Quantifying the Effects of Chip Seal Volumetrics on the Occurrence of Pavement Flushing
Publication: Journal of Materials in Civil Engineering
Volume 26, Issue 8
Abstract
The reported study was undertaken to investigate the micromechanical interactions that occur between sprayed seal (chip seal) layer materials in order to examine their relationship to the initiation of flushing. In particular, the deformation patterns of chip seal pavement samples with respect to lateral cyclic loading as well as the changes that occur to the distribution of air voids within a chip seal layer during loading were investigated. The effect of binder volume and air void volume on the development of flushing of the chip seal samples was also investigated. The reported study was based on laboratory testing of chip seal pavement samples (cores) that were obtained from in-service, flushed pavements in New Zealand. The cores, of 200-mm diameter and thicknesses ranging from 32.4 to 55.5 mm, were subjected to varying levels of lateral cyclic loading using a wheel tracking machine and the deformation that had occurred on the surface of the cores was measured. The cores were then scanned using a computed tomography (CT) scanner to examine changes that had occurred to the air void volume of the cores during the wheel tracking test, and the reductions in air void volume were compared with the quantity of flushing that was displayed on the cores. The cores were tested to determine the binder volumes in order to investigate how flushing development was affected by the ratio of binder volume and air void volume. The results from the analyses demonstrated that a strong correlation existed between flushing and air void volume reduction, where a larger reduction in air void volume directly corresponded to a higher amount of flushing. The deformation pattern of the cores indicated the likely state of stability of the chip seal structure, and the state of stability in turn indicated the best method of maintenance that was required for a flushed surface. The study findings demonstrated that the combination of wheel tracking and CT scanning is an extremely effective analysis method that can be used to determine the state of stability of a chip seal and to select the best maintenance treatment for pavement flushing.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors would like to thank New Zealand Transport Agency (NZTA), Fulton Hogan Ltd, Transfield Services Ltd, Christchurch City Council, and The University of Auckland Bioengineering Institute for their contribution to this study.
References
Alderson, A. (2008). “Flushing distress mechanism in seals.” 1st Sprayed Sealing Conf.—Cost Effective High Performance Surfacings, ARRB Group, Vermont South, Victoria, Australia.
ASTM. (2005). “Standard test method for percent air voids in compacted dense and open bituminous paving mixtures.” D3203-05, West Conshohocken, PA.
ASTM. (2011). “Standard test methods for quantitative extraction of bitumen from bituminous paving mixtures.” D2172M-11, West Conshohocken, PA.
Austroads. (2006). “AGPT/T231 deformation resistance of asphalt mixtures by the wheel tracking test.” Austroads Incorporated, Sydney, Australia.
Austroads. (2008). “Seal distress mechanisms: An initial study into flushing.” Austroads Publication No. AP-T108/08, Austroads Incorporated, Sydney, Australia.
Brzezicki, J. M., and Kasperkiewicz, J. (1999). “Automatic image analysis in evaluation of aggregate shape.” J. Comput. Civ. Eng., 123–128.
Buttlar, W. G., Bozkurt, D., Al-Khateeb, G. G., and Waldhoff, A. S. (1999). “Understanding asphalt mastic behaviour through micromechanics.”, Transportation Research Board, Washington, DC.
Byers, C. C., Saleh, M. F., and Pidwerbesky, B. D. (2004). “Evaluation of melter slag as a base course material.” Int. J. Pavement Eng., 5(4), 193–199.
Coree, B. J. (1999). “Hot-mix asphalt volumetrics revisited—A new paradigm.”, Transportation Research Board, Washington, DC, 50–58.
Frost, J. D. (1999). “Editorial.” J. Comput. Civ. Eng., 59–60.
Gransberg, D., and James, D. M. B. (2005). Chip seal best practices, Transportation Research Board, Washington, DC.
Gransberg, D. D. (2005). “Chip seal program excellence in the United States.”, Transportation Research Board, Washington, DC, 72–82.
Gransberg, D. D., and Pidwerbesky, B. (2007). “Strip sealing and ultra-high-pressure watercutting technique for restoring skid resistance on low-volume roads life-cycle cost comparison.”, Transportation Research Board, Washington, DC, 234–239.
Gransberg, D. D., Pidwerbesky, B., and James, D. M. B. (2005). “Analysis of New Zealand chip seal design and construction practices, 1st.” National Conf. on Roadway Pavement Preservation, Transportation Research Board, Washington, DC.
Gray, W., and Hart, G. (2003). “Recycling of chip sealed pavements—New Zealand experience in combating top surface layer instability issues.” XXIInd PIARC World Road Congress, South African National Roads Agency, South Africa.
Kodippily, S. (2013). Modelling the flushing mechanism of thin flexible surface pavements, Civil and Environmental Engineering, Univ. of Auckland, Auckland, New Zealand.
Kodippily, S., Henning, T. F. P., and Ingham, J. M. (2012). “Detecting flushing of thin sprayed seal pavements using pavement management data.” J. Transp. Eng., 665–673.
Krishnan, J. M., and Rajagopal, K. R. (2005). “On the mechanical behavior of asphalt.” Mech. Mater., 37(11), 1085–1100.
Krishnan, J. M., and Rao, C. L. (2000). “Mechanics of air voids reduction of asphalt concrete using mixture theory.” Int. J. Eng. Sci., 38(12), 1331–1354.
Lawson, W. D., and Senadheera, S. (2009). “Chip seal maintenance—Solutions for bleeding and flushed pavement surfaces.”, Transportation Research Board, Washington, DC, 61–68.
Li, W., Sun, P., and Zhang, C. (2012). “Laboratory test study on asphalt concrete with steel slag aggregates.” Appl. Mech. Mater., 152–154, 117–120.
Masad, E., Muhunthan, B., Shashidhar, N., and Harman, T. (1999). “Internal structure characterization of asphalt concrete using image analysis.” J. Comput. Civ. Eng., 88–95.
O’Flaherty, C. A. (2002). Highways: The location, design, construction and maintenance of road pavements, 4th Ed., Butterworth-Heinemann, Oxford, U.K.
Shashidhar, N. (1999). “X-ray tomography of asphalt concrete.”, Transportation Research Board, Washington, DC, 186–192.
Taniguchi, S., Nishizaki, I., and Moriyoshi, A. (2008). “A study of longitudinal cracking in asphalt pavement using CT scanner.” Road Mater. Pavement Des., 9(3), 549–558.
Tashman, L., Wan, L., and Thyagarajan, S. (2007). “Microstructure characterization for modelling HMA behaviour using imaging technology.” Road Mater. Pavement Des., 8(2), 207–238.
Transit New Zealand. (2005). “Specifications for asphaltic concrete.”, New Zealand.
Von Quintus, H. L. (1991). Asphalt-aggregate mixture analysis system: AAMAS, Transportation Research Board, National Research Council, Washington, DC.
Wang, L., Wang, X., Mohammad, L., and Wang, Y. (2004). “Application of mixture theory in the evaluation of mechanical properties of asphalt concrete.” J. Mater. Civ. Eng., 167–174.
Information & Authors
Information
Published In
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Aug 26, 2013
Accepted: Feb 27, 2014
Published online: May 7, 2014
Published in print: Aug 1, 2014
Discussion open until: Oct 7, 2014
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.