Investigation of the Cause of Disintegration of Alkali-Activated Slag at Temperature Exposure of 50°C
Publication: Journal of Materials in Civil Engineering
Volume 23, Issue 12
Abstract
Tests reported in this paper show that alkali-activated slag paste (AASP) can totally disintegrate when exposed to oven drying at 40–50°C with circulating air. This phenomenon has not been previously reported in the literature. Further tests eliminated two possible reasons for the disintegration: (1) carbonation of calcium-silicate-hydrate (C-S-H) gel leading to loss of strength and (2) differential shrinkage and cracking leading to disintegration of the samples. Thermal gravimetric analysis (TGA) confirmed that maximum mass loss of about 18% occurred at approximately 40°C. It is postulated that the mass loss is attributed to the loss of chemically-bound water resulting from the disintegration of C-S-H gel and strength loss. This conclusion is arrived in this paper by the process of elimination. Disintegration of AASP at this relatively low temperature is a serious issue and warrants further research on exact cause and possible remedies.
Get full access to this article
View all available purchase options and get full access to this article.
References
Alarcon-Ruiz, L., Platret, G., Massieu, E., and Ehrlacher, A. (2005). “The use of thermal analysis in assessing the effect of temperature on a cement paste.” Cem. Concr. Res., 35(3), 609–613.
Bakharev, T. (2001). “Alkali activated slag concrete: chemistry, microstructure and durability.” Ph.D. dissertation, Dept. of Civil Engineering, Monash Univ., Melbourne, Australia.
Bakharev, T., Sanjayan, J. G., and Cheng, Y. B. (1999). “Alkali activation of Australian slag cements.” Cem. Concr. Res., 29(1), 113–120.
Bakharev, T., Sanjayan, J. G., and Cheng, Y. B. (2001a). “Resistance of alkali-activated slag concrete to alkali-aggregate reaction.” Cem. Concr. Res., 31(2), 331–334.
Bakharev, T., Sanjayan, J. G., and Cheng, Y. B. (2001b). “Resistance of alkali-activated slag concrete to carbonation.” Cem. Concr. Res., 31(9), 1277.
Bin, X., and Xincheng, P. (1999). Study on the durability of solid alkaline AAS cement. 2nd Int. Conf. on Alkaline Cements and Concretes, Kiev, Ukraine, 64–71.
Bissonnette, B., et al. (1999). “Influence of key parameters on drying shrinkage of cementitious materials.” Cem. Concr. Res., 29(10), 1655–1662.
Chen, W., and Brouwers, H. J. H. (2007). “The hydration of slag, part 1: Reaction models for alkali-activated slag.” J. Mater. Sci., 42(2), 428.
Collins, F. G., and Sanjayan, J. G. (1998). “Early age strength and workability of slag pastes activated by NaOH and .” Cem. Concr. Res., 28(5), 655–664.
Collins, F. G. (1999). “High early strength concrete using alkali activated slag.” Ph.D. dissertation, Dept. of Civil Engineering, Monash Univ., Melbourne, Australia.
Collins, F. G., and Sanjayan, J. G. (1999). “Workability and mechanical properties of alkali activated slag concrete.” Cem. Concr. Res., 29(3), 455–458.
Collins, F. G., and Sanjayan, J. G. (2000a). “Effect of pore size distribution on drying shrinkage of alkali-activated slag concrete.” Cem. Concr. Res., 30(9), 1401–1406.
Collins, F. G., and Sanjayan, J. G. (2000b). “Cracking tendency of alkali-activated slag concrete subjected to restrained shrinkage.” Cem. Concr. Res., 30(5), 791–798.
Collins, F. G., and Sanjayan, J. G. (2001). “Early age strength and workability of slag pastes activated by sodium silicates.” Mag. Concr. Res., 53(5), 321–326.
Deja, J. (2002). “Carbonation aspects of alkali activated slag mortars and concretes.” Sil. Ind., 67(3–4), 37–42.
Gallé, C. (2001). “Effect of drying on cement-based materials pore structure as identified by mercury intrusion porosimetry: A comparative study between oven, vacuum, and freeze-drying.” Cem. Concr. Res., 31(10), 1467–1477.
Greenspan, L. (1977). “Humidity fixed points of binary saturated aqueous solutions.” J. Res. Natl. Bur. Stand., Sect. A, 81A(1), 89–96.
Gruskovnjak, A., Lothenbach, B., Holzer, L., Figi, R., and Winnefeld, F. (2006). “Hydration of alkali-activated slag: comparison with ordinary Portland cement.” Adv. Cem. Res., 18(3), 119–128.
Guerrieri, M., Sanjayan, J. G., and Collins, F. G. (2008). “Residual compressive behavior of alkali-activated concrete exposed to elevated temperatures.” Fire Mater., 33(1), 51–62.
Jumppanen, U. M., Diederichs, U., and Hinrichsmeyer, K. (1986). “Material properties of -concrete at high temperatures.” Research Rep. 452, Technical Research Centre of Finland, 60.
Keey, R. B. (2000). Kiln-drying of lumber, Springer-Verlag, Berlin.
Khoury, G. A. (1992). “Compressive strength of concrete at high temperatures: A reassessment.” Mag. Concr. Res., 44(161), 291–309.
Kutti, T. (1992). “Hydration products of alkali activated slag.” 9th Int. Congress on the Chemistry of Cement India, Vol. 4, New Delhi, 468–474.
Lu, T., and Chen, C. (2007). “Uncertainty evaluation of humidity sensors calibrated by saturated salt solutions.” Measurement, 40(6), 591–599.
Mejía de Gutierrez, R., Maldonado, J., and Gutiérrez, C. (2004). “Performance of alkaline activated slag at high temperatures.” Mater. Constr., 54(276), 87–94.
Mendes, A., Sanjayan, J. G., and Collins, F. G. (2008). “Phase transformations and mechanical strength of OPC/slag pastes submitted to high temperatures.” Mater. Struct., 41(2), 345–350.
Palacios, M., and Puertas, F. (2006). “Effect of carbonation on alkali-activated slag paste.” J. Am. Ceram. Soc., 89(10), 3211–3221.
Palomo, A., Grutzeck, M. W., and Blanco, M. T. (1999). “Alkali-activated fly ashes: A cement for the future.” Cem. Concr. Res., 29(8), 1323–1329.
Pan, Z., Cheng, L., Lu, Y., and Yang, N. (2002). “Hydration products of alkali-activated slag-red mud cementitious material.” Cem. Concr. Res., 32(3), 357.
Phan, L. T. (1996). “Fire performance of high-strength concrete: A report of the state of-the-art.” Report Number: NISTIR 5934, Building and Fire Research Laboratory, National Institute of Standards and Technology, Gaithersburg, MD.
Puertas, F., Palacios, M., and Vazquez, T. (2006). “Carbonation process of alkali-activated slag mortars.” J. Mater. Sci., 41(10), 3071–3082.
Purdon, A. O. (1940). “The action of alkalis on blast-furnace slag.” J. Soc. Chem. Ind., London, 59(12), 191–202.
Rovnanikova, P., and Bayer, P. (2006). Concrete structures for traffic network, Proc., 2nd Central European Congress on Concrete Engineering, Hradec Kralove, Czech Republic.
Rovnanikova, P., Bayer, P., Rovnanik, P., and Novak, J. (2005). Cement combinations for durable concrete, Proc., Int. Conf., Dundee, UK.
Russell, D., Basheer, P. A. M., Rankin, G. I. B., and Long, A. E. (2001). “Effect of relative humidity and air permeability on prediction of the rate of carbonation of concrete.” Proc. Inst. Civ. Eng. Struct. Build., 146(3), 319–326.
Shi, C., Krivenko, P., and Roy, D. (2006). Alkali-Activated Cements and Concretes, Taylor & Francis, London.
Talling, B., and Brandstetr, J. (1989). Proc., 3rd International Conf. on Fly Ash, Slag, and Natural Pozzolans in Concrete, ACI SP, 114(2), 1519.
Yousuf, M., Mollah, A., Hess, T. R., Tsai, Y.-N., and Cocke, D. L. (1993). “An FTIR and XPS investigations of the effects of carbonation on the solidification/stabilization of cement based systems-Portland type V with zinc.” Cem. Concr. Res., 23(4), 773–784.
Zuda, L., Pavlik, Z., Rovnanikova, P., Bayer, P., and Cerny, R. (2006). “Properties of alkali activated aluminosilicate material after thermal load.” Int. J. Thermophys., 27(4), 1250–1263.
Zuda, L., Rovnanik, P., Bayer, P., and Cerny, R. (2007). “Thermal properties of alkali-activated slag subjected to high temperatures.” J. Build. Phys., 30(4), 337–350.
Information & Authors
Information
Published In
Journal of Materials in Civil Engineering
Volume 23 • Issue 12 • December 2011
Pages: 1589 - 1595
Copyright
© 2011 American Society of Civil Engineers.
History
Received: Jan 26, 2010
Accepted: Mar 24, 2011
Published online: Mar 26, 2011
Published in print: Dec 1, 2011
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.