High-Strength Geopolymer Using Fine High-Calcium Fly Ash
Publication: Journal of Materials in Civil Engineering
Volume 23, Issue 3
Abstract
In this paper, the synthesis of high-strength geopolymer using fine high-calcium fly ash was studied. The effect of fineness of fly ash on the setting time of geopolymer paste, workability, strength development, and drying shrinkage of geopolymer mortars made from classified fine high-calcium fly ash was investigated. Air-classified fly ash with three different finenesses—coarse original fly ash (CFA), medium-fineness fly ash (MFA), and fine fly ash (FFA)—from the Mae Moh Power Station was used for this study. The heat-cured geopolymers were activated with sodium hydroxide (NaOH) and sodium silicate. A small amount of water was incorporated for workability. The results indicate that the setting time of paste decreases with an increase in fly-ash fineness. The flow, strength, and drying-shrinkage characteristics of mortars were improved using fine fly ash. Geopolymer mortars with high 28-day compressive strength of 86.0 MPa were obtained.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The writers would like to acknowledge the financial support from the Thailand Research Fund through the Royal Golden Jubilee Ph.D. Program (Grant No. UNSPECIFIEDPHD/0074/2548) and the Faculty of Engineering, Khon Kaen University.
References
ASTM. (2007). “Standard test method for flow of hydraulic cement mortar.” C1437-07, Philadelphia.
ASTM. (2008a). “Standard test method for compressive strength of hydraulic cement mortars (using 2-in. or [50 mm] cube specimens).” C109/C109M-08, Philadelphia.
ASTM. (2008b). “Standard test method for time of setting of hydraulic cement by Vicat needle.” C191-08, Philadelphia.
ASTM. (2009a). “Standard test method for density of hydraulic cement.” C188-09, Philadelphia.
ASTM. (2009b). “Standard test method for drying shrinkage of mortar containing hydraulic cement.” C596-09, Philadelphia.
Bakharev, T. (2005a). “Geopolymeric materials prepared using Class F fly ash and elevated temperature curing.” Cem. Concr. Res., 35(6), 1224–1232.
Bakharev, T. (2005b). “Resistance of geopolymer materials to acid attack.” Cem. Concr. Res., 35(4), 658–670.
Chindaprasirt, P., Chareerat, T., and Sirivivananon, V. (2007a). “Workability and strength of coarse high calcium fly ash geopolymer.” Cem. Concr. Compos., 29(3), 224–229.
Chindaprasirt, P., Homwuttiwong, S., and Sirivivatnanon, V. (2004). “Influence of fly ash fineness on strength, drying shrinkage and sulfate resistance of blended cement mortar.” Cem. Concr. Res., 34(7), 1087–1092.
Chindaprasirt, P., Jaturapitakkul, C., Challe, W., and Rattanasak, U. (2009). “Comparative study on the characteristics of fly ash and bottom ash geopolymers.” Waste Manage. (Amsterdam, Neth.), 29(2), 539–543.
Chindaprasirt, P., Jaturapitakkul, C., and Sinsiri, T. (2007b). “Effect of fly ash fineness on microstructure of blended cement paste,” Constr. Build. Mater., 21(7), 1534–1541.
Chindaprasirt, P., and Rattanasak, U. (2010). “Utilization of blended fluidized bed combustion (FBC) ash and pulverized coal combustion (PCC) fly ash in geopolymer.” Waste Manage. (Amsterdam, Neth.), 30(4), 667–672.
Chindaprasirt, P., Ruangsiriyakul, S., Cao, T., and Bucea, L. (2001). “Influence of Mae Moh fly ash fineness on characteristics, strength and drying shrinkage development of blended cement mortars.” Proc., 8th East Asia-Pacific Conf. on Structural Engineering and Construction, EASEC, Singapore.
Davidovits, J. (1999). “Chemistry of geopolymeric systems, terminology.” Proc., 2nd Int. Conf., Geopolymere, J. Davidovits, R. Davidovits, and C. James, eds., Geopolymer Institute, Saint-Quentin, France, 9–40.
Davidovits, J. (2008). Geopolymer chemistry and applications, 2nd Ed., Geopolymer Institute, Saint-Quentin, France.
De Silva, P., Sagoe-Crenstil, K., and Sirivivatnanon, V. (2007). “Kinetics of geopolymerization: Role of and .” Cem. Concr. Res., 37(4), 512–518.
Detphan, S., and Chindaprasirt, P. (2009). “Preparation of fly ash and rice husk ash geopolymer.” Int. J. Miner., Metall. Mater., 16(6), 720–726.
Diaz, E., Allouche, E., and Eklund, S. (2010). “Factors affecting the suitability of fly ash as source materials for geopolymers.” Fuel, 89(5), 992–996.
Duxson, P., Fernandez-Jimenez, A., Provis, J., Lukey, G., Palomo, A., and van Deventer, J. (2007). “Geopolymer technology: The current state of the art.” J. Mater. Sci., 42(9), 2917–2933.
Duxson, P., and Provis, J. L. (2008). “Design precursors for geopolymer cements,” J. Am. Ceram. Soc., 91(12), 3864–3869.
Erdogdu, K., and Turker, P. (1998). “Effects of fly ash particle size on strength of portland cement fly ash mortars.” Cem. Concr. Res., 28(9), 1217–1222.
Fernandez-Jimenez, A., Palomo, A., and Criado, M. (2005). “Microstructure development of alkali-activated fly ash cement: A descriptive model.” Cem. Concr. Res., 35(6), 1204–1209.
Fernandez-Jimenez, A., Palomo, A., and Lopez-Hombrados, C. (2006). “Engineering properties of alkali-activated fly ash concrete.” ACI Mater. J., 103(2), 106–112.
Guo, X., Shi, H., and Dick, W. (2010), “Compressive strength and microstructural characteristics of Class C fly ash geopolymer.” Cem. Concr. Compos., 32(2), 142–147.
Hardjito, D., Cheak, C. C., and Ing, C. H. L. (2008). “Strength and setting times of low calcium fly ash based geopolymer mortar,” Mod. Appl. Sci., 2(4), 3–11.
Hardjito, D., Wallah, S. E., Sumajouw, D. M. J., and Rangan, B. V. (2004a). “Brief review of development of geopolymer concrete.” Proc., George Hoff Symp., American Concrete Institute, Las Vegas.
Hardjito, D., Wallah, S. E., Sumajouw, D. M. J., and Rangan, B. V. (2004b). “On the development of fly ash–based geopolymer concrete.” ACI Mater. J., 101(6), 467–472.
Hou, Y., Wnag, D., Zhou, W., Lu, H., and Wang, L. (2009). “Effect of activator and curing mode on fly ash-based geopolymers.” J. Wuhan Univ. Technol., Mater. Sci. Ed., 24(5), 711–715.
Khale, D., and Chaudhary, R. (2007). “Mechanism of geopolymerization and factors influencing its development: A review.” J. Mater. Sci., 42(3), 729–746.
Kiattikomol, K., Jaturapitakkul, C., Songpiriyakij, S., and Chutubtim, S. (2001). “A study of ground coarse fly ashes with different finenesses from various sources as pozzolanic materials.” Cem. Concr. Compos., 23(4–5), 335–343.
Komljenovic, M., Bascarevic, Z., and Bradic, V. (2010), “Mechanical and microstructural properties of alkali-activated fly ash geopolymers.” J. Hazard. Mater., 181(1–3), 35–42.
Komnitsas, K., and Zaharaki, D. (2007). “Geopolymerisation: A review and prospects for the minerals industry.” Miner. Eng., 20(14), 1261–1277.
Kovalchuk, G., Fernández-Jiménez, A., and Palomo, A. (2007). “Alkali-activated fly ash: Effect of thermal curing conditions on mechanical and microstructural development—Part II.” Fuel, 86(3), 315–322.
Kumar, S., Kumar, R., Alex, T. C., Bandopadhyay, A., and Mehotra, S. P. (2007). “Influence of reactivity of fly ash on geopolymerisation.” Adv. Appl. Ceram., 106(3), 120–127.
Malhotra, V. M. (2002). “Introduction: Sustainable development and concrete technology.” Concr. Int., 24(7), 22.
Nicholson, C., et al. (2005). “Building innovation through geopolymer technology.” Chem. N. Z., 69(3), 10–12.
Rattanasak, U., and Chindaprasirt, P. (2009). “Influence of NaOH solution on the synthesis of fly ash geopolymer.” Miner. Eng., 22(12), 1073–1078.
Roy, D. M., Arjunan, P., and Silsbee, M. R. (2001). “Effect of silica fume, metakaolin, and low-calcium fly ash on chemical resistance of concrete.” Cem. Concr. Res., 31(12), 1809–1813.
Sathonsaowaphak, A., Chindaprasirt, P., and Pimraksa, K. (2009). “Workability and strength of lignite bottom ash geopolymer mortar.” J. Hazard. Mater., 168(1), 44–50.
Skavara, F., Jilek, T., and Kopecky, L. (2005). “Geopolymer materials based on fly ash.” Ceram.-Silik., 49(3), 195–204.
Swanepoel, J. C., and Strydom, C. A. (2002). “Utilisation of fly ash in a geopolymeric material.” Appl. Geochem., 17(8), 1143–1148.
Temuujin, J., and van Riessen, A. (2009). “Effect of mechanical activation of fly ash on the properties of geopolymer cured at ambient temperature.” J. Mater. Process. Technol., 209(12–13), 5276–5280.
Temuujin, J., van Riessen, A., and Williams, R. (2009), “Influence of calcium compounds on the mechanical properties of fly ash geopolymer pastes.” J. Hazard. Mater., 167(1–3), 82–88.
Van Jaarsveld, J. G. S., Van Deventer, J. S. J., and Lukey, G. C. (2002). “The effect of composition and temperature on the properties of fly ash and kaolinite-based geopolymer.” Chem. Eng. J. (London), 89(1–3), 63–73.
Wallah, S., Hardjito, D., Sumajouw, D., and Rangan, B. (2004). “Geopolymer concrete: A better key for better long-term performance and durability.” Proc., ICFRC Int. Conf. on Fibre Composites, High Performance Concretes and Smart Materials, Chennai, India.
Winnefeld, F., Leemann, A., Lucuk, M., Svoboda, P., and Neuroth, M. (2010). “Assessment of phase formation in alkali activated low and high calcium fly ashes in building materials.” Constr. Build. Mater., 24(6), 1086–1093.
Information & Authors
Information
Published In
Copyright
© 2011 American Society of Civil Engineers.
History
Received: Feb 10, 2010
Accepted: Aug 3, 2010
Published online: Aug 5, 2010
Published in print: Mar 1, 2011
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.