Experimental Study on Effects of Casting Procedures on Compressive Strength, Water Permeability, and Interfacial Transition Zone Porosity of Rock-Filled Concrete
Publication: Journal of Materials in Civil Engineering
Volume 28, Issue 8
Abstract
This study investigated the effects of different casting procedures on compressive strength, water permeability, and interfacial transition zone (ITZ) porosity of rock-filled concrete (RFC). Mixes of concrete with the same proportions were cast using the self-compacting method (the casting procedure of RFC) and the vibration method (the casting procedure of normal concrete). A control group of concrete was prepared to reveal the effects of aggregate size. Compressive tests and water permeability tests were performed in accordance with the current codes. Scanning electron microscopy was used to calculate the porosity of the ITZ by processing the second electron and backscattered electron images of the ITZ. The findings indicate that the self-compacting method can improve compressive strength and particularly impermeability grade. Switching the vibration method to the self-compacting method also significantly reduces ITZ porosity, especially the ITZ porosity at the lateral surface of the aggregate.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
We thank the National Natural Science Foundation of China (Grant No. 51239006) and the National 863 Technology Research and Development Program of China (No. 2012AA06A112) for its financial support and the Ph.D. candidates Chuanhu Zhang and Xiaorong Xu for their help.
References
An, X. H., Huang, M. S., Zhou, H., and Jin, F. (2009). Rock-filled concrete in China—Self-compacting concrete for massive concrete, RILEM, Bagneux, France.
Basheer, L., Basheer, P. A. M., and Long, A. E. (2005). “Influence of coarse aggregate on the permeation durability and the microstructure characteristics of ordinary portland cement concrete.” Constr. Build. Mater., 19(9), 682–690.
Diamond, S., and Huang, J. D. (2001). “The ITZ in concrete—A different view based on image analysis and SEM observations.” Cem. Concr. Compos., 23(2-3), 179–188.
Erdem, S., Dawson, A. R., and Thom, N. H. (2012). “Influence of the micro- and nanoscale local mechanical properties of the interfacial transition zone on impact behavior of concrete made with different aggregates.” Cem. Concr. Res., 42(2), 447–458.
Feng, J., Liu, S., and Wang, Z. (2015). “Effects of ultrafine fly ash on the properties of high-strength concrete.” J. Therm. Anal. Calorim., 121(3), 1213–1223.
Gagn, R., Boisvert, A., and Michel, P. (1996). “Effect of superplasticizer dosage on mechanical properties, permeability, and freeze-thaw durability of high-strength concretes with and without silica fume.” ACI Mater. J., 93(2), 111–120.
Igarashi, S.-I., Watanabe, A., and Kawamura, M. (2005). “Evaluation of capillary pore size characteristics in high-strength concrete at early ages.” Cem. Concr. Res., 35(3), 513–519.
Jin, F., An, X. H., Shi, J. J., and Zhang, C. (2005). “Study on rock-filled concrete dam.” J. Hydraul. Eng., 36(11), 1347–1352 (in Chinese).
Leemann, A., Muench, B., Gasser, P., and Holzer, L. (2006). “Influence of compaction on the interfacial transition zone and the permeability of concrete.” Cem. Concr. Res., 36(8), 1425–1433.
Ministry of Water Resources. (2006). “Test code for hydraulic concrete.”, Beijing (in Chinese).
Ollivier, J. P., Maso, J. C., and Bourdette, B. (1995). “Interfacial transition zone in concrete.” Adv. Cem. Based Mater., 2(1), 30–38.
Otsuki, N., Miyazato, S.-I., and Yodsudjai, W. (2003). “Influence of recycled aggregate on interfacial transition zone strength chloride penetration and carbonation of concrete.” J. Mater. Civ. Eng., 443–451.
Persson, B. (2001). “A comparison between mechanical properties of self-compacting concrete and the corresponding properties of normal concrete.” Cem. Concr. Res., 31(2), 193–198.
Poon, C. S., Lam, L., and Wong, Y. L. (2000). “A study on high strength concrete prepared with large volumes of low calcium fly ash.” Cem. Concr. Res., 30(3), 447–455.
Prokopski, G., and Halbiniak, J. (2000). “Interfacial transition zone in cementitious materials.” Cem. Concr. Res., 30(4), 579–583.
Schulze, J. (1999). “Influence of water-cement ratio and cement content on the properties of polymer-modified mortars.” Cem. Concr. Res., 29(6), 909–915.
Scrivener, K. L., and Nemati, K. M. (1996). “The percolation of pore space in the cement paste aggregate interfacial zone of concrete.” Cem. Concr. Res., 26(1), 35–40.
Wong, H. S., Zobel, M., Buenfeld, N. R., and Zimmerman, R. W. (2009). “Influence of the interfacial transition zone and microcracking on the diffusivity permeability and sorptivity of cement-based materials after drying.” Mag. Concr. Res., 61(8), 571–589.
Xie, Y. T., Corr, D. J., Chaouche, M., Jin, F., and Shah, S. P. (2014). “Experimental study of filling capacity of self-compacting concrete and its influence on the properties of rock-filled concrete.” Cem. Concr. Res., 56, 121–128.
Yang, C. C., and Su, J. K. (2002). “Approximate migration coefficient of interfacial transition zone and the effect of aggregate content on the migration coefficient of mortar.” Cem. Concr. Res., 32(10), 1559–1565.
Information & Authors
Information
Published In
Copyright
© 2016 American Society of Civil Engineers.
History
Received: Apr 28, 2015
Accepted: Dec 1, 2015
Published online: Mar 1, 2016
Published in print: Aug 1, 2016
Discussion open until: Aug 1, 2016
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.