Effects of Rheological Performance, Antifoaming Admixture, and Mixing Procedure on Air Bubbles and Strength of UHPC
Publication: Journal of Materials in Civil Engineering
Volume 31, Issue 4
Abstract
This paper investigates the effects of rheological performance, antifoaming admixtures (AFA 1 and AFA 2), and mixing procedure on air bubbles and the mechanical strength of ultra-high-performance concrete (UHPC). Thirty-eight mixtures were prepared by varying the water-to-binder ratio from 0.21 to 0.27, the dosage of superplasticizer (SP) from 2.5% to 4.0%, cationic polyacrylamide from 0‰ to 3.0‰, AFAs from 0.5‰ to 4.0‰, and mixing duration from 4 to 12 min at two mixing speeds. The air content in a fresh mixture and air bubble parameters in hardened samples were measured using a pressure gauge method and digital image analysis, respectively. Compressive and flexural strengths were tested for all the mixtures after 7 and 28 days of standard curing. Results show that a lower yield stress and/or plastic viscosity and higher incorporation of AFAs reduce the content of air bubbles in hardened UHPC. Higher mixing speed is more beneficial for reducing the content and average diameter of entrapped air bubbles. The 28-day compressive strength linearly increases with the decreasing content and average diameter of air bubbles. Air bubbles with diameters larger than 1 mm have worse effects on strength of UHPC than the smaller bubbles. Therefore, mechanical strength of UHPC can be improved by controlling the content and size of air bubbles through regulating rheological properties, incorporating anti-foaming admixture and optimizing mixing procedure.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This work was supported by the National Natural Science Foundation of China (51578192).
References
Alkaysi, M., S. El-Tawil, Z. C. Liu, and W. Hansen. 2016. “Effects of silica powder and cement type on durability of ultra high performance concrete (UHPC).” Cem. Concr. Compos. 66: 47–56. https://doi.org/10.1016/j.cemconcomp.2015.11.005.
Banfill, P. F. G. 1991. “The rheology of fresh mortar.” Mag. Concr. Res. 43 (154): 13–21. https://doi.org/10.1680/macr.1991.43.154.13.
BSI (British Standards Institution). 2009. Testing fresh concrete: Air content: Pressure methods. EN 12350-7. London: BSI.
Chinese National Standard. 1999. Method of testing cements: Determination of strength. GB/T 17671. Beijing: Standard Press of China.
Chinese National Standard. 2005. Test method for activity of industrial waste slag used as addition to cement. GB/T 12957. Beijing: Standard Press of China.
Chinese National Standard. 2007. Common portland cement. GB 175. Beijing: Standard Press of China.
Choi, P., J. H. Yeon, and K. K. Yun. 2016. “Air-void structure, strength, and permeability of wet-mix shotcrete before and after shotcreting operation: The influences of silica fume and air-entraining agent.” Cem. Concr. Compos. 70: 69–77. https://doi.org/10.1016/j.cemconcomp.2016.03.012.
Chopin, D., F. D. Larrard, and B. Cazacliu. 2004. “Why do HPC and SCC require a longer mixing time?” Cem. Concr. Res. 34 (12): 2237–2243. https://doi.org/10.1016/j.cemconres.2004.02.012.
Dils, J., V. Boel, and G. D. Schutter. 2013. “Influence of cement type and mixing pressure on air content, rheology and mechanical properties of UHPC.” Constr. Build. Mater. 41 (11): 455–463. https://doi.org/10.1016/j.conbuildmat.2012.12.050.
Dils, J., V. Boel, and G. D. Schutter. 2015. “Vacuum mixing technology to improve the mechanical properties of ultra-high performance concrete.” Mater. Struct. 48 (11): 3485–3501. https://doi.org/10.1617/s11527-014-0416-2.
Dils, J., G. D. Schutter, and V. Boel. 2012. “Influence of mixing procedure and mixer type on fresh and hardened properties of concrete: A review.” Mater. Struct. 45 (11): 1673–1683. https://doi.org/10.1617/s11527-012-9864-8.
Du, L. X., and K. J. Folliard. 2005. “Mechanisms of air entrainment in concrete.” Cem. Concr. Res. 35 (8): 1463–1471. https://doi.org/10.1016/j.cemconres.2004.07.026.
Gołaszewski, J., and J. Szwabowski. 2004. “Influence of superplasticizers on rheological behavior of fresh cement mortars.” Cem. Concr. Res. 34 (2): 235–248. https://doi.org/10.1016/j.cemconres.2003.07.002.
Graybeal, B. A. 2005. “Characterization of the behavior of ultra-high performance concrete.” Ph.D. thesis, Dept. of Civil and Environmental Engineering, Univ. of Maryland.
Graybeal, B. A. 2008. “UHPC in the U.S. highway transportation system.” In Proc., 2nd Int. Symp. on Ultra-High Performance Concrete. Kassel, Germany: Kassel University Press.
Han, D., G. C. Lee, S. J. Yoon, and K. M. Kim. 2015. “Viscosity influence of rising behavior of model air bubbles in fresh mortar.” Constr. Build. Mater. 76: 10–15. https://doi.org/10.1016/j.conbuildmat.2014.11.016.
Huang, H. H., X. J. Gao, L. S. Li, and H. Wang. 2018. “Improvement effect of steel fiber orientation control on mechanical performance of UHPC.” Constr. Build. Mater. 188: 709–721. https://doi.org/10.1016/j.conbuildmat.2018.08.146.
Huang, H. H., X. J. Gao, H. Wang, and H. Ye. 2017. “Influence of rice husk ash on strength and permeability of ultra-high performance concrete.” Constr. Build. Mater. 149: 621–628. https://doi.org/10.1016/j.conbuildmat.2017.05.155.
Kearsley, E. P., and P. J. Wainwright. 2002. “The effect of porosity on the strength of foamed concrete.” Cem. Concr. Res. 32 (2): 233–239. https://doi.org/10.1016/S0008-8846(01)00665-2.
Khayat, K. H. 1998. “Viscosity-enhancing admixtures for cement-based materials: An overview.” Cem. Concr. Compos. 20 (2–3): 171–188. https://doi.org/10.1016/S0958-9465(98)80006-1.
Khayat, K. H., and J. Assaad. 2002. “Air-void stability in self-consolidating concrete.” ACI Mater. J. 99 (4): 408–416. https://doi.org/10.14359/12224.
Larrard, F. D., and T. Sedran. 1994. “Optimization of ultra-high-performance concrete by the use of a packing model.” Cem. Concr. Res. 24 (6): 997–1009. https://doi.org/10.1016/0008-8846(94)90022-1.
Łaźniewska-Piekarczyk, B., and J. Szwabowski. 2012a. “Anti-foaming admixture (AFA) and its influences on the properties of a fresh self-compacting concrete mix.” J. Civ. Eng. Manage. 18 (2): 151–157. https://doi.org/10.3846/13923730.2012.657410.
Łaźniewska-Piekarczyk, B., and J. Szwabowski. 2012b. “The influence of the type of anti-foaming admixture and superplasticizer on the properties of self-compacting mortar and concrete.” J. Civ. Eng. Manage. 18 (3): 408–415. https://doi.org/10.3846/13923730.2012.698908.
Łaźniewska-Piekarczyk, B., and J. Szwabowski. 2015. “Influence of anti-foaming admixture type on several properties of high performance self-compacting concrete.” J. Mater. Civ. Eng. 27 (9): 04014247. https://doi.org/10.1061/(ASCE)MT.1943-5533.0001056.
Luping, T. 1986. “A study of the quantitative relationship between strength and pore-size distribution of porous materials.” Cem. Concr. Res. 16 (1): 87–96. https://doi.org/10.1016/0008-8846(86)90072-4.
Mazanec, O., D. Lowke, and P. Schießl. 2010. “Mixing of high performance concrete: Effect of concrete composition and mixing intensity on mixing time.” Mater. Struct. 43 (3): 357–365. https://doi.org/10.1617/s11527-009-9494-y.
Mielenz, R. C., V. E. Wolkodoff, and J. E. Backstrom. 1958. “Origin, evolution, and effects of the air void system in concrete. Part I: Entrained air in unhardened concrete.” ACI Struct. J. 30 (1): 95–121.
Nambiar, E. K. K., and K. Ramamurthy. 2007. “Air-void characterisation of foam concrete.” Cem. Concr. Res. 37 (2): 221–230. https://doi.org/10.1016/j.cemconres.2006.10.009.
Peterson, K., J. Carlson, L. Sutter, and T. V. Dam. 2009. “Methods for threshold optimization for images collected from contrast enhanced concrete surfaces for air-void system characterization.” Mater. Charact. 60 (7): 710–715. https://doi.org/10.1016/j.matchar.2008.10.005.
Rebentrost, M., and G. Wight. 2008. “Experience and applications of Ultra-High performance concrete in Asia.” In Proc., 2nd Int. Symp. on Ultra-high Performance Concrete. Kassel, Germany: Kassel University Press.
Rejeb, S. K. 1996. “Improving compressive strength of concrete by a two-step mixing method.” Cem. Concr. Res. 26 (4): 585–592. https://doi.org/10.1016/0008-8846(96)00030-0.
Richard, P., and M. Cheyrezy. 1995. “Composition of reactive powder concretes.” Cem. Concr. Res. 25 (7): 1501–1511. https://doi.org/10.1016/0008-8846(95)00144-2.
Shi, C. J., Z. M. Wu, J. F. Xiao, D. H. Wang, Z. Y. Huang, and Z. Fang. 2015. “A review on ultra high performance concrete. Part I: Raw materials and mixture design.” Constr. Build. Mater. 101: 741–751. https://doi.org/10.1016/j.conbuildmat.2015.10.088.
Sikorski, D., H. Tabuteau, and J. R. D. Bruyn. 2009. “Motion and shape of bubbles rising through a yield-stress fluid.” J. Non-Newtonian Fluid Mech. 159 (1–3): 10–16. https://doi.org/10.1016/j.jnnfm.2008.11.011.
Szwabowski, J., and B. Łaźniewska-Piekarczyk. 2008. “The increase of air-content in SCC mixes under the influence of carboxylate superolasticizers.” Cem. Wapno Beton 4: 205–215.
Tripathi, M. K., K. C. Sahu, G. Karapetsas, and O. K. Matar. 2015. “Bubble rise dynamics in viscoplastic material.” J. Non-Newtonian Fluid Mech. 222: 217–226. https://doi.org/10.1016/j.jnnfm.2014.12.003.
Wang, D. H., C. J. Shi, Z. M. Wu, J. F. Xiao, Z. Y. Huang, and Z. Fang. 2015. “A review on ultra high performance concrete. Part II: Hydration, microstructure and properties.” Constr. Build. Mater. 96: 368–377. https://doi.org/10.1016/j.conbuildmat.2015.08.095.
Zhang, B. L., H. B. Tan, W. G. Shen, G. L. Xu, B. G. Ma, and X. L. Ji. 2018. “Nano-silica and silica fume modified cement mortar used as Surface Protection Material to enhance the impermeability.” Cem. Concr. Compos. 92: 7–17. https://doi.org/10.1016/j.cemconcomp.2018.05.012.
Zou, F. B., H. B. Tan, Y. L. Guo, B. G. Ma, X. Y. He, and Y. Zhou. 2017. “Effect of sodium gluconate on dispersion of polycarboxylate superplasticizer with different grafting density in side chain.” J. Ind. Eng. Chem. 55: 91–100. https://doi.org/10.1016/j.jiec.2017.06.032.
Information & Authors
Information
Published In
Copyright
©2019 American Society of Civil Engineers.
History
Received: Mar 7, 2018
Accepted: Sep 19, 2018
Published online: Jan 28, 2019
Published in print: Apr 1, 2019
Discussion open until: Jun 28, 2019
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.