Effectiveness of Products in Managing Metallic Corrosion Induced by Cyclic Deicer Exposure: Laboratory Study Using Multielectrode Array Sensors, Electrochemical Impedance, and Laser Profilometer
Publication: Journal of Materials in Civil Engineering
Volume 28, Issue 5
Abstract
A total of 12 multielectrode array sensors were utilized to assess the individual effectiveness of two corrosion inhibitors and one coating under cyclic deicer exposure conditions. There were four sensor groups, and each group consisted of nine-pin probes that were fabricated from 1008 carbon steel, 304 stainless steel, and 1100 aluminum, respectively. A total of two environmental exposure tests were conducted, in which 2.3% NaCl and 3.0% solutions were used as salt, respectively. The two tests each included eight environmental cycles and with 24 h per cycle. For all the exposed sensors, the most severe corrosion occurred at the beginning of the humidity stage. For sensors in the control group, exhibited a corrosion attack throughout the exposure period, whereas NaCl only exhibited an apparent corrosion attack during the humidity stage. Both the sensor corrosion rates and mass loss results indicate that the inhibitors had a much greater effect for than for NaCl. Although the coating showed significant benefits in protecting the metallic substrates, the cyclic exposure to led to greater coating deterioration than did NaCl. For validation, impedance measurements were conducted on carbon steel panels subjected to similar exposures, and three-dimensional laser profilometer scans were performed to characterize their surface morphology after the exposures.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The research reported herein was financially supported by the Washington Department of Transportation (WSDOT) as well as the Research & Innovative Technology Administration (RITA) at the U.S. Department of Transportation (USDOT) through the Alaska University Transportation Center (AUTC) and Western Transportation Institute. The authors thank all the professionals who provided products for testing and Yan Zhang for his assistance in the laboratory testing. The authors also acknowledge the funding support by the ChuTian Scholar Visiting Professorship Fund provided by the Hubei Department of Education to Wuhan Polytechnic University. The authors neither declare any conflict of interest nor endorse any product or test protocol. The brand names were mentioned for the convenience of the reader only, and the findings are constrained to the investigated conditions and should not be generalized.
References
Budiansky, N. D., Bocher, F., Cong, H., Hurley, M. F., and Scully, J. R. (2007). “Use of coupled multi-electrode arrays to advance the understanding of selected corrosion phenomena.” Corrosion, 63(6), 537–554.
Fay, L., and Shi, X. (2011). “Laboratory investigation of performance and impacts of snow and ice control chemicals for winter road service.” J. Cold Reg. Eng., 89–114.
He, X., and Shi, X. (2009). “Self-repairing coating for corrosion protection of aluminum alloys.” Prog. Org. Coat., 65(1), 37–43.
Li, Y., Fang, Y., Seeley, N., Jungwirth, S., Jackson, E., and Shi, X. (2013). “Corrosion by chloride deicers on highway maintenance equipment: Renewed perspective and laboratory investigation.” Transportation Research Record, 2361, 106–113.
Li, Y., Kumar, P., Shi, X., Nguyen, T. A., Xiao, Z., and Wu, J. (2012). “Electroless synthesis of Ni-P and Ni-P-Zn alloy coatings for protecting steel rebar from chloride-induced corrosion.” Int. J. Electrochem. Sci., 7, 8151–8169.
Li, Y., Zhang, Y., Jungwirth, S., Seely, N., Fang, Y., and Shi, X. (2014). “Corrosion inhibitors for metals in maintenance equipment: Introduction and recent developments.” Corros. Rev., 32(5–6), 163–181.
Menzies, T. R. (1992). “Overview of National Research Council study on the comparative costs of using rock salt and CMA for highway deicing.” Resour. Conserv. Recycl., 7(1), 43–50.
Monty, C., Miller, C. M., Schneider IV, W. H., and Rodriguez, A. (2014). “Evaluation of the effectiveness of salt neutralizers for washing snow and ice equipment.”, Ohio Dept. of Transportation, Columbus, OH.
SAE International. (2003). “Laboratory cyclic corrosion test.” The SAE Automotive Corrosion and Prevention Committee, 〈http://standards.sae.org/j2334_200312/〉.
Shi, X., Fay, L., Yang, Z., Nguyen, T. A., and Liu, Y. (2009a). “Corrosion of deicers to metals in transportation infrastructure: Introduction and recent developments.” Corros. Rev., 27(1–2), 23–52.
Shi, X., Fortune, K., Smithlin, R., Akin, M., and Fay, L. (2013a). “Exploring the performance and corrosivity of chloride deicer solutions: Laboratory investigation and quantitative modeling.” Cold Reg. Sci. Technol., 86, 36–44.
Shi, X., Li, Y., Jungwirth, S., Fang, Y., Seeley, N., and Jackson, E. (2013b). “Identification and laboratory assessment of best practices to protect DOT equipment from the corrosive effect of chemical deicers.”, Washington State Dept. of Transportation, Olympia, WA.
Shi, X., Nguyen, T. A., Suo, Z., Liu, Y., and Avci, R. (2009b). “Effect of nanoparticles on the anticorrosion and mechanical properties of epoxy coating.” Surf. Coat. Technol., 204(3), 237–245.
Shi, X., Veneziano, D., Xie, N., and Gong, J. (2013c). “Use of chloride-based ice control products for sustainable winter maintenance: A balanced perspective.” Cold Reg. Sci. Technol., 86, 104–112.
Stephens, E., Pitman, S., Mattlin, K., Chamberlin, C., and Mahl, M. (2006). “Effects of highway ice-clearing treatments on corrosion of heavy vehicle materials and components.” A Project Interim Rep. Presentation for the Pacific Northwest Snowfighters Association, Helena, MT.
Tan, Y., Aung, N. N., and Liu, T. (2012). “Evaluating localised corrosion intensity using the wire beam electrode.” Corros. Sci., 63, 379–386.
Tan, Y., and Liu, T. (2013). “Inhibiting localized corrosion of aluminum and aluminum alloy by rare earth metal compounds: Behaviors and characteristics observed using an electrochemically integrated multi-electrode array.” J. Electrochem. Soc., 160(4), C147–C158.
Tedim, J., et al. (2012). “Zn–Al layered double hydroxides as chloride nanotraps in active protective coatings.” Corros. Sci., 55, 1–4.
Wang, Y., Underhill, R. S., and Klassen, B. (2006). “Review of corrosion control programs and research activities for army vehicles.”, Defense Research and Development Canada, Ottawa.
Xi, Y., and Xie, Z. (2002). “Corrosion effects of magnesium chloride and sodium chloride on automobile components.”, Colorado Dept. of Transportation, Denver.
Yang, L., and Chiang, K. T. (2009). “A review of coupled multielectrode array sensors for corrosion monitoring and a study on the behaviors of the anodic and cathodic electrodes.” J. ASTM Int., 6(3), 16–25.
Yang, L., Chiang, K. T., Yu, H., Pabalan, R. T., Dasgupta, B., and Ibarra, L. (2014). “Threshold chloride levels for localized carbon steel corrosion in simulated concrete pore solutions using coupled multielectrode array sensors.” Corrosion, 70(8), 850–857.
Yang, L., and Sridhar, N. (2006). “Coupled multielectrode array systems and sensors for real-time corrosion monitoring—A review.” Proc., Corrosion/2006, NACE International, San Diego.
Yu, H., Chiang, K. T. K., and Yang, L. (2012). “Threshold chloride level and characteristics of reinforcement corrosion initiation in simulated concrete pore solutions.” Constr. Build. Mater., 26(1), 723–729.
Zhang, X., Leygraf, C., and Wallinder, I. O. (2013). “Atmospheric corrosion of Galfan coatings on steel in chloride-rich environments.” Corros. Sci., 73, 62–71.
Information & Authors
Information
Published In
Copyright
© 2015 American Society of Civil Engineers.
History
Received: Dec 22, 2014
Accepted: Aug 11, 2015
Published online: Nov 6, 2015
Discussion open until: Apr 6, 2016
Published in print: May 1, 2016
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.