Calcium Leaching of Cement Asphalt Paste and Its Effects on Dynamic Mechanical Properties
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 7
Abstract
Calcium leaching is an important durability issue of cement asphalt (CA) mortar used in high-speed rails. Calcium leaching affects CA mortar’s mechanical properties, which are critical for its structural performance. In this paper, the calcium leaching of CA paste and its effects on the dynamic mechanical properties of CA paste are studied. CA pastes were immersed in ammonium nitrate solution for different ages. The concentrations of the calcium and silicon ions in the leaching solution were monitored by inductively coupled plasma-atomic emission spectrometry (ICP-AES). Changes in porosity, bulk density, and contents of calcium hydroxide and calcium silicate hydrate (C-S-H) in leached specimens with time were measured. The dynamic mechanical properties of CA paste were measured by dynamic mechanical thermal analysis (DMTA). Results showed that the calcium leaching of CA paste by ammonium nitrate solution was mostly completed within 7 days. Thermal gravity analysis (TGA) results showed that the calcium leaching, which caused significant mass loss and porosity gain, was mainly contributed by the decomposition of calcium hydroxide (CH) and partly by C-S-H gel. The addition of asphalt only changed the volume fraction of cement hydrates in the CA paste, but did not improve the leaching resistance of cement hydrates. The calcium leaching negatively affected the storage modulus, but positively affected the loss factor of CA pastes.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
Financial support by the National Natural Science Foundation of China (Grant No. 51478476) and the National Basic Research Program of China (973 Program) (Grant No. 2013CB036201) are highly appreciated.
References
Adenot, F., and M. Buil. 1992. “Modeling of the corrosion of the cement paste by deionized water.” Cem. Concr. Res. 22 (2–3): 489–496.
Berner, U. R. 1988. “Modelling the incongruent dissolution of hydrated cement minerals.” Radiochim. Acta 44–45 (2): 387–394.
Buil, M. 1992. “A model of the attack of pure water or under-saturated lime solutions on cement.” ASTM STP 1123: 227–241.
Carde, C., and R. Francois. 1997. “Effect of the leaching of calcium hydroxide from cement paste on mechanical and physical properties.” Cem. Concr. Res. 27 (4): 539–550.
Carde, C., R. Francois, and J. P. Ollivier. 1995. “Microstructural changes and mechanical effects due to the leaching of calcium hydroxide from cement paste.” In Proc., Material Research Society’s Symp. on Mechanisms of Chemical Degradation of Cement-Based Systems, edited by K. L. Scrivener and J. F. Young, 30–37. Boston.
Carde, C., R. Francois, and J. M. Torrenti. 1996. “Leaching of both calcium hydroxide and C-S-H from cement paste: Modeling the mechanical behavior.” Cem. Concr. Res. 26 (8): 1257–1268.
Chen, J. J., J. J. Thomas, and H. M. Jennings. 2006. “Decalcification shrinkage of cement paste.” Cem. Concr. Res. 36 (5): 801–809.
China Railway Ministry. 2008. Provisional technical conditions of CRTS II type of emulsified asphalt cement mortar for slab track in passenger dedicated line railway. [In Chinese.] Beijing: China Railway Ministry.
Chinese Standard. 2007. “Common portland cement.” GB175-2007. Beijing: Chinese Standard.
Deng, D. H., Q. Tian, Z. Q. Liu, and Q. Yuan. 2014. “Physical structure of hardened cement asphalt paste for the slab track of high-speed railway.” [In Chinese.] Sci. Sin. Technol. 44 (7): 661–671.
Fang, L., Q. Yuan, D. H. Deng, Y. R. Pan, and Y. Wang. 2017. “Effect of mix parameters on the dynamic mechanical properties of cement asphalt mortar.” J. Mater. Civ. Eng. 29 (8): 04017080.
Gautier, P. E. 2015. “Slab track: Review of existing systems and optimization potentials including very high speed.” Constr. Build. Mater. 92 (Sep): 9–15.
Georgios, C. 2002. “The elastic properties of calcium leached cement pastes and mortars: A multi-scale investigation.” Ph.D. dissertation, Univ. of London. http://hdl.handle.net/1721.1/65060.
Gerard, B., C. L. Bellego, and O. Bernard. 2002. “Simplified modeling of calcium leaching of concrete in various environments.” Mater. Struct. 35 (10): 632–640.
Heukamp, F. H., F. J. Ulm, and J. T. Germaine. 2001. “Mechanical properties of calcium-leached cement pastes: Triaxial stress states and the influence of the pore pressure.” Cem. Concr. Res. 31 (5): 767–774.
Huang, B., and C. X. Qian. 2011. “Experiment study of chemo-mechanical coupling behavior of leached concrete.” Constr. Build. Mater. 25 (5): 2649–2654.
Jain, J., and N. Neithalath. 2009. “Analysis of calcium leaching behavior of plain and modified cement pastes in pure water.” Cem. Concr. Compos. 31 (3): 176–185.
Jennings, H. M. 2008. “Refinements to colloid model of C-S-H in cement: CM-II.” Cem. Concr. Res. 38 (3): 275–289.
Kamali, S., M. Moranville, E. Garboczi, S. Prene, and B. Gerard. 2004. “Hydrate dissolution influence on the Young’s modulus of cement pastes.” In Proc., Int. Conf. for Fracture Mechanics of Concrete Structures. Vail, CO.
Lesueura, D., J. Petit, and H. J. Ritter. 2013. “The mechanisms of hydrated lime modification of asphalt mixtures: A state-of-the-art review.” Road Mater. Pavement Des. 14 (1): 1–16.
Mainguy, M., C. Tognazzi, J. M. Torrenti, and F. Adenot. 2000. “Modelling of leaching in pure cement paste and mortar.” Cem. Concr. Res. 30 (1): 83–90.
Powers, T. C., and T. L. Brownyard. 1948. Studies of the Physical Properties of Hardened Portland Cement Paste. Chicago: Research Laboratories of the Portland Cement Association.
RILEM (International Union of Laboratories and Experts in Construction Materials, Systems and Structures). 1984. “CPC 11.3 Absorption of water by immersion under vacuum.” Mater. Struct. 17 (101): 391–394.
Ruiz, L. A., G. Platret, E. Massieu, and A. Ehrlacher. 2005. “The use of thermal analysis in assessing the effect of temperature on a cement paste.” Cem. Concr. Res. 35 (3): 609–613.
Rutherford, T., Z. J. Wang, X. Shu, B. S. Huang, and D. Clark. 2014. “Laboratory investigation into mechanical properties of cement emulsified asphalt mortar.” Constr. Build. Mater. 65 (13): 76–83.
Taylor, H. F. W. 1997. Cement chemistry. London: Thomas Telford.
Tian, Q., Q. Yuan, L. Fang, Y. Wang, Z. Liu, and D. Deng. 2017. “Estimation of elastic modulus of cement asphalt binder with high content of asphalt.” Constr. Build. Mater. 133 (4): 98–106.
Wang, Y., Q. Yuan, D. H. Deng, T. Ye, and L. Fang. 2017. “Measuring the pore structure of cement asphalt mortar by nuclear magnetic resonance.” Constr. Build. Mater. 137 (8): 450–458.
Wang, Z. J., X. Shu, T. Rutherford, B. S. Huang, and D. Clark. 2015. “Effects of asphalt emulsion on properties of fresh cement emulsified asphalt mortar.” Constr. Build. Mater. 75 (2): 25–30.
Yuan, Q., W. T. Liu, Y. R. Pan, D. H. Deng, and Z. Q. Liu. 2016. “Characterization of cement asphalt mortar for slab track by dynamic mechanical thermoanalysis.” J. Mater. Civ. Eng. 28 (3): 04015154.
Information & Authors
Information
Published In
Copyright
©2018 American Society of Civil Engineers.
History
Received: Sep 21, 2017
Accepted: Dec 14, 2017
Published online: Apr 24, 2018
Published in print: Jul 1, 2018
Discussion open until: Sep 24, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.