Monitoring of Sulfate Attack in Concrete by and MAS NMR Spectroscopy
Publication: Journal of Materials in Civil Engineering
Volume 27, Issue 8
Abstract
and magic angle spinning (MAS) nuclear magnetic resonance (NMR) spectroscopy techniques were employed towards evaluation of hydrated cement paste and concrete subjected to accelerated sulfate attack. Quantitative analyses of the NMR spectra of specimens subjected to different periods of sulfate attack indicated that the chain length of tetrahedra was lowered by sulfate attack. NMR spectra indicated that sulfate attack produced a significant rise in the intensity of ettringite and a sharp drop in the concentration of monosulfate hydrate, which are some primary indications of sulfate attack on concrete. Fourier-transform infrared (FTIR) spectroscopy method was employed in order to verify the result of NMR spectroscopy.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The writers wish to acknowledge the financial support of the DOT Contract No. DTRT57-12-C-10064 for the research reported in this paper. The writers are thankful to Fred Faridazar from U.S. DOT (Turner-Fairbank Highway Research Center) for guidance and support throughout the project. The writers are also thankful to Dr. Rui H. Huang to run NMR spectroscopy on prepared samples.
References
Andersen, M. D., Jakobsen, H. J., and Skibsted, J. (2004). “Characterization of white portland cement hydration and the C-S-H structure in the presence of sodium aluminate by and MAS NMR spectroscopy.” Cement Concrete Res., 34(5), 857–868.
ASTM. (2005). “Standard specification for chemical admixtures for concrete.” C494/C494M-05a, West Conshohocken, PA.
ASTM. (2012). “Standard test method for length change of hydraulic-cement mortars exposed to a sulfate solution.” C1012, West Conshohocken, PA.
ASTM. (2013). “Standard test methods for chemical analysis of hydraulic cement.” C114, West Conshohocken, PA.
Baghabra Al-Amoudi, O. S. (2002). “Attack on plain and blended cements exposed to aggressive sulfate environments.” Cement Concrete Compos., 24(3), 305–316.
Bensted, J. (1999). “Thaumasite—Background and nature in deterioration of cements, mortars and concretes.” Cement Concrete Compos., 21(2), 117–121.
Broekmans, M. A. T. M. (2009). “Petrography as an essential complementary method in forensic assessment of concrete deterioration: Two case studies.” Mater. Charact., 60(7), 644–654.
Brunet, F., Charpentier, T., Chao, C. N., Peycelon, H., and Nonat, A. (2010). “Characterization by solid-state NMR and selective dissolution techniques of anhydrous and hydrated CEM V cement pastes.” Cement Concrete Res., 40(2), 208–219.
Cano-Barrita, P. F., et al. (2009). “Embedded NMR sensors to monitor evaporable water loss caused by hydration and drying in portland cement mortar.” Cement Concrete Res., 39(4), 324–328.
Chatterji, S. (2005). “Chemistry of alkali-silica reaction and testing of aggregates.” Cement Concrete Compos., 27(7–8), 788–795.
Cohen, M. (1983). “Theories of expansion in sulfoaluminate-type expansive cements: Schools of thought.” Cement Concrete Res., 13(6), 809–818.
Comi, C., Fedele, R., and Perego, U. (2009). “A chemo-thermo-damage model for the analysis of concrete dams affected by alkali-silica reaction.” Mech. Mater., 41(3), 210–230.
Dai, J.-G., Akira, Y., Wittmann, F. H., Yokota, H., and Zhang, P. (2010). “Water repellent surface impregnation for extension of service life of reinforced concrete structures in marine environments: The role of cracks.” Cement Concrete Compos., 32(2), 101–109.
Detwiler, R. J., Taylor, P. C., Powers, L. J., Corley, W. G., Delles, J. B., and Johnson, B. R. (2000). “Assessment of concrete in sulfate soils.” J. Perform. Constr. Facil., 89–96.
Haselbach, L. M., and Ma, S. (2008). “Potential for carbon adsorption on concrete: Surface XPS analyses.” Environ. Sci. Technol., 42(14), 5329–5334.
Idiart, A. E., Lopez, C. M., and Carol, I. (2011). “Chemo-mechanical analysis of concrete cracking and degradation due to external sulfate attack: A meso-scale model.” Cem. Concr. Compos., 33(3), 411–423.
Irassar, E., Bonavetti, V., and Gonzalez, M. (2003). “Microstructural study of sulfate attack on ordinary and limestone portland cements at ambient temperature.” Cement Concrete Res., 33(1), 31–41.
James, B., Laila, R., and Alizadeh, R. (2009). “A MAS NMR study of modified C-S-H nanostructures.” Cement Concrete Compos., 31(8), 585–590.
Juel, I., Herfort, D., Gollop, R., Konnerup-Madsen, J., Jakobsen, H. J., and Skibsted, J. (2003). “A thermodynamic model for predicting the stability of thaumasite.” Cement Concrete Compos., 25(8), 867–872.
Limbachiya, M. C., Marrocchino, E., and Koulouris, A. (2007). “Chemical-mineralogical characterisation of coarse recycled concrete aggregate.” Waste Manage., 27(2), 201–208.
Liu, T., Zou, D., Teng, J., and Yan, G. (2012). “The influence of sulfate attack on the dynamic properties of concrete column.” Constr. Build. Mater., 28(1), 201–207.
Liu, Z., De Schutter, G., Deng, D., and Yu, Z. (2010). “Micro-analysis of the role of interfacial transition zone in ‘salt weathering’ on concrete.” Constr. Build. Mater., 24(11), 2052–2059.
Ma, B., Gao, X., Byars, E. A., and Zhou, Q. (2006). “Thaumasite formation in a tunnel of Bapanxia Dam in western China.” Cement Concrete Res., 36(4), 716–722.
Mehta, P. K., and Monteiro, P. J. M. (2006). Concrete microstructure, properties, and materials, McGraw-Hill, New York.
Millard, S. G., Molyneaux, T. C. K., Barnett, S. J., and Gao, X. (2010). “Dynamic enhancement of blast-resistant ultra high performance fibre-reinforced concrete under flexural and shear loading.” Int. J. Impact Eng., 37(4), 405–413.
MNOVA version 9.0.1 [Computer software]. Santiago de Compostela, A Coruña, Spain, Mestrelab Research.
Monteiro, P. J., and Kurtis, K. E. (2003). “Time to failure for concrete exposed to severe sulfate attack.” Cement Concrete Res., 33(7), 987–993.
Muller, A. C. A., Scrivener, K. L., Gajewicz, A. M., and McDonald, P. J. (2013). “Use of bench-top NMR to measure the density, composition and desorption isotherm of C-S-H in cement paste.” Microporous Mesoporous Mater., 178, 99–103.
Odler, I., and Gasser, M. (1988). “Mechanism of sulfate expansion in hydrated portland cement.” J. Am. Ceram. Soc., 71(11), 1015–1020.
Pajares, I., Martinez-Ramirez, S., and Blanco-Varela, M. T. (2003). “Evolution of ettringite in presence of carbonate, and silicate ions.” Cement Concrete Compos., 25(8), 861–865.
Pardal, X., Brunet, F., Charpentier, T., Pochard, I., and Nonat, A. (2012). “ and solid-state NMR characterization of calcium-aluminosilicate-hydrate.” Inorg. Chem., 51(3), 1827–1836.
Park, Y. S., Suh, J. K., Lee, J. H., and Shin, Y. S. (1999). “Strength deterioration of high strength concrete in sulfate environment.” Cement Concrete Res., 29(9), 1397–1402.
Perlo, J., Casanova, F., and Blümich, B. (2005). “Profiles with microscopic resolution by single-sided NMR.” J. Magn. Reson., 176(1), 64–70.
Peyvandi, A., Soroushian, P., Balachandra, A. M., and Sobolev, K. (2013). “Enhancement of the durability characteristics of concrete nanocomposite pipes with modified graphite nanoplatelets.” Constr. Build. Mater., 47, 111–117.
Porteneuve, C., Zanni, H., Vernet, C., Kjellsen, K. O., Korb, J.-P., and Petit, D. (2001). “Nuclear magnetic resonance characterization of high-and ultrahigh-performance concrete: Application to the study of water leaching.” Cement Concrete Res., 31(12), 1887–1893.
Qazweeni, J. A., and Daoud, O. K. (1991). “Concrete deterioration in a 20-year-old structure in Kuwait.” Cement Concrete Res., 21(6), 1155–1164.
Ramachandran, V. S., and Beaudoin, J. J. (1999). Handbook of analytical techniques in concrete science and technology, Noyes, Norwich, New York.
Richardson, I. G. (2000). “Nature of the hydration products in hardened cement pastes.” Cement Concrete Compos., 22(2), 97–113.
Sachlova, S., Prikryl, R., and Pertold, Z. (2010). “Alkali-silica reaction products: Comparison between samples from concrete structures and laboratory test specimens.” Mater. Charact., 61(12), 1379–1393.
Sargolzahi, M., Kodjo, S. A., Rivard, P., and Rhazi, J. (2010). “Effectiveness of nondestructive testing for the evaluation of alkali-silica reaction in concrete.” Constr. Build. Mater., 24(8), 1398–1403.
Schneider, J., Cincotto, M. A., and Panepucci, H. (2001). “ and high-resolution NMR characterization of calcium silicate hydrate phases in activated blast-furnace slag pastes.” Cement Concrete Res., 31(7), 993–1001.
Schneider, J. F., Hasparyk, N. P., Silva, D. A., and Monteiro, P. J. M. (2008). “Effect of lithium nitrate on the alkali-silica reaction gel.” J. Am. Ceram. Soc., 91(10), 3370–3374.
Schneider, U., and Chen, S. W. (2005). “Deterioration of high-performance concrete subjected to attack by the combination of ammonium nitrate solution and flexure stress.” Cement Concrete Res., 35(9), 1705–1713.
Shi, X., Fay, L., Peterson, M. M., Berry, M., and Mooney, M. (2011). “A FESEM/EDX investigation into how continuous deicer exposure affects the chemistry of portland cement concrete.” Constr. Build. Mater., 25(2), 957–966.
Skibsted, J., and Hall, C. (2008). “Characterization of cement minerals, cements and their reaction products at the atomic and nano scale.” Cement Concrete Res., 38(2), 205–225.
Sotiriadis, K., Nikolopoulou, E., Tsivilis, S., Pavlou, A., Xhaniotakis, E., and Swamy, R. N. (2013). “The effect of chloride on the thaumasite form of sulfate attack of limestone cement concrete containing mineral admixtures at low temperature.” Constr. Build. Mater., 43, 156–164.
Tan, L. X., Huang, S. L., Han, J. Y., and Ding, Q. J. (2011). “Research on hydration mechanism of 50% portland cement-50% fly ash systems with TA and NMR techniques.” Adv. Mater. Res., 287–290(1), 1135–1139.
Taylor, R., Richardson, I. G., and Brydson, R. M. D. (2010). “Composition and microstructure of 20-year-old ordinary portland cement-ground granulated blast-furnace slag blends containing 0 to 100% slag.” Cement Concrete Res., 40(7), 971–983.
Villain, G., Thiery, M., and Platret, G. (2007). “Measurement methods of carbonation profiles in concrete: Thermogravimetry, chemical analysis and gammadensimetry.” Cement Concrete Res., 37(8), 1182–1192.
Wang, L., He, Z., and Dong, Y. (2013). “Investigation of the pozzolanic reaction in silica fume-cement paste by MAS NMR.” Adv. Mater. Res., 634–638(1), 2774–2777.
Ylmén, R., Jäglid, U., Steenari, B.-M., and Panas, I. (2009). “Early hydration and setting of portland cement monitored by IR, SEM and vicat techniques.” Cement Concrete Res., 39(5), 433–439.
Yun, H., et al. (2002a). “Detection of free chloride in concrete by NMR.” Cement Concrete Res., 34(3), 379–390.
Yun, H., et al. (2002b). “Developments in chlorine detection in concrete using NMR.” Proc., Society of Photooptical Instrumentation Engineers (SPIE), Vol. 4696, Bellingham, WA, 310–321.
Zanni, H., Cheyrezy, M., Maret, V., Philippot, S., and Nieto, P. (1996). “Investigation of hydration and pozzolanic reaction in reactive powder concrete (RPC) using NMR.” Cement Concrete Res., 26(1), 93–100.
Zhang, F. J., Yuan, Y. S., and Wang, R. Y. (2011). “Deterioration and evaluation method of mechanics behavior of reinforced concrete column under sulfate attack.” Mech. Mater., 90–93(1), 3085–3088.
Information & Authors
Information
Published In
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Mar 27, 2014
Accepted: Aug 5, 2014
Published online: Oct 7, 2014
Discussion open until: Mar 7, 2015
Published in print: Aug 1, 2015
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.