Hydration and Properties of Slag Cement Activated by Alkali and Sulfate
Publication: Journal of Materials in Civil Engineering
Volume 29, Issue 9
Abstract
In this paper, the results of a study on the influence of sodium hydroxide, calcium hydroxide, aluminum hydroxide, sodium sulfate, calcium sulfate, and calcium sulfate dihydrate as activators on the setting time and mechanical properties of slag–cement mixtures are presented. The results obtained show that the sulfate is more effective in activating the activity of the slag cement than the other chemical activators. Specimens prepared from calcium sulfate, blast-furnace slag, and ordinary portland cement exhibit better mechanical performance compared to admixtures prepared from other mix ratios. The sulfate ions from sulfates would react with from slag cement and form the reaction product ettringite. However, the addition of sodium hydroxide seems ineffective in activating the slag cement. Successive addition of sodium hydroxide deteriorates the mechanical strength of the slag cement. The reaction kinetics are also studied by examining the hydration products of slag-blended cement paste through the technologies of X-ray diffraction (XRD), scanning electron microscopy (SEM), and nuclear magnetic resonance spectroscopy (NMR). Those experimental results provide detailed insights into the understanding of how the activators influence the hydration products of slag-blended cement and structural models of calcium silicate hydrates (C-S-H).
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This research work was financially supported by the National Natural Science Foundation of China, Grant No. 51378309.
References
ASTM. (2005). “Standard test methods for time of setting of hydraulic cement mortar by modified vicat needle.” ASTM C807-05, West Conshohocken, PA.
Bellmann, F., and Stark, J. (2009). “Activation of blast furnace slag by a new method.” Cem. Concr. Res., 39(8), 644–650.
Fernández-Jiménez, A., Puertas, F., Sobrados, I., and Sanz, J. (2003). “Structure of calcium silicate hydrates formed in alkaline-activated slag: influence of the type of alkaline activator.” J. Am. Ceram. Soc., 86(8), 1389–1394.
Fredericci, C., Zanotto, E., and Ziemath, E. (2000). “Crystallization mechanism and properties of a blast furnace slag glass.” J. Non-Cryst. Solids, 273(1), 64–75.
Glukhovsky, V., Rostovskaja, G., and Rumyna, G. (1980). “High strength slag-alkaline cements.” Proc., 7th Int. Congress on the Chemistry of Cement, Editions Septima, Paris.
Guo, X. L., and Shi, H. S. (2013). “Modification of steel slag powder by mineral admixture and chemical activators to utilize in cement-based materials.” Mater. Struct., 46(8), 1265–1273.
Hilbig, H., and Buchwald, A. (2006). “The effect of activator concentration on reaction degree and structure formation of alkali-activated ground granulated blast furnace slag.” J. Mater. Sci., 41(19), 6488–6491.
Kourounis, S., Tsivilis, S., Tsakiridis, P. E., Papadimitriou, G. D., and Tsibouki, Z. (2007). “Properties and hydration of blended cements with steelmaking slag.” Cem. Concr. Res., 37(6), 815–822.
Krivenko, P. V., Skurchinskaya, J. V., and Sidorenko, J. A. (1993). “The sodium sulfate-based slag alkaline cement.” Proc., 3rd Beijing Int. Symp. on Cement and Concrete, Tsinghua University Press, China.
Krizan, D., and Zivanovic, B. (2002). “Effects of dosage and modulus of water glass on early hydration of alkali–slag cements.” Cem. Concr. Res., 32(8), 1181–1188.
Li, C., Sun, H. H., and Li, L. T. (2011). “Glass phase structure of blast furnace slag.” Adv. Mater. Res., 168(1), 3–7.
Ma, H. (2013). “Multi-scale modeling of the microstructure and transport properties of contemporary concrete.” Ph.D. thesis, Hong Kong Univ. of Science and Technology, Hong Kong.
Ma, H. (2014). “Mercury intrusion porosimetry in concrete technology: Tips of measurement, pore structure parameter acquisition and application.” J. Porous Mater., 21(2), 207–215.
Ma, H., and Li, Z. (2013). “Realistic pore structure of portland cement paste: Experimental study and numerical simulation.” Comput. Concr., 11(4), 317–336.
Martinez-Aguilar, O., Castro-Borges, P., and Escalante-García, J. (2010). “Hydraulic binders of fluorgypsum–portland cement and blast furnace slag, stability and mechanical properties.” Constr. Build. Mater., 24(5), 631–639.
Matschei, T., Bellmann, F., and Stark, J. (2005). “Hydration behaviour of sulphate-activated slag cements.” Adv. Cem. Res., 17(4), 167–178.
Murgier, S., Zanni, H., and Gouvenot, D. (2004). “Blast furnace slag cement: A and NMR study.” C. R. Chim., 7(3–4), 389–394.
Osborne, G. (1999). “Durability of portland blast-furnace slag cement concrete.” Cem. Concr. Compos., 21(1), 11–21.
Papayianni, I., and Anastasiou, E. (2010). “Production of high-strength concrete using high volume of industrial by-products.” Constr. Build. Mater., 24(8), 1412–1417.
PCPDFWIN version 2.0 [Computer software]. International Center for Diffraction Data, Newtown Square, PA.
Powers, T. C. (1900). “Studies of the physical properties of hardened portland cement paste.” J. Am. Ceram. Soc., 41(1), 1–6.
Purdon, A. (1940). “The action of alkalis on blast-furnace slag.” J. Soc. Chem. Ind., 59(1), 191–205.
Rashad, A., Bai, Y., Basheer, P., Collier, N., and Milestone, N. (2012). “Chemical and mechanical stability of sodium sulfate activated slag after exposure to elevated temperature.” Cem. Concr. Res., 42(2), 333–343.
Rashad, A., Bai, Y., Basheer, P., Milestone, N., and Collier, N. (2013). “Hydration and properties of sodium sulfate activated slag.” Cem. Concr. Compos., 37(1), 20–29.
Richardson, I., Brough, A., Groves, G., and Dobson, C. (1994). “The characterization of hardened alkali-activated blast-furnace slag pastes and the nature of the calcium silicate hydrate (CSH) phase.” Cem. Concr. Res., 24(5), 813–829.
Richardson, I., and Groves, G. (1997). “The structure of the calcium silicate hydrate phases present in hardened pastes of white portland cement/blast-furnace slag blends.” J. Mater. Sci., 32(18), 4793–4802.
Schneider, J., Cincotto, M. A., and Panepucci, H. (2001). “ and high-resolution NMR characterization of calcium silicate hydrate phases in activated blast-furnace slag pastes.” Cem. Concr. Res., 31(7), 993–1001.
Shi, C., and Day, R. L. (1996). “Some factors affecting early hydration of alkali-slag cements.” Cem. Concr. Res., 26(3), 439–447.
Wang, Q., Yan, P., and Mi, G. (2012). “Effect of blended steel slag—GBFS mineral admixture on hydration and strength of cement.” Constr. Build. Mater., 35(0), 8–14.
Wang, S.-D., Pu, X.-C., Scrivener, K., and Pratt, P. (1995). “Alkali-activated slag cement and concrete: A review of properties and problems.” Adv. Cem. Res., 7(27), 93–102.
Wang, S.-D., and Scrivener, K. L. (2003). “ and NMR study of alkali-activated slag.” Cem. Concr. Res., 33(5), 769–774.
Wu, X., Jiang, W., and Roy, D. M. (1990). “Early activation and properties of slag cement.” Cem. Concr. Res., 20(6), 961–974.
Yüksel, İ., Bilir, T., and Özkan, Ö. (2007). “Durability of concrete incorporating non-ground blast furnace slag and bottom ash as fine aggregate.” Build. Environ., 42(7), 2651–2659.
Živica, V. (2007). “Effects of type and dosage of alkaline activator and temperature on the properties of alkali-activated slag mixtures.” Constr. Build. Mater., 21(7), 1463–1469.
Information & Authors
Information
Published In
Copyright
©2017 American Society of Civil Engineers.
History
Received: Mar 11, 2016
Accepted: Nov 2, 2016
Published online: Apr 13, 2017
Published in print: Sep 1, 2017
Discussion open until: Sep 13, 2017
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.