Relationship between Chemical Shrinkage and Electrical Resistivity for Cement Pastes at Early Age
Publication: Journal of Materials in Civil Engineering
Volume 26, Issue 2
Abstract
The objective of this paper is to investigate the relationship between the chemical shrinkage and electrical resistivity of portland cement pastes during the first 3 days. Plain cement pastes with water to cement (W/C) ratios 0.3, 0.4, and 0.5 were used in this paper. Chemical shrinkage was measured by dilatometry according to industry standards for test methods for chemical shrinkage of hydraulic cement paste. Electrical resistivity was measured by a noncontacting electrical resistivity apparatus. The relationship between electrical resistivity and degree of hydration was investigated. The results obtained show that the relationship between chemical shrinkage and electrical resistivity appears to be roughly linear after 12 h. Note that the electrical resistivity after 12 h can be used to determine the chemical shrinkage and degree of hydration.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors gratefully acknowledge the financial support from the National Natural Science Foundation of China (NSFC) under Grant No. 51178202.
References
ASTM. (2007). “Standard test method for chemical shrinkage of hydraulic cement paste.” C1608-07, West Conshohocken, PA.
Bouasker, M., Mounanga, P., Turcry, P., Loukili, A., and Khelidj, A. (2008). “Chemical shrinkage of cement pastes and mortars at very early age: Effect of limestone filler and granular inclusions.” Cem. Concr. Comp., 30(1), 13–22.
Jensen, O. M., and Hansen, P. F. (2001). “Water-entrained cement-based materials I. Principles and theoretical background.” Cem. Concr. Res., 31(4), 647–654.
Justnes, H., et al. (2000). “Chemical shrinkage of cement pastes with plasticizing admixtures.” Nordic. Concr. Res., 24, 39–54.
Justnes, H., Van Gemert, A., Verboven, F., and Sellevold, E. J. (1996). “Total and external chemical shrinkage of low w/c ratio cement pastes.” Adv. Cem. Res., 8(31), 121–126.
Li, Z., Wei, X., and Li, W. (2003). “Preliminary interpretation of portland cement hydration process using resistivity measurements.” ACI Mater. J., 100(3), 253–257.
Lura, P., Winnefeld, F., and Klemm, S. (2010). “Simultaneous measurements of heat of hydration and chemical shrinkage on hardening cement pastes.” J. Therm. Anal. Calorim., 101(3), 925–932.
Parrott, L. J., Geiker, M., Gutteridge, W. A., and Killoh, D. (1990). “Monitoring portland cement hydration: Comparison of methods.” Cem. Concr. Res., 20(6), 919–926.
Sant, G., Lura, P., and Weiss, J. (2006). “Measurement of volume change in cementitious materials at early ages: Review of testing protocols and interpretation of results.”, Transportation Research Board, Washington, DC.
Information & Authors
Information
Published In
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Apr 16, 2013
Accepted: May 13, 2013
Published online: May 15, 2013
Discussion open until: Oct 15, 2013
Published in print: Feb 1, 2014
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.