Use of Natural Zeolite to Produce Self-Consolidating Concrete with Low Portland Cement Content and High Durability
Publication: Journal of Materials in Civil Engineering
Volume 25, Issue 5
Abstract
Self-consolidating concrete (SCC) is one of the innovative products in concrete technology that has been developed in recent years. However, many researchers are still trying to optimize the mixture proportions and investigate the incorporation of new materials in SCC. The typical high content of portland cement in SCC is one of the main challenges in optimization of its mixture proportions. This high cement consumption increases the production cost of SCC and, considering the large amount of emitted during portland cement production, is also undesirable from an environmental point of view. In this study, two approaches were employed to lower the portland cement content in SCC mixtures, namely, adopting a dense aggregate grading and partially replacing portland cement with natural zeolite. Portland cement was replaced by natural zeolite at different percentages to investigate the effect of this natural pozzolan on the fresh and hardened properties of the SCC mixtures. Fresh properties of the SCC mixtures were assessed by slump flow, T50 time, J-ring, and GTM screen stability tests. Compressive strength, electrical resistivity, and rapid chloride penetration tests (RCPTs) were carried out to evaluate the hardened properties of the SCC mixtures. It was concluded that producing a durable SCC mixture containing a low portland cement content of is possible while keeping the total cementitious materials content at a constant . On the basis of the fresh-SCC test results, using higher replacement levels of natural zeolite (up to 30%) led to improved segregation resistance but increased the required dosage of high-range water-reducer agent. At hardened state, using higher replacement levels of natural zeolite resulted in lower RCPT values and higher surface resistivity.
Get full access to this article
View all available purchase options and get full access to this article.
References
Ahmadi, B., and Shekarchi, M. (2010). “Use of natural zeolite as a supplementary cementitious material.” Cem. Concr. Compos., 32(2), 134–141.
ASTM. (1997). “Standard test method for electrical indication of concrete’s ability to resist chloride ion penetration.” C1202, West Conshohocken, PA.
ASTM. (2009a). “Standard test method for passing ability of self-consolidating concrete by J-ring.” C1621/C1621M–09b, West Conshohocken, PA.
ASTM. (2009b). “Standard test method for slump flow of self-consolidating concrete.” C1611/C1611M, West Conshohocken, PA.
ASTM. (2011a). “Standard specification for portland cement.” C150/C150M–11, West Conshohocken, PA.
ASTM. (2011b). “Standard test methods for chemical analysis of hydraulic cement.” C114–11, West Conshohocken, PA.
Bilim, C. (2011). “Properties of cement mortars containing clinoptilolite as a supplementary cementitious material.” Constr. Build. Mater., 25(8), 3175–3180.
Caputo, D., Liguori, B., and Colella, C. (2008). “Some advances in understanding the pozzolanic activity of zeolites: The effect of zeolite structure.” Cem. Concr. Compos., 30(5), 455–462.
Chan, S. Y. N., and Ji, X. (1999). “Comparative study of the initial surface absorption and chloride diffusion of high performance zeolite, silica fume and PFA concretes.” Cem. Concr. Compos., 21(4), 293–300.
Colella, C. (2007). “Natural zeolites and environment.” Introduction to zeolite science and practice (studies in surface science and catalysis), Vol. 168, 3rd Ed., J. Čejka, H. van Bekkum, A. Corma and F. Schueth, eds., Elsevier, Amsterdam, 999–1035.
Damtoft, J. S., Lukasik, J., Herfort, D., Sorrentino, D., and Gartner, E. M. (2008). “Sustainable development and climate change initiatives.” Cem. Concr. Res., 38(2), 115–127.
EFNARC. (2002). Specifications and Guidelines for Self-Compacting Concrete, Surrey, United Kingdom.
Felekoglu, B., Turkel, S., and Baradan, B. (2007). “Effect of water/cement ratio on the fresh and hardened properties of self-compacting concrete.” Build. Environ., 42(4), 1795–1802.
Feng, N., and Hao, T. (1998). “Mechanism of natural zeolite powder in preventing alkali-silica reaction in concrete.” Adv. Cem. Res., 10(3), 101–108.
Feng, N., Li, G. Z., and Zang, X. W. (1990). “High-strength and flowing concrete with a zeolitic mineral admixture.” Cem. Concr. Aggregates, 12(2), 61–69.
Feng, N., and Peng, G. (2005). “Applications of natural zeolite to construction and building materials in China.” Construct Build. Mater., 19(8), 579–584.
Feng, N., Yang, H., and Zu, L. (1988). “The strength effect of mineral admixture on cement concrete.” Cem. Concr. Res., 18(3), 464–472.
Florida Dept. of Transportation (FDOT). (2004). “Florida method of test for concrete resistivity as an electrical indicator of its permeability.”, Tallahassee, FL.
Freddy, L., Kandhal, P., Brown, E., Lee, D.-Y., and Kennedy, T. (1996). Hot mix asphalt materials, mixture design, and construction, 2nd Ed., National Asphalt Pavement Association Research and Education Foundation, Lanham, MD.
Georgiadis, A., Sideris, K. K., and Anagnostopoulos, N. S. (2010). “Properties of SCC produced with limestone filler or viscosity modifying admixture.” J. Mater. Civ. Eng., 22(4), 352–360.
Ghourchian, S., Wyrzykowski, M., Lura, P., Shekarchi, M., and Ahmadi, B. (2013). “An investigation on the use of zeolite aggregates for internal curing of concrete.” Construct. Build. Mater., 40, 135–144.
Hassan, A., Hossain, K., and Lachemi, M. (2009). “Corrosion resistance of self-consolidating concrete in full-scale reinforced beams.” Cem. Concr. Compos., 31(1), 29–38.
Jana, D. (2007). “A new look to an old pozzolan, clinoptilolite: A promising pozzolan in concrete.” Proc., 29th ICMA Conf. on Cement Microscopy, International Cement Microscopy Association, Quebec City, Canada, 168–206.
Janotka, I., and Števula, L. (1998). “Effect of bentonite and zeolite on durability of cement suspension under sulfate attack.” ACI Mater. J., 95(6), 710–715.
Karakurt, C., and Topcu, I. B. (2011). “Effect of blended cements produced with natural zeolite and industrial by-products on alkali-silica reaction and sulfate resistance of concrete.” Construct. Build. Mater., 25(4), 1789–1795.
Khayat, K. H. (1998). “Viscosity-enhancing admixtures for cement based materials.” Cem. Concr. Comp., 20(2–3), 171–188.
Lachemi, M., Hossain, K. M. A., Lambros, V., Nkinamubanzi, P.-C., and Bouzoubaa, N. (2004). “Performance of new viscosity enhancing admixtures in enhancing the rheological properties of cement paste.” Cem. Concr. Res., 34(6), 917–926.
Mehta, P. K. (1999). “Concrete technology for sustainable development.” Concr. Int., 21(11), 47–52.
Mehta, P. K., and Monteiro, P. J. M. (1997). Concrete: Microstructure, properties, and materials, Indian Concrete Institute, Chennai, India.
Mesbah, H. A., Yahia, A., and Khayat, K. H. (2011). “Electrical conductivity method to assess static stability of self-consolidating concrete electrical conductivity method to assess static stability of self-consolidating concrete.” Cem. Concr. Res., 41(5), 451–458.
Mielenz, R. C., Greene, K. T., and Schieltz, N. C. (1951). “Natural pozzolan for concrete.” Econ. Geo., 46(3), 311–328.
Najimi, M., Sobhani, J., Ahmadi, B., and Shekarchi, M. (2012). “An experimental study on durability properties of concrete containing zeolite as a highly reactive natural pozzolan.” Construct. Build. Mater., 35, 1023–1033.
Ortega, E. A., Cheeseman, C., Knight, J., and Loizidou, M. (2000). “Properties of alkali-activated clinoptilolite.” Cem. Concr. Res., 30(10), 1641–1646.
Perraki, T., Kakali, G., and Kontoleon, F. (2003). “The effect of natural zeolites on the early hydration of portland cement.” Micropor. Mesopor. Mater., 61(1–3), 205–212.
Ramezanianpour, A. A., Ghiasvand, E., Nickseresht, I., Mahdikhani, M., and Moodi, F. (2009). “Influence of various amounts of limestone powder on performance of portland limestone cement concretes.” Cem. Concr. Compos., 31(10), 715–720.
Ramezanianpour, A. A., Pilvar, A., Mahdikhani, M., and Moodi, F. (2011). “Practical evaluation of relationship between concrete resistivity, water penetration, rapid chloride penetration and compressive strength.” Constr. Build. Mater., 25(5), 2472–2479.
Şahmaran, S., Özkan, N., Keskin, S. B., Uzal, B., Yaman, İ. Ö., and Erdem, T. K. (2008). “Evaluation of natural zeolite as a viscosity-modifying agent for cement-based grouts.” Cem. Concr. Res., 38(7), 930–937.
Shekarchi, M., Ahmadi, B., and Najimi, M. (2012). “Use of Natural Zeolite as Pozzolanic Material in Cement and Concrete Composites.” Chapter 27, Handbook of Natural Zeolites, V. J. Inglezakis, and A. A. Zorpas, eds., Bentham Science Publishers, 665–694.
Siddique, R. (2011). “Properties of self-compacting concrete containing class F fly ash.” Mater Des., 32(3), 1501–1507.
Sobolev, K., and Amirjanov, A. (2010). “Application of genetic algorithm for modeling of dense packing of concrete aggregates.” Constr. Build. Mater., 24(8), 1449–1455.
Türkel, S., and Kandemir, A. (2010). “Fresh and hardened properties of SCC made with different aggregate and mineral admixtures.” J. Mater. Civ. Eng., 22(10), 1025–1032.
Vejmelkova, E., Keppert, M., Grzeszczyk, S., Skaliński, B., and Černý, R. (2010). “Properties of self-compacting concrete mixtures containing metakaolin and blast furnace slag.” Constr. Build. Mater., 25(3), 1325–1331.
Yazıcı, H. (2008). “The effect of silica fume and high-volume Class C fly ash on mechanical properties, chloride penetration and freeze—thaw resistance of self-compacting concrete.” Constr. Build. Mater., 22(4), 456–462.
Yildirim, H., Ilica, T., and Sengul, O. (2011). “Effect of cement type on the resistance of concrete against chloride penetration.” Constr. Build. Mater., 25(3), 1282–1288.
Information & Authors
Information
Published In
Copyright
© 2013 American Society of Civil Engineers.
History
Received: Nov 3, 2011
Accepted: Jun 18, 2012
Published online: Aug 25, 2012
Published in print: May 1, 2013
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.