Abstract
The anchorage of a cable-stayed bridge failed and was subsequently replaced by another anchorage made of SAE/AISI 1045 steel. The new structural component has been assessed by using different options of failure assessment diagrams. Tensile tests were performed on both the base metal and weld metal of a welded coupon composed of SAE/AISI 1045 and ASTM A572 steels. The fracture toughness was estimated from the results of Charpy tests performed on the heat-affected zone (HAZ) of SAE/AISI 1045 steel. In addition, finite element analysis was used to determine the stress state caused by four heavy vehicles (T3-S2-R4 type) localized on one side of the column. Based on two types of postulated defects, the stress state of the tie rods, and the material fracture toughness, the failure assessment diagrams were constructed to predict the critical load that can be withstood by the anchorage and the weld metal. The results indicate that both the SAE/AISI 1045 steel and the weld metal could work safely under typical operating conditions of the bridge, even when there is a detachment of one of the anchorages. The weld metal is susceptible to plastic collapse failure, while the HAZ of the steel is susceptible to a combination of fracture and plastic collapse. It is also noted that the critical stress predicted by Option 1 on the HAZ of SAE/AISI 1045 tends to be more conservative than that predicted by Option 2. The degree of conservatism ranges from 7.8% up to 12% for a superficial flaw and from 6.2% to 15.5% for an embedded flaw.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
All data, models, and code generated or used during the study appear in the published article.
References
AASHTO/AWS (AASHTO/American Welding Society). 2010. Bridge welding code. AASHTO/AWS D1.5M/D1.5:2010. Miami, FL: AASHTO/AWS.
Anaya, M. 2018. “Metodología para la calibración de modelos de elemento finito de puentes atirantados” [Methodology for the calibration of finite element models of cable-stayed bridges]. [In Spanish.] M.S. thesis, Research and Graduate Div. of the School of Engineering, Autonomous Univ. of Queretaro.
Astiz, M. A. 1997. “Composite construction in cable-stayed bridge towers.” In Proc., Composite Construction: Conventional and Innovative—Conf. Report, 127–132. Berkeley, CA: Univ. of California.
ASTM. 2001a. Standard specification for high strength low-alloy columbium-vanadium structural steel. ASTM A572/A572M-01. West Conshohocken, PA: ASTM.
ASTM. 2001b. Standard specification for steel casting, high strength, for structural purposes. ASTM A148/A148M-01. West Conshohocken, PA: ASTM.
ASTM. 2013. Standard test methods for determining average grain size. ASTM E112-13. West Conshohocken, PA: ASTM.
ASTM. 2016a. Standard test method for notched bar impact testing of metallic materials. ASTM E 23-16b. West Conshohocken, PA: ASTM.
ASTM. 2016b. Standard test method for tension testing of metallic materials. ASTM E8/E8M-16a. West Conshohocken, PA: ASTM.
AWS (American Welding Society). 1983. “Metal and their weldability.” In Vol. 1 of Welding handbook. 7th ed. Miami, FL: AWS.
AWS (American Welding Society). 2005. Specification for the qualification of welder test facilities. AWS B5.4:2005. Miami, FL: AWS.
AWS (American Welding Society). 2007. Standard methods for mechanical testing of welds. AWS B4.0:2007. Miami, FL: AWS.
Bramfitt, B. L., and O. A. Benscoter. 2002. Metallographer’s guide. Materials Park, OH: ASM International.
BSI (British Standards Institution). 1995. Destructive test on welds in metallic. Impact tests. Test specimen location, notch orientation and examination. BS EN 875:1995. London: BSI.
BSI (British Standards Institution). 2013. Guide to methods for assessing the acceptability of flaws in metallic structures. BS 7910:2013. London: BSI.
Campbell, F. C. 2008. Elements of metallurgy and engineering alloys. Materials Park, OH: The American Society for Metals International.
Cho, S., J. Yim, S. W. Shin, H. J. Jung, C. B. Yun, and M. L. Wang. 2013. “Comparative field study of cable tension measurement for a cable-stayed bridge.” J. Bridge Eng. 18 (8): 748–757. https://doi.org/10.1061/(ASCE)BE.1943-5592.0000421.
Clubey, K. S., and S. N. Winter. 2003. “On the fatigue and fracture of site splice welds at River Mardle Viaduct.” Eng. Fail. Anal. 10 (5): 593–604. https://doi.org/10.1016/S1350-6307(03)00022-0.
Díaz García, M. A., S. Cicero, and O. R. Ramos Gutierrez. 2018. “Structural integrity assessment of the welded joints of the constitution of 1812 bridge (Cádiz, Spain).” Eng. Fail. Anal. 90 (Aug): 518–533. https://doi.org/10.1016/j.engfailanal.2018.04.012.
Dieter, E. G. 1998. Mechanical metallurgy: SI metric edition. London: Mc Graw-Hill.
FITNET FFS (FITNET Fitness-for-Service). 2008. Vol. 1 of 2008—Procedure. Edited by M. Koçak, S. Webster, J. J. Janosch, R. A. Ainsworth, and R. Koers. Geesthacht, Germany: Gesellschaft fürKernenergieverwertung in Schiffbau und Schiffahrt mbH Forschungszentrum.
Ghali, E., and M. Krishnadev. 2006. “Physical and mechanical metallurgy of premature failure of tie rods of a cable-stayed bridge.” Eng. Fail. Anal. 13 (1): 117–126. https://doi.org/10.1016/j.engfailanal.2004.10.014.
Gutierrez-Solana, F., and S. Cicero. 2009. “FITNET FFS procedure: A unified European procedure for structural integrity assessment.” Eng. Fail. Anal. 16 (2): 559–577. https://doi.org/10.1016/j.engfailanal.2008.02.007.
Habashi, M., and M. Tvrdy. 2015. “Relationships between and CVN at the lower shelf of the transition curve CVN-T.” J. Mater. Sci. Eng. A 5 (5–6): 209–220. https://doi.org/10.17265/2161-6213/2015.5-6.004.
Lee, J. S., J. B. Ju, J. Jang, W. S. Kim, and D. Kwon. 2004. “Weld crack assessment in API X65 pipeline: Failure assessment diagrams with variations in representative mechanical properties.” Mater. Sci. Eng., A 373 (1–2): 122–130. https://doi.org/10.1016/j.msea.2003.12.039.
Li, D., J. Ou, C. Lan, and H. Li. 2012. “Monitoring and failure analysis of corroded bridge cables under fatigue loading using acoustic emission sensors.” Sensors 12 (4): 3901–3915. https://doi.org/10.3390/s120403901.
López, J. A., F. J. Carrión, D. Samayoa, and P. R. Orozco. 2009. “Verification of the ultrasonic qualification for structural integrity of partially embedded steel elements.” Adv. Mater. Res. 65 (Mar): 69–78. https://doi.org/10.4028/www.scientific.net/AMR.65.69.
Maljaars, J., and T. Vrouwenvelder. 2014. “Fatigue failure analysis of stay cables with initial defect: Ewijk bridge case study.” Struct. Saf. 51 (Nov): 47–56. https://doi.org/10.1016/j.strusafe.2014.05.007.
Martínez, A., F. Carrión, J. Quintana, J. Hernández, H. Gasca, A. Hernández, M. Machorro, M. Anaya, and I. Valenzuela. 2019. “Assessment for indirect vs direct methods to know the tension of cables in stayed bridges.” In Proc., IABSE-SMIS 2nd Bridge Engineering Workshop. Queretaro, Mexico: Mexican Group of The International Association for Bridge and Structural Engineering.
Milne, I., R. A. Ainsworth, A. R. Dowling, and A. T. Stewart. 1988. “Assessment of the integrity of structures containing defects.” Int. J. Press. Vessels Pip. 32 (1–4): 3–104. https://doi.org/10.1016/0308-0161(88)90071-3.
Newman, J. C., and I. S. Raju. 1981. “An empirical stress intensity factor equation for the surface crack.” Eng. Fract. Mech. 15 (1–2): 185–192. https://doi.org/10.1016/0013-7944(81)90116-8.
Raju, I. S., and J. C. Newman. 1979. “Stress intensity factors for a wide range of semi-elliptical surface cracks in finite—Thickness plates.” Eng. Fract. Mech. 11 (4): 817–829. https://doi.org/10.1016/0013-7944(79)90139-5.
Rao, N. B., and A. R. Acharya. 1989. “Charpy V-notch impact test: A partial alternate to ASTM E 399 fracture testing for routine quality control applications.” Eng. Fract. Mech. 32 (1): 39–42. https://doi.org/10.1016/0013-7944(89)90204-X.
SAE (Society of Automotive Engineers) International. 2001. Chemical composition of SAE carbon steel. SAE J403-200111. West Conshohocken, PA: SAE International.
Terán, J., S. Cicero, T. García, J. A. Alvarez, M. Martínez, and J. T. Pérez. 2014. “Structural Integrity of the cast steel upper anchorage elements used in a cable stayed bridge.” Eng. Struct. 81 (Dec): 309–317. https://doi.org/10.1016/j.engstruct.2014.10.018.
Valle, J. C. 2011. “Determinación del factor de intensidad de esfuerzos en un componente structural de acero colado” [Determination of the stress intensity factor in a structural component of cast steel]. [In Spanish.] M.S. thesis, Dept. of Mechanical Engineering, Celaya Technological Institute.
Zerbst, U., M. Schödel, S. Webster, and R. A. Ainsworth. 2000. Fitness-for-service fracture assessment of structures containing cracks. London: Elsevier.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: Apr 1, 2020
Accepted: Aug 11, 2020
Published online: Jan 29, 2021
Published in print: Apr 1, 2021
Discussion open until: Jun 29, 2021
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.