Characterization of Self-Healing Processes Induced by Calcium Nitrate Microcapsules in Cement Mortar
Publication: Journal of Materials in Civil Engineering
Volume 29, Issue 1
Abstract
The objective of this study was to evaluate the self-healing effectiveness of urea-formaldehyde microcapsules with calcium nitrate as a healing agent in cement mortar. Calcium nitrate was selected as a healing agent because of its ability to react with available unhydrated cement particles in crack surfaces contributing to the formation of new hydration products that may potentially heal the crack. Self-healing capability of cement mortar with different microcapsule contents was evaluated under dry and wet healing conditions. Cracks ranging from 27.0 to 386.5 μm on average were created by three-point bending and indirect tensile tests. Cracks were observed by light microscopy over a 28-day healing period. Analysis of captured images showed signs of healing in the form of small crystallike features on the edge of the cracks on water-cured specimens after 7 days of healing. Furthermore, an improvement in self-healing efficiency was reported in specimens with microcapsule contents of 0.85 and 1.0% compared to the control after 14 days of the healing period. Environmental scanning electron microscopy (ESEM) coupled with energy dispersive spectroscopy (EDS) was utilized to investigate the morphology and chemical nature of the healing products. Crystallike and gellike healing products were found with the majority being crystallike. Crystallike healing products were likely calcium carbonate in the form of calcite crystals, whereas gellike healing product’s chemical nature was presumably calcium silicate hydrate (CSH).
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors would like to acknowledge the financial support through a grant from Qatar National Research Foundation (QNRF)/ National Priorities Research Program (NPRP) as well as the laboratory support from Louisiana Transportation Research Center (LTRC).
References
Abdelrazig, B. E. I., Bonner, D. G., Nowell, D. V., Dransfield, J. M., and Egan, P. J. (1999). “The solution chemistry and early hydration of ordinary Portland cement pastes with and without admixtures.” Thermochim. Acta, 340-341, 417–430.
Balonis, M., Medala, M., and Glasser, F. P. (2011). “Influence of calcium nitrate and nitrite on the constitution of AF, and AFt cement hydrates.” Adv. Cem. Res., 23(3), 129–143.
Edvardsen, C. (1999). “Water permeability and autogenous healing of cracks in concrete.” ACI Mater. J., 96(4), 448–454.
Gilford, J., III, Hassan, M., Rupnow, T., Barbato, M., Okeil, A., and Asadi, S. (2014). “Dicyclopentadiene and sodium silicate microencapsulation for self-healing of concrete.” J. Mater. Civ. Eng., 886–896.
Hassan, M., Milla, J., Rupnow, T., Al-Ansari, M., and Daly, B. (2016). “Micro-encapsulation of calcium nitrate for concrete applications.” Transp. Res. Rec., in press.
Huang, H., and Ye, G. (2011). “Application of sodium silicate solution as self-healing agent in cementitious materials.” Int. RILEM Conf. on Advances in Construction Materials through Science and Engineering, Vol. 1, RILEM Publications SARL, Hong Kong, China, 530–535.
Justnes, H. (1995). “Technical calcium nitrate as set accelerator for cement at low temperatures.” Cem. Concr. Res., 25(8), 1766–1774.
Justnes, H. (2003). “Explanation of long-term compressive strength of concrete cause by the set accelerator calcium nitrate.” International Congress on the Chemistry of Cement (ICCC), Durban, South Africa, 475–484.
Justnes, H. (2010). “Calcium nitrate as a multifunctional concrete admixture.” Concrete, 44(1), 34–36.
Kaes, M., Van Tittelboom, K., and De Belie, N. (2014). “The efficiency of self-healing cementitious materials by means of encapsulated polyurethane in chloride containing environments.” Constr. Build. Mater., 71, 528–537.
Karagöl, F., Demirboga, R., Kaygusuz, M. A., Yadollahi, M. M., and Polat, R. (2013). “The influence of calcium nitrate as antifreeze admixture on the compressive strength of concrete exposed to low temperatures.” Cold Reg. Technol., 89, 30–35.
Li, V. C., and Hebert, E. (2012). “Robust self-healing concrete for sustainable infrastructure.” J. Adv. Concr. Technol., 10(6), 207–218.
Li, W., Jiang, Z., Yang, Z., Zhao, N., and Yuan, W. (2013). “Self-healing efficiency of cementitious materials containing microcapsules filled with healing adhesive: Mechanical restoration and healing process monitored by water absorption.” PLoS One, 8(11), e81616.
Lv, Z., and Chen, H. (2014). “A probabilistic method for determining the volume fraction of pre-embedded capsules in self-healing materials.” Smart Mater. Struct., 23(11), 115009.
Milla, J., Hassan, M., Rupnow, T., Al-Ansari, M., and Arce, G. (2016). “Evaluation of the effect of self-healing calcium nitrate microcapsules on concrete properties.” J. Transp. Res. Rec., in press.
Pelletier, M., Brown, R., Shukla, A., and Bose, A. (2015). “Self-healing concrete with a microencapsulated healing agent.” 〈http://energetics.chm.uri.edu/system/files/Self%20healing%20concrete%20-7-11.pdf〉 (Jul. 3, 2015).
Ramachandran, V. S. (1995). Concrete admixtures handbook, 2nd Ed., Noyes Publications, NJ, 740–756.
Van Tittelboom, K., and De Belie, N. (2013). “Self-healing in cementitious materials: A review.” Materials, 6(6), 2182–2217.
Van Tittelboom, K., De Belie, N., Van Loo, D., and Jacobs, P. (2011). “Self-healing efficiency of cementitious materials containing tubular capsules filled with healing agent.” Cem. Concr. Compos., 33(4), 497–505.
Wang, J. Y., Soens, H., Verstraete, W., and De Belie, N. (2014). “Self-healing concrete by use of microencapsulated bacterial spores.” Cem. Concr. Res., 56, 139–152.
White, S. R., et al. (2001). “Autonomic healing of polymer composites.” Nature, 409(6822), 794–797.
Winter, N. B. (2012). Scanning electron microscopy of cement and concrete, WHD Microanalysis, Rendlesham, Woodbridge, U.K.
Wu, M., Johannesson, B., and Geiker, M. (2012). “A review: Self-healing in cementitious materials and engineered cementitious composite as a self-healing material.” Constr. Build. Mater., 28(1), 571–583.
Yang, Z. X., Hollar, J., He, X. D., and Shi, X. M. (2011). “A self-healing cementitious composite using oil core/silica gel shell microcapsulses.” Cem. Concr. Compos., 33(4), 506–512.
Zemskov, S. V., Jonkers, H. M., and Vermolen, F. J. (2011). “Two analytical models for the probability characteristics of a crack hitting encapsulated particles: Application to self-healing materials.” Comput. Mater. Sci., 50(12), 3323–3333.
Information & Authors
Information
Published In
Copyright
© 2016 American Society of Civil Engineers.
History
Received: Dec 11, 2015
Accepted: Jun 16, 2016
Published online: Aug 10, 2016
Published in print: Jan 1, 2017
Discussion open until: Jan 10, 2017
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.