Prediction of Service Life and Evaluation of Probabilistic Life-Cycle Cost for Surface-Repaired Carbonated Concrete
Publication: Journal of Materials in Civil Engineering
Volume 32, Issue 10
Abstract
Concrete structures are economical and typically durable when exposed to a variety of environmental conditions. However, carbonation results in a reduction of the durability of reinforced concrete members because it damages the passive film surrounding the reinforcement, which accelerates corrosion processes and may ultimately lead to premature failure of the members. Predicting service life is complex because it depends strongly on changes in materials and environmental conditions. Existing carbonation models predict the service life based on deterministic theories. In this study, deterministic and probabilistic methods are applied to study concrete carbonation in the presence of repair materials using the maintenance periods and repair cost according to the coefficient of variation (COV) of the carbonation depth of each repair material. Water-based paint, organic alkaline inhibitor, inhibiting surface coating, and corrosion-inhibiting mortar (IM) were used as repair materials. An accelerated carbonation experiment using 20% was performed for 5 days, and then the repair materials were applied on the concrete surface. Then the samples were put back in the carbonation chamber and carbonation depth was measured after 7, 14, and 28 days. Based on the COV value, the carbonation depth and maintenance periods were predicted. These were used as parameters for the probabilistic life-cycle cost (LCC) model. Results showed that carbonation inhibition was best when the repair was done using IM. Cost results obtained from deterministic and probabilistic models were compared. When the probabilistic model is applied, the repair cost is evaluated as a curve, unlike with the deterministic model. The probabilistic model reduces the maximum cost by 50% compared to the deterministic model. As the COV decreased (indicating better quality concrete), the probabilistic model results approached those of the deterministic model evaluation.
Get full access to this article
View all available purchase options and get full access to this article.
Data Availability Statement
Some or all data, models, or code generated or used during the study are proprietary or confidential in nature and may only be provided with restrictions.
Acknowledgments
This research was supported by a basic science research program through the National Research Foundation (NRF) of Korea funded by the Ministry of Science, ICT and Future Planning (2015R1A5A1037548) and the Ministry of Education (NRF-2018R1A6A3A03013322).
References
Alipour, A., B. Shafei, and M. S. Shinozuka. 2013. “Capacity loss evaluation of reinforced concrete bridges located in extreme chloride-laden environments.” Struct. Infrastruct. Eng. 9 (1): 8–27. https://doi.org/10.1080/15732479.2010.525243.
Alonso, C., C. Andrade, and J. Gonzalez. 1988. “Relation between resistivity and corrosion rate of reinforcements in carbonated mortar made with several cement types.” Cem. Concr. Res. 18 (5): 687–698. https://doi.org/10.1016/0008-8846(88)90091-9.
Ammar, M., T. Zayed, and O. Moselhi. 2012. “Fuzzy-based life-cycle cost model for decision making under subjectivity.” J. Constr. Eng. Manage. 139 (5): 556–563. https://doi.org/10.1061/(ASCE)CO.1943-7862.0000576.
Ann, K. Y., S. W. Pack, J. P. Hwang, H. W. Song, and S. H. Kim. 2010. “Service life prediction of a concrete bridge structure subjected to carbonation.” Constr. Build. Mater. 24 (8): 1494–1501. https://doi.org/10.1016/j.conbuildmat.2010.01.023.
Architectural Institute of Japan. 2016. Recommendations for durability design and construction practice of reinforced concrete buildings. [In Japanese.] Tokyo: Architectural Institute of Japan.
Awaja, F., S. Zhang, M. Tripathi, A. Nikiforov, and N. Pugno. 2016. “Cracks, microcracks and fracture in polymer structure: Formation, detection, autonomic repair.” Prog. Mater Sci. 83 (Oct): 536–573. https://doi.org/10.1016/j.pmatsci.2016.07.007.
Ba, M., C. Qian, and L. Huang. 2010. “Probabilistic method and its application for evaluating carbonation life of newly-built concrete structures.” J. Southeast Univ. (English Edition) 26 (4): 578–581. https://doi.org/10.3969/j.issn.1003-7985.2010.04.016.
Bentur, A. 1997. Steel corrosion in concrete: Fundamentals and civil engineering practice. Edited by S. Diamond, and N. S. Berke. London: E & FN Spon.
Binder, F. 2013. “Life cycle costs of selected concrete repair methods demonstrated on chloride contaminated column.” In Proc., 11th Int. Probabilistic Workshop. Tábor, Brno: Ing. Vladislav Pokorný—Litera Brno.
Chiu, C., M. Kanematsu, T. Noguchi, and H. Nagai. 2008a. “Optimal maintenance plan of RC building damaged by concrete carbonation using immune algorithm.” J. Struct. Constr. Eng. 73 (624): 173–180. https://doi.org/10.3130/aijs.73.173.
Chiu, C., Y. Lyu, and W. Jean. 2014. “Probability-based damage assessment for reinforced concrete bridge columns considering the corrosive and seismic hazards in Taiwan.” Nat. Hazards 71 (3): 2143–2164. https://doi.org/10.1007/s11069-013-1002-6.
Chiu, C., T. Noguchi, and M. Kanematsu. 2008b. “Optimal maintenance plan for rc members by minimizing life-cycle cost including deterioration risk due to carbonation.” J. Adv. Concr. Technol. 6 (3): 469–480. https://doi.org/10.3151/jact.6.469.
Cho, H.-C., H. Ju, J. Y. Oh, K. Lee, K. Hahm, and K. S. Kim. 2016. “Estimation of concrete carbonation depth considering multiple influencing factors on the deterioration of durability for reinforced concrete structures.” Adv. Mater. Sci. Eng. 2016: 18. https://doi.org/10.1155/2016/4814609.
De Jesus, R., J. Collado, J. Go, M. Rosanto, and J. Tan. 2017. “Modelling of carbonation of reinforced concrete structures in Intramuros, Manila using artificial neural network.” Int. J. Geomate 13 (35): 87–92. https://doi.org/10.21660/2017.35.6683.
Delnavaz, A., and A. A. Ramezanianpour. 2012. “The assessment of carbonation effect on chloride diffusion in concrete based on artificial neural network model.” Mag. Concr. Res. 64 (10): 877–884. https://doi.org/10.1680/macr.11.00059.
Du, S., J. Wu, O. AlShareedah, and X. Shi. 2019. “Nanotechnology in cement-based materials: A review of durability, modeling, and advanced characterization.” Nanomaterials 9 (9): 1213. https://doi.org/10.3390/nano9091213.
Firouzi, A., and A. Rahai. 2012. “An integrated ANN-GA for reliability based inspection of concrete bridge decks considering extent of corrosion-induced cracks and life cycle costs.” Sci. Iranica 19 (4): 974–981. https://doi.org/10.1016/j.scient.2012.06.002.
Fowler, D. W. 2009. “Chapter 7: Repair materials for concrete structures.” In Failure, distress and repair of concrete structures. Edited by N. Delatte, 194–207. Sawston, CA: Woodhead Publishing.
Frangopol, D. M., and M. Liu. 2007. “Maintenance and management of civil infrastructure based on condition, safety, optimization, and life-cycle cost.” Struct. Infrastruct. Eng. 3 (1): 29–41. https://doi.org/10.1080/15732470500253164.
Freddi, F., J. E. Padgett, and A. Dallasta. 2012. “Life cycle cost analysis of low ductility rc frame buildings retrofitted by modern retrofit techniques.” In Proc., 5th European Conf. on Structural Control. Genova, Italy: European Conference on Structural Control.
Grace, N. F., E. A. Jensen, C. D. Eamon, and X. Shi. 2012. “Life-cycle cost analysis of carbon fiber-reinforced polymer reinforced concrete bridges.” ACI Struct. J. 109 (5): 697–704.
Islam, S., and T. Kishi. 2010. “Effects of cover properties and repair methods on LCC estimation of reinforced concrete structure.” Soc. Soc. Manage. Syst. Internet J. 6 (1): 1–8.
Jung, K., H. M. Park, J. H. Kim, G. Kim, and J. S. Kong. 2013. “Development of a probabilistic life-cycle cost model for marine structures exposed to chloride attack based on Bayesian approach using monitoring data.” KSCE J. Civ. Eng. 17 (5): 1073–1082. https://doi.org/10.1007/s12205-013-0350-9.
KCI (Korea Concrete Institute). 2017. Korea structural concrete design code 2012. Seoul: KCI.
Kellouche, Y., B. Boukhatem, M. Ghrici, and A. Tagnit-Hamou. 2019. “Exploring the major factors affecting fly-ash concrete carbonation using artificial neural network.” Neural Comput. Appl. 31 (2): 969–988. https://doi.org/10.1007/s00521-017-3052-2.
Korean Standard. 2004. Method for measuring carbonation depth of concrete; Korean agency for technology and standards. KS F 2596. Seoul: Korean Standard.
Kumar, R., P. Gardoni, and M. Sanchez-Silva. 2009. “Effect of cumulative seismic damage and corrosion on the life-cycle cost of reinforced concrete bridges.” Earthquake Eng. Struct. Dyn. 38 (7): 887–905. https://doi.org/10.1002/eqe.873.
Lee, H. M. 2018. “A study on the carbonation service life and LCC repair evaluation of RC structure applied by repair method.” Ph.D. thesis, Dept. of Architectural Engineering, Hanyang Univ.
Lee, H. M., H. Lee, S. Min, S. Lim, and J. Singh. 2018a. “Carbonation-induced corrosion initiation probability of rebars in concrete with/without finishing materials.” Sustainability 10 (10): 3814. https://doi.org/10.3390/su10103814.
Lee, H. M., H. S. Lee, and J. K. Singh. 2017. “Prediction model for the carbonation of post-repair materials in carbonated RC structures.” Materials 10 (5): 492. https://doi.org/10.3390/ma10050492.
Lee, H. M., H. Yang, and H. S. Lee. 2018b. “Probabilistic lcc evaluation for surface repair of carbonated RC structure.” [In Korean.] J. Archit. Inst. Korea Struct. Constr. 34 (2): 41–48. https://doi.org/10.5659/JAIK_SC.2018.34.2.41.
Li, Z., and S. Madanu. 2009. “Highway project level life-cycle benefit/cost analysis under certainty, risk, and uncertainty: Methodology with case study.” J. Transp. Eng. 135 (8): 516–526. https://doi.org/10.1061/(ASCE)TE.1943-5436.0000012.
Liu, J., Q. Qiu, X. Chen, F. Xing, N. Han, Y. He, and Y. Ma. 2017. “Understanding the interacted mechanism between carbonation and chloride aerosol attack in ordinary portland cement concrete.” Cem. Concr. Res. 95 (May): 217–225. https://doi.org/10.1016/j.cemconres.2017.02.032.
Mohammed, M. K., A. R. Dawson, and N. H. Thom. 2014. “Carbonation of filler typed self-compacting concrete and its impact on the microstructure by utilization of 100% CO2 accelerating techniques.” Constr. Build. Mater. 50 (Jan): 508–516. https://doi.org/10.1016/j.conbuildmat.2013.09.052.
Mullard, J. A., and M. G. Stewart. 2011. “Life-cycle cost assessment of maintenance strategies for RC structures in chloride environments.” J. Bridge Eng. 17 (2): 353–362. https://doi.org/10.1061/(ASCE)BE.1943-5592.0000248.
Nasir, M., H. Chong, and S. Osman. 2015. “Probabilistic life cycle cost model for repairable system.” Proc., IOP Conf. Ser.: Mater. Sci. Eng. 78 (1): 012027. https://doi.org/10.1088/1757-899X/78/1/012027.
Palle, T. C. 2009. “Life-cycle cost-benefit (LCCB) analysis of bridges from a user and social point of view.” Struct. Infrastruct. Eng. 5 (1): 49–57. https://doi.org/10.1080/15732470701322818.
Park, D. C. 2008. “Carbonation of concrete in relation to permeability and degradation of coatings.” Constr. Build. Mater. 22 (11): 2260–2268. https://doi.org/10.1016/j.conbuildmat.2007.07.032.
Peng, L., and M. G. Stewart. 2016. “Climate change and corrosion damage risks for reinforced concrete infrastructure in China.” Struct. Infrastruct. Eng. 12 (4): 499–516. https://doi.org/10.1080/15732479.2013.858270.
Portela, E. D. L., T. N. Bittencourt, and A. T. Beck. 2015. “Application of a full probabilistic model for predicting the advance of carbonation front in concrete structures.” In Proc., XXXVI Iberian Latin-American Congress on Computational Methods in Engineering, edited by N. A. Dumont. Rio de Janeiro, Brazil: ABMEC.
Ryu, H. S., and H. S. Lee. 2012. “Study on the anti-corrosion properties of organic and inorganic inhibitor by electrochemical treatment in aqueous solution.” Adv. Mater. Res. 415–417: 2070–2073. https://doi.org/10.4028/www.scientific.net/AMR.415-417.2070.
Ryu, H. S., S. Shin, and H. S. Lee. 2017. “An experimental study on the resistance to penetration of harmful ions in surface coatings material containing organic corrosion inhibitor.” [In Korean.] Korean Inst. Build. Constr. 17 (2): 157–166. https://doi.org/10.5345/JKIBC.2017.17.2.157.
Ryu, H. S., J. K. Singh, H. M. Yang, H. S. Lee, and M. A. Ismail. 2016. “Evaluation of corrosion resistance properties of N, N′-Dimethyl ethanolamine corrosion inhibitor in saturated solution with different concentrations of chloride ions by electrochemical experiments.” Constr. Build. Mater. 114 (Jul): 223–231. https://doi.org/10.1016/j.conbuildmat.2016.03.174.
Soleimani, S., P. Ghods, O. B. Isgor, and J. Zhang. 2010. “Modeling the kinetics of corrosion in concrete patch repairs and identification of governing parameters.” Cem. Concr. Compos. 32 (5): 360–368. https://doi.org/10.1016/j.cemconcomp.2010.02.001.
Sun, Y., and D. G. Carmichael. 2018. “Uncertainties related to financial variables within infrastructure life cycle costing: A literature review.” Struct. Infrastruct. Eng. 14 (9): 1233–1243. https://doi.org/10.1080/15732479.2017.1418008.
Swei, O., J. Gregory, and R. Kirchain. 2013. “Probabilistic characterization of uncertain inputs in the life-cycle cost analysis of pavements.” Transp. Res. Rec. 2366 (1): 71–77. https://doi.org/10.3141/2366-09.
Takewaka, K., and S. Mastumoto. 1988. “Quality and cover thickness of concrete based on the estimation of chloride penetration in marine environments.” Spec. Publ. 109 (Aug): 381–400.
Talukdar, S., N. Banthia, J. R. Grace, and S. Cohen. 2012. “Carbonation in concrete infrastructure in the context of global climate change: Part 2—Canadian urban simulations.” Cem. Concr. Compos. 34 (8): 931–935. https://doi.org/10.1016/j.cemconcomp.2012.04.012.
Torres, H., E. Correa, J. G. Castaño, and F. Echeverría. 2017. “Simplified mathematical model for concrete carbonation.” J. Mater. Civ. Eng. 29 (10): 04017150. https://doi.org/10.1061/(ASCE)MT.1943-5533.0002001.
Total-LCC. 2010. Total-LCC technical manual. [In Japanese.] Tokyo: Total Information Service Corp.
Val, D. V., and M. G. Stewart. 2003. “Life-cycle cost analysis of reinforced concrete structures in marine environments.” Struct. Saf. 25 (4): 1343–362. https://doi.org/10.1016/S0167-4730(03)00014-6.
Yang, K., J. Singh, B. Lee, and S. Kwon. 2017. “Simple technique for tracking chloride penetration in concrete based on the crack shape and width under steady-state conditions.” Sustainability 9 (2): 282. https://doi.org/10.3390/su9020282.
Zayed, T. M., L.-M. Chang, and J. D. Fricker. 2002. “Life-cycle cost analysis using deterministic and stochastic methods: Conflicting results.” J. Perform. Constr. Facil. 16 (2): 63–74. https://doi.org/10.1061/(ASCE)0887-3828(2002)16:2(63).
Zhu, X., Z. Chen, H. Wang, Y. Chen, and L. Xu. 2018. “Probabilistic generalization of a comprehensive model for the deterioration prediction of RC structure under extreme corrosion environments.” Sustainability 10 (9): 3051. https://doi.org/10.3390/su10093051.
Zhu, Y., Y. Tao, and R. Rayegan. 2012. “A comparison of deterministic and probabilistic life cycle cost analyses of ground source heat pump (GSHP) applications in hot and humid climate.” Energy Build. 55 (Dec): 312–321. https://doi.org/10.1016/j.enbuild.2012.08.039.
Information & Authors
Information
Published In
Copyright
©2020 American Society of Civil Engineers.
History
Received: Mar 26, 2019
Accepted: Apr 7, 2020
Published online: Jul 29, 2020
Published in print: Oct 1, 2020
Discussion open until: Dec 29, 2020
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.