Early-Age Strength of Alkali-Activated Slag Mortar Based on Burned Oyster Shell and Other Chemical Activators
Publication: Journal of Materials in Civil Engineering
Volume 31, Issue 9
Abstract
An alkaline-activated, ground-granulated blast furnace slag (BFS) was used as a binder for mortar prepared using river sand. Sixteen mortar mixes with four different BFS:sand ratios (4%, 8%, 12%, and 16% dry weight) were investigated. The BFS hydration of these mortar mixes was activated using four different activator solutions (1 mol): burned oyster shell (OS), calcium hydroxide (CH), sodium hydroxide (SH), and potassium hydroxide (PH). After curing for 3 and 7 days, the unconfined compressive strength (UCS) of the mortar increases with an increasing BFS:sand ratio, regardless of the activator type. The UCS of the mortar increased with increasing pH value of the activator. The mortar activated with OS had similar but slightly lower mechanical properties (60%–90% UCS, 70%–97% peak load strain, 0.78%–100% maximum strain, 40%–114% elastic modulus, 55%–100% toughness) relative to the mortar activated by CH, while the mortars activated by SH had mechanical properties similar to those of the mortar activated by PH. In all mortar samples, activated by different activators, CSH, , and were found. The mechanical properties (strength, peak load strain, maximum strain, elastic modulus, and toughness) of the mortar samples were analyzed.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This research was part of the first author’s PhD studies, sponsored by the Ministry of Land, Transport and Maritime Affairs and the Kyungpook National University, Korea; some data were published in Korean (Park and Choi 2013), but further analysis was carried out during his postdoctoral studies at Iowa State University. The authors would like to acknowledge the Korean Geotechnical Society for its permission to use the raw data presented in this paper. This work was also partially supported by a National Research Foundation of Korea (NRF) grant funded by the Korean government (Grant No. NRF-2018R1A5A1025137).
References
Altan, E., and S. T. Erdoğan. 2012. “Alkali activation of a slag at ambient and elevated temperatures.” Cem. Concr. Compos. 34 (2): 131–139. https://doi.org/10.1016/j.cemconcomp.2011.08.003.
ASTM. 2008. Standard test method for unconfined compressive strength index of chemical-grouted soils. ASTM D4219. West Conshohocken, PA: ASTM.
Barnett, S. J., M. N. Soutsos, S. G. Millard, and J. H. Bungey. 2006. “Strength development of mortars containing ground granulated blast-furnace slag: Effect of curing temperature and determination of apparent activation energies.” Cem. Concr. Res. 36 (3): 434–440. https://doi.org/10.1016/j.cemconres.2005.11.002.
Cheah, C. B., M. H. Samsudin, M. Ramli, W. K. Part, and L. E. Tan. 2017. “The use of high calcium wood ash in the preparation of ground granulated blast furnace slag and pulverized fly ash geopolymers: A complete microstructural and mechanical characterization.” J. Cleaner Prod. 156 (Jul): 114–123. https://doi.org/10.1016/j.jclepro.2017.04.026.
Cheng, T. W., and J. P. Chiu. 2003. “Fire-resistant geopolymer produced by granulated blast furnace slag.” Miner. Eng. 16 (3): 205–210. https://doi.org/10.1016/S0892-6875(03)00008-6.
de Moraes Pinheiro, S. M., A. Font, L. Soriano, M. M. Tashima, J. Monzo, M. V. Borrachero, and J. Paya. 2018. “Olive-stone biomass ash (OBA): An alternative alkaline source for the blast furnace slag activation.” Constr. Build. Mater. 178 (Jul): 327–338. https://doi.org/10.1016/j.conbuildmat.2018.05.157.
Djobo, J. N. Y., H. K. Tchakouté, N. Ranjbar, A. Elimbi, L. N. Tchadjié, and D. Njopwouo. 2016. “Gel composition and strength properties of alkali-activated oyster shell-volcanic ash: Effect of synthesis conditions.” J. Am. Ceram. Soc. 99 (9): 3159–3166. https://doi.org/10.1111/jace.14332.
Escalante, J. I., L. Y. Gomez, K. K. Johal, G. Mendoza, H. Mancha, and J. Mendez. 2001. “Reactivity of blast-furnace slag in Portland cement blends hydrated under different conditions.” Cem. Concr. Res. 31 (10): 1403–1409. https://doi.org/10.1016/S0008-8846(01)00587-7.
Gao, X., B. Yuan, Q. L. Yu, and H. J. H. Brouwers. 2017. “Characterization and application of 442 municipal solid waste incineration (MSWI) bottom ash and waste granite powder in alkali activated slag.” J. Cleaner Prod. 164 (Oct): 410–419. https://doi.org/10.1016/j.jclepro.2017.06.218.
Kim, H. S., J. W. Park, Y. J. An, J. S. Bae, and C. Han. 2011. “Activation of ground granulated blast furnace slag cement by calcined alunite.” Mater. Trans. 52 (2): 210–218. https://doi.org/10.2320/matertrans.M2010350.
Kim, M. S., Y. Jun, C. Lee, and J. E. Oh. 2013. “Use of CaO as an activator for producing a price-competitive non-cement structural binder using ground granulated blast furnace slag.” Cem. Concr. Res. 54 (Dec): 208–214. https://doi.org/10.1016/j.cemconres.2013.09.011.
Kim, S. Y., Y. Jun, D. Jeon, and J. E. Oh. 2017. “Synthesis of structural binder for red brick production based on red mud and fly ash activated using and .” Constr. Build. Mater. 147 (Aug): 101–116. https://doi.org/10.1016/j.conbuildmat.2017.04.171.
Kuo, W., H. Wang, C. Shu, and D. Su. 2013. “Engineering properties of controlled low-strength materials containing waste oyster shells.” Constr. Build. Mater. 46 (Sep): 128–133. https://doi.org/10.1016/j.conbuildmat.2013.04.020.
Lee, K. M., H. K. Lee, S. H. Lee, and G. Y. Kim. 2006. “Autogenous shrinkage of concrete containing granulated blast-furnace slag.” Cem. Concr. Res. 36 (7): 1279–1285. https://doi.org/10.1016/j.cemconres.2006.01.005.
Leng, F., N. Feng, and X. Ju. 2000. “An experimental study on the properties of resistance to diffusion of chloride ions of fly ash and blast furnace slag concrete.” Cem. Concr. Res. 30 (6): 989–992. https://doi.org/10.1016/S0008-8846(00)00250-7.
Li, Q., Z. Li, and G. Yuan. 2012. “Effects of elevated temperatures on properties of concrete containing ground granulated blast furnace slag as cementitious material.” Constr. Build. Mater. 35 (Oct): 687–692. https://doi.org/10.1016/j.conbuildmat.2012.04.103.
Lima, P. R. L., R. D. T. Filho, and J. A. M. Filho. 2014. “Compressive stress-strain behaviour of cement mortar-composites reinforced with short sisal fibre.” Mater. Res. 17 (1): 38–46. https://doi.org/10.1590/S1516-14392013005000181.
Luna-Galiano, Y., C. Leiva, R. Villegas, F. Arroyo, L. Vilches, and C. Fernandez-Pereira. 2018. “Carbon fiber waste incorporation in blast furnace slag geopolymer composites.” Mater. Lett. 233 (Dec): 1–3. https://doi.org/10.1016/j.matlet.2018.08.099.
Majhi, R. K., A. N. Nayak, and B. Mukharjee. 2018. “Development of sustainable concrete using recycled coarse aggregate and ground granulated blast furnace slag.” Constr. Build. Mater. 159 (Jan): 417–430. https://doi.org/10.1016/j.conbuildmat.2017.10.118.
Nataraja, M. C., N. Dhang, and A. P. Gupta. 1999. “Stress-strain curves for steel-fiber reinforced concrete under compression.” Cem. Concr. Compos. 21 (5–6): 383–390. https://doi.org/10.1016/S0958-9465(99)00021-9.
Okonta, F. N., and O. O. Ojuri. 2014. “The stabilization of weathered dolerite aggregates with cement, lime, and lime fly ash for pavement construction.” Adv. Mater.Sci.Eng. 2014: 11. https://doi.org/10.1016/S0958-9465(99)00021-9.
Palomo, A., M. T. Blanco, M. L. Granizo, F. Puertas, T. Vazquez, and M. W. Grutzeck. 1999. “Chemical stability of cementitious materials based on metakaolin.” Cem. Concr. Res. 29 (7): 997–1004. https://doi.org/10.1016/S0008-8846(99)00074-5.
Park, S. S. 2011. “Unconfined compressive strength and ductility of fiber-reinforced cemented sand.” Constr. Build. Mater. 25 (2): 1134–1138. https://doi.org/10.1016/j.conbuildmat.2010.07.017.
Park, S. S., and S. G. Choi. 2013. “A study on sand cementation and its early strength using blast furnace slag and alkaline activators.” [In Korean.] J. Korean Geotech. Soc. 29 (4): 45–56. https://doi.org/10.7843/kgs.2013.29.4.45.
Poon, C. S., Z. H. Shui, and L. Lam. 2004. “Compressive behavior of fiber reinforced high-performance concrete subjected to elevated temperatures.” Cem. Concr. Res. 34 (12): 2215–2222. https://doi.org/10.1016/j.cemconres.2004.02.011.
Provis, J. L. 2017. “Alkali-activated materials.” Cem. Concr. Res. 114 (Dec): 40–48. https://doi.org/10.1016/j.cemconres.2017.02.009.
Song, H. W., and V. Saraswathy. 2006. “Studies on the corrosion resistance of reinforced steel in concrete with ground granulated blast-furnace slag—An overview.” J. Hazard. Mater. 138 (2): 226–233. https://doi.org/10.1016/j.jhazmat.2006.07.022.
Song, S., D. Sohn, H. M. Jennings, and T. O. Mason. 2000. “Hydration of alkali-activated ground granulated blast furnace slag.” J. Mater. Sci. 35 (1): 249–257. https://doi.org/10.1023/A:1004742027117.
Su, N., Y. H. Wu, and C. Y. Mar. 2000. “Effect of magnetic water on the engineering properties of concrete containing granulated blast-furnace slag.” Cem. Concr. Res. 30 (4): 599–605. https://doi.org/10.1016/S0008-8846(00)00215-5.
Wan, S., X. Zhou, M. Zhou, Y. Han, Y. Chen, J. Geng, T. Wang, and S. Xu. 2018. “Hydration characteristics and modeling of ternary system of municipal solid wastes incineration fly ash-blast furnace slag-cement.” Constr. Build. Mater. 180 (Aug): 154–166. https://doi.org/10.1016/j.conbuildmat.2018.05.277.
Wang, J., F. Li, Z. Zhou, P. Du, D. Xu, N. Xie, X. Cheng, and Y. Liu. 2018. “Effect of zeolite on waste based alkali-activated inorganic binder efflorescence.” Constr. Build. Mater. 158 (Jan): 683–690. https://doi.org/10.1016/j.conbuildmat.2017.10.065.
Wang, P. Z., R. Trettin, and V. Rudert. 2005. “Effect of fineness and particle size distribution of granulated blast-furnace slag on the hydraulic reactivity in cement systems.” Adv. Cem. Res. 17 (4): 161–167. https://doi.org/10.1680/adcr.2005.17.4.161.
Wang, S. D., K. L. Scrivener, and P. L. Pratt. 1994. “Factors affecting the strength of alkali-activated slag.” Cem. Concr. Res. 24 (6): 1033–1043. https://doi.org/10.1016/0008-8846(94)90026-4.
Wild, S., J. M. Kinuthia, G. I. Jones, and D. D. Higgins. 1998. “Effects of partial substitution of lime with ground granulated blast furnace slag (GGBS) on the strength properties of lime-stabilised sulphate-bearing clay soils.” Eng. Geol. 51 (1): 37–53. https://doi.org/10.1016/S0013-7952(98)00039-8.
Yang, J. M., H. O. Shin, Y. S. Yoon, and D. Mitchell. 2017. “Benefits of blast furnace slag and steel fibers on the static and fatigue performance of prestressed concrete sleepers.” Eng. Struct. 134 (Mar): 317–333. https://doi.org/10.1016/j.engstruct.2016.12.045.
Yeau, K. Y., and E. K. Kim. 2005. “An experimental study on corrosion resistance of concrete with ground granulate blast-furnace slag.” Cem. Concr. Res. 35 (7): 1391–1399. https://doi.org/10.1016/j.cemconres.2004.11.010.
Yuksel, I., T. Bilir, and O. Ozkan. 2007. “Durability of concrete incorporating non-ground blast furnace slag and bottom ash as fine aggregate.” Build. Environ. 42 (7): 2651–2659. https://doi.org/10.1016/j.buildenv.2006.07.003.
Yum, W. S., Y. Jeong, H. Song, and J. E. Oh. 2018. “Recycling of limestone fines using - and -activated slag systems for eco-friendly concrete brick production.” Constr. Build. Mater. 185 (Oct): 275–284. https://doi.org/10.1016/j.conbuildmat.2018.07.112.
Zhang, T. W., Y. Y. Zhao, X. L. Zhang, and X. C. Zhang. 2016. “Test on the mechanical properties of cement treatment soil under triaxial compression.” In Proc., Progress in Civil, Architectural and Hydraulic Engineering IV, edited by Y. H. Kim, 213–218. London: Taylor & Francis.
Živica, V. 2007. “Effects of type and dosage of alkaline activator and temperature on the properties of alkali-activated slag mixtures.” Constr. Build. Mater. 21 (7): 1463–1469. https://doi.org/10.1016/j.conbuildmat.2006.07.002.
Information & Authors
Information
Published In
Copyright
©2019 American Society of Civil Engineers.
History
Received: Jun 29, 2018
Accepted: Mar 28, 2019
Published online: Jun 19, 2019
Published in print: Sep 1, 2019
Discussion open until: Nov 19, 2019
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.