumasite.” Cem. Concr. Res. 34 (9): 1599–1612. https://doi.org/10.1016/j.cemconres.2004.02.024.
CSA (Canadian Standards Association). 2014. Cementitious materials used in concrete. CSA A3001: Toronto: Canadian Standards Association.
Damidot, D., and F. Glasser. 1993. “Thermodynamic investigation of the CaO system at 25°C and the influence of .” Cem. Concr. Res. 23 (1): 221–238. https://doi.org/10.1016/0008-8846(93)90153-Z.
Diamond, S. 2003. “Thaumasite in Orange County, southern California: An inquiry into the effect of low temperature.” Cem. Concr. Compos. 25 (8): 1161–1164. https://doi.org/10.1016/S0958-9465(03)00138-0.
Freyburg, E., and A. Berninger. 2003. “Field experiences in concrete deterioration by thaumasite formation: Possibilities and problems in thaumasite analysis.” Cem. Concr. Compos. 25 (8): 1105–1110. https://doi.org/10.1016/S0958-9465(03)00135-5.
Gollop, R., and H. Taylor. 1992. “Microstructural and microanalytical studies of sulfate attack. I: Ordinary portland cement paste.” Cem. Concr. Res. 22 (6): 1027–1038. https://doi.org/10.1016/0008-8846(92)90033-R.
Gollop, R., and H. Taylor. 1995. “Microstructural and microanalytical studies of sulfate attack III. Sulfate-resisting portland cement: Reactions with sodium and magnesium sulfate solutions.” Cem. Concr. Res. 25 (7): 1581–1590. https://doi.org/10.1016/0008-8846(95)00151-2.
Hagelia, P., R. Sibbick, N. Crammond, and C. Larsen. 2003. “Thaumasite and secondary calcite in some Norwegian concretes.” Cem. Concr. Compos. 25 (8): 1131–1140. https://doi.org/10.1016/S0958-9465(03)00143-4.
Hartshorn, S., J. Sharp, and R. Swamy. 1999. “Thaumasite formation in portland-limestone cement pastes.” Cem. Concr. Res. 29 (8): 1331–1340. https://doi.org/10.1016/S0008-8846(99)00100-3.
Hobbs, D. 2003. “Thaumasite sulfate attack in field and laboratory concretes: Implications for specifications.” Cem. Concr. Compos. 25 (8): 1195–1202. https://doi.org/10.1016/S0958-9465(03)00145-8.
Hooton, R., M. Nokken, and M. Thomas. 2007. Portland-limestone cement: State-of-the-art report and gap analysis for CSA A 3000. Toronto: St. Lawrence Cement.
Ipavec, A., R. Gabrovšek, T. Vuk, V. Kaučič, J. Maček, and A. Meden. 2011. “Carboaluminate phases formation during the hydration of calcite-containing portland cement.” J. Am. Ceram. Soc. 94 (4): 1238–1242. https://doi.org/10.1111/j.1551-2916.2010.04201.x.
Irassar, E. 2009. “Sulfate attack on cementitious materials containing limestone filler—A review.” Cem. Concr. Res. 39 (3): 241–254. https://doi.org/10.1016/j.cemconres.2008.11.007.
Irassar, E., V. Bonavetti, M. Trezza, and M. González. 2005. “Thaumasite formation in limestone filler cements exposed to sodium sulphate solution at 20°C.” Cem. Concr. Compos. 27 (1): 77–84. https://doi.org/10.1016/j.cemconcomp.2003.10.003.
Justnes, H. 2003. “Thaumasite formed by sulfate attack on mortar with limestone filler.” Cem. Concr. Compos. 25 (8): 955–959. https://doi.org/10.1016/S0958-9465(03)00120-3.
Khoshnazar, R., and Y. Shao. 2018. “Characterization of carbonation-cured cement paste using X-ray photoelectron spectroscopy.” Constr. Build. Mater. 168 (Apr): 598–605. https://doi.org/10.1016/j.conbuildmat.2018.02.175.
Lee, S. T., R. D. Hooton, H. S. Jung, D. H. Park, and C. S. Choi. 2008. “Effect of limestone filler on the deterioration of mortars and pastes exposed to sulfate solutions at ambient temperature.” Cem. Concr. Res. 38 (1): 68–76. https://doi.org/10.1016/j.cemconres.2007.08.003.
Ma, B., X. Gao, E. A. Byars, and Q. Zhou. 2006. “Thaumasite formation in a tunnel of Bapanxia Dam in western China.” Cem. Concr. Res. 36 (4): 716–722. https://doi.org/10.1016/j.cemconres.2005.10.011.
Macphee, D., and S. Diamond. 2003. “Thaumasite in cementitious materials.” Cem. Concr. Compos. 25 (8): 805–807. https://doi.org/10.1016/S0958-9465(03)00165-3.
Mangat, P., and J. El-Khatib. 1992. “Influence of initial curing on sulphate resistance of blended cement concrete.” Cem. Concr. Res. 22 (6): 1089–1100. https://doi.org/10.1016/0008-8846(92)90039-X.
Matschei, T., and F. P. Glasser. 2015. “Thermal stability of thaumasite.” Mater. Struct. 48 (7): 2277–2289. https://doi.org/10.1617/s11527-014-0309-4.
Monkman, S., and Y. Shao. 2006. “Assessing the carbonation behavior of cementitious materials.” J. Mater. Civ. Eng. 18 (6): 768–776. https://doi.org/10.1061/(ASCE)0899-1561(2006)18:6(768).
Nied, D., K. Enemark-Rasmussen, E. L’Hopital, J. Skibsted, and B. Lothenbach. 2016. “Properties of magnesium silicate hydrates (MSH).” Cem. Concr. Res. 79 (Jan): 323–332. https://doi.org/10.1016/j.cemconres.2015.10.003.
Nielsen, P., S. Nicolai, A. Darimont, and X. Kestemont. 2014. “Influence of cement and aggregate type on thaumasite formation in concrete.” Cem. Concr. Compos. 53 (Oct): 115–126. https://doi.org/10.1016/j.cemconcomp.2014.06.011.
Ramezanianpour, A. M., and R. D. Hooton. 2013. “Thaumasite sulfate attack in portland and portland-limestone cement mortars exposed to sulfate solution.” Constr. Build. Mater. 40 (Mar): 162–173. https://doi.org/10.1016/j.conbuildmat.2012.09.104.
Rostami, V., Y. Shao, and A. J. Boyd. 2011a. “Carbonation curing versus steam curing for precast concrete production.” J. Mater. Civ. Eng. 24 (9): 1221–1229. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000462.
Rostami, V., Y. Shao, and A. J. Boyd. 2011b. “Durability of concrete pipes subjected to combined steam and carbonation curing.” Constr. Build. Mater. 25 (8): 3345–3355. https://doi.org/10.1016/j.conbuildmat.2011.03.025.
Rostami, V., Y. Shao, A. J. Boyd, and Z. He. 2012. “Microstructure of cement paste subject to early carbonation curing.” Cem. Concr. Res. 42 (1): 186–193. https://doi.org/10.1016/j.cemconres.2011.09.010.
Sahu, S., S. Badger, and N. Thaulow. 2002. “Evidence of thaumasite formation in southern California concrete.” Cem. Concr. Compos. 24 (3–4): 379–384. https://doi.org/10.1016/S0958-9465(01)00090-7.
Shao, Y., V. Rostami, Z. He, and A. J. Boyd. 2013. “Accelerated carbonation of portland limestone cement.” J. Mater. Civ. Eng. 26 (1): 117–124. https://doi.org/10.1061/(ASCE)MT.1943-5533.0000773.
Shtepenko, O., C. Hills, A. Brough, and M. Thomas. 2006. “The effect of carbon dioxide on -dicalcium silicate and portland cement.” Chem. Eng. J. 118 (1–2): 107–118. https://doi.org/10.1016/j.cej.2006.02.005.
Thomas, M., C. Rogers, and R. Bleszynski. 2003. “Occurrences of thaumasite in laboratory and field concrete.” Cem. Concr. Compos. 25 (8): 1045–1050. https://doi.org/10.1016/S0958-9465(03)00134-3.
Torres, S., J. Sharp, R. Swamy, C. Lynsdale, and S. Huntley. 2003. “Long term durability of portland-limestone cement mortars exposed to magnesium sulfate attack.” Cem. Concr. Compos. 25 (8): 947–954. https://doi.org/10.1016/S0958-9465(03)00160-4.
Zhang, D., X. Cai, and B. Jaworska. 2020. “Effect of pre-carbonation hydration on long-term hydration of carbonation-cured cement-based materials.” Constr. Build. Mater. 231 (Jan): 117122. https://doi.org/10.1016/j.conbuildmat.2019.117122.
Zhang, D., Z. Ghouleh, and Y. Shao. 2017. “Review on carbonation curing of cement-based materials.” J. Util. 21 (Oct): 119–131. https://doi.org/10.1016/j.jcou.2017.07.003.
Zhang, D., V. C. Li, and B. R. Ellis. 2018. “Optimal pre-hydration age for sequestration through portland cement carbonation.” ACS Sustainable Chem. Eng. 6 (12): 15976–15981. https://doi.org/10.1021/acssuschemeng.8b03699.
Zhang, D., V. C. Li, and B. R. Ellis. 2019. “Ettringite-related dimensional stability of portland cement mortars.” ACS Sustainable Chem. Eng. 7 (19): 16310–16319. https://doi.org/10.1021/acssuschemeng.9b03345.
Zhang, D., and Y. Shao. 2016a. “Early age carbonation curing for precast reinforced concretes.” Constr. Build. Mater. 113 (Jun): 134–143. https://doi.org/10.1016/j.conbuildmat.2016.03.048.
Zhang, D., and Y. Shao. 2016b. “Effect of early carbonation curing on chloride penetration and weathering carbonation in concrete.” Constr. Build. Mater. 123 (Oct): 516–526. https://doi.org/10.1016/j.conbuildmat.2016.07.041.
Zhang, D., and Y. Shao. 2018. “Surface scaling of concrete exposed to freeze-thaw cycles.” J. Util. 27 (Oct): 137–144. https://doi.org/10.1016/j.jcou.2018.07.012.
Zhang, D., and Y. Shao. 2019. “Enhancing chloride corrosion resistance of precast reinforced concrete by carbonation curing.” ACI Mater. J. 116 (3): 3–12. https://doi.org/10.14359/51714461.
Zhang, J., and G. W. Scherer. 2011. “Comparison of methods for arresting hydration of cement.” Cem. Concr. Res. 41 (10): 1024–1036. https://doi.org/10.1016/j.cemconres.2011.06.003.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: May 5, 2020
Accepted: Aug 31, 2020
Published online: Jan 26, 2021
Published in print: Apr 1, 2021
Discussion open until: Jun 26, 2021
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.