Microwave Absorbing Mortar Using Magnetic Hollow Fly Ash Composite as Absorbent
Publication: Journal of Materials in Civil Engineering
Volume 30, Issue 6
Abstract
A new type of microwave absorption cement-based material was prepared by using a magnetic hollow fly ash microspheres composite as the absorbent. Through the chemical precipitation method, a nano- layer was coated on the surface of HFAM to obtain the composite. Then the composite was added into mortar to prepare microwave absorption cement-based material. The mineral components, micromorphology, and electromagnetic parameters of the composite and the reflection loss of the cement-based material were investigated. It was found that the composite had superparamagnetism, and its saturation magnetization and the residual magnetization were and almost zero, respectively. The best microwave absorption of the cement-based material was obtained at 3% composite to cement, of which the bandwidth of the reflection loss lower than (responding to 90% microwave absorption) was nearing 8 GHz, showing excellent microwave absorption performance.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The work presented in this paper was supported by the National Natural Science Foundation of China (Nos. 51372183, 50902106, and 51461135005), and the program of New Century Excellent Talents in University of China (No. NCET-10-0660).
References
Al-Ghamdi, A. A., et al. (2016). “Conductive carbon black/magnetite hybrid fillers in microwave absorbing composites based on natural rubber.” J. Compos. Part B, 96(8), 231–241.
Ashiq, M. N., Iqbal, M. J., and Gul, I. H. (2011). “Effect of Al-Cr doping on the structural, magnetic and dielectric properties of strontium hexaferrite nanomaterials.” J. Magn. Magn. Mater., 323(3), 259–263.
Balmori, A. (2009). “Electromagnetic pollution from phone masts: Effects on wildlife.” Pathophysiol., 16(2–3), 191–199.
Bi, S., Ma, L., Mei, B., Tian, Q., Liu, C. H., and Zhong, C. R. (2014). “Silicon carbide/carbon nanotube heterostructures: Controllable synthesis, dielectric properties and microwave absorption.” Adv. Powder Technol., 25(4), 1273–1279.
Deng, H., Li, X., Peng, Q., Wang, X., Chen, J. P., and Li, Y. D. (2005). “Monodisperse magnetic single-crystal ferrite microspheres.” Angew. Chem. Int. Ed., 44(18), 2782–2785.
Du, G. X., Wang, X. H., Tu, G. R., Zhou, X. H., and Hao, W. X. (2006). “Preparation of microwave absorbing ceramic material by electroless Ni-Co plating.” Chin. J. Inorg. Chem., 22(2), 281–286 (in Chinese).
Guan, H., Liu, S., Duan, Y., and Zhao, Y. (2007). “Investigation of the electromagnetic characteristics of cement based composites filled with EPS.” Cem. Concr. Compos., 29(1), 49–54.
He, Z., Qi, S., Zhong, X., Oiu, H., and Wang, J. (2014). “Preparation and microwave absorbing properties of hollow glass composites with core-shell structure.” J. Mater. Sci. Mater. Electron., 25(8), 3455–3460.
Kashi, S., Gupta, R. K., Baum, T., Kao, N., and Bhattacharya, S. N. (2016). “Morphology, electromagnetic properties and electromagnetic interference shielding performance of poly lactide/graphene nanoplatelet nanocomposites.” Mater. Des., 95(4), 119–126.
Koops, C. G. (1951). “On the dispersion of resistivity and dielectric constant of some semiconductors at audio frequencies.” Phys. Rev., 83(1), 121–124.
Krishnaveni, T., Kanth, B. R., Raju, V. S. R., and Murthy, S. R. (2006). “Fabrication of multilayer chip inductors using Ni-Cu–Zn ferrites.” J. Alloys Compd., 414(1), 282–286.
Li, B. Y., Duan, Y. P., and Liu, S. H. (2012). “The electromagnetic characteristics of fly ash and absorbing properties of cement-based composites using fly ash as cement replacement.” Constr. Build. Mater., 27(1), 605–611.
Li, G., Hu, G. G., Zhou, H. D., Fan, X. J., and Li, X. G. (2002). “Attractive microwave-absorbing properties of manganite powders.” Mater. Chem. Phys., 75(1), 101–104.
Li, W., Wei, J., Wang, W., Hu, D., Li, Y., and Guan, J. (2016). “Ferrite-based metamaterial microwave absorber with absorption frequency magnetically tunable in a wide range.” Mater. Des., 110(15), 27–34.
Li, X., et al. (2006). “Preparation of low-density superparamagnetic microspheres by coating glass micro balloons with magnetite nanoparticles.” Mater. Sci. Eng. B., 135(1), 38–43.
Li, X. A., Zhang, B., Ju, C. H., Han, X. J., Du, Y. C., and Xu, P. (2011). “Morphology-controlled synthesis and electromagnetic properties of porous nanostructures from iron alkoxide precursors.” J. Phys. Chem. C., 115(25), 12350–12357.
Liu, Q., et al. (2013). “Solvothermal synthesis of hollow glass composites as a lightweight microwave absorber.” J. Mater. Sci., 48(17), 6048–6055.
Muthusamy, S., and Chung, D. D. L. (2010). “Carbon-fiber cement-based materials for electromagnetic shielding.” ACI Mater. J., 107(6), 602–610.
Nam, I. W., Lee, H. K., Sim, J. B., and Choi, S. M. (2012). “Electromagnetic characteristics of cement matrix materials with carbon nanotubes.” ACI Mater. J., 109(3), 363–370.
Unver, I. S., and Durmus, Z. (2017). “Magnetic and microwave absorption properties of magnetite ()@conducting polymer (PANI, PPY, PT) composites.” IEEE Trans. Magn., 53(10), 1–8.
Wang, L. B., See, K. Y., Ling, Y., and Koh, W. J. (2012). “Study of metal foams for architectural electromagnetic shielding.” J. Mater. Civ. Eng., 488–493.
Wei, J., Liu, J. H., and Li, S. M. (2007). “Electromagnetic and microwave absorption properties of magnetic films plated on hollow glass spheres.” J. Magn. Magn. Mater., 312(2), 414–417.
Xu, J., et al. (2007). “Preparation and magnetic properties of magnetite nanoparticles by sol-gel method.” J. Magn. Magn. Mater., 309(2), 307–311.
Yang, C. M., Li, H. Y., Xiong, D. B., and Cao, Z. Y. (2009). “Hollow microsphere composites: Preparation, characterization, and applications in microwave absorption.” React. Funct. Polym., 69(2), 137–144.
Zhang, X. M., et al. (2015). “Thermal conversion of an @metal-organic framework: A new method for an efficient Fe-Co/nanoporous carbon microwave absorbing material.” Nanoscale, 7(30), 12932–12942.
Zhang, X. Z., and Sun, W. (2010). “Microwave absorbing properties of double-layer cementitious composites containing Mn-Zn ferrite.” Cem. Concr. Compos., 32(9), 726–730.
Zhu, L. Y., Zeng, X. J., Li, X. P., Yang, B., and Yu, R. H. (2017). “Hydrothermal synthesis of magnetic /graphene composites with good electromagnetic microwave absorbing performances.” J. Magn. Magn. Mater., 426(7), 114–120.
Information & Authors
Information
Published In
Copyright
©2018 American Society of Civil Engineers.
History
Received: Jun 29, 2017
Accepted: Dec 4, 2017
Published online: Apr 12, 2018
Published in print: Jun 1, 2018
Discussion open until: Sep 12, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.