Reliability-Based Service Life Prediction of Corrosion-Affected Metal Pipes with Mixed Mode Fracture
Publication: Journal of Engineering Mechanics
Volume 144, Issue 2
Abstract
This paper presents a time-dependent reliability method for the assessment of corrosion-affected metal pipe failures. Two nonlinear limit state functions are proposed for brittle and ductile pipes with mixed mode fracture. For brittle materials, a general failure criterion taking into account all three fracture modes is adopted, whereas for ductile materials, the criterion of stress intensity factor is used, based on a newly developed model of elastic fracture toughness. Stochastic models of corresponding load effects are developed and an upcrossing method is used to quantify the probability of failure and predict the remaining service life. A case study is presented to illustrate the proposed method, followed by a sensitivity analysis to investigate the effects of key variables on the probability of pipe failure. The use of Mode I fracture toughness rather than mixed-mode fracture toughness of the pipe is found to underestimate the probability of its failure. The corrosion and internal pressure have the most influence on the probability of failure for both brittle and ductile pipes, whereas pipe internal radius has the least effect. The method presented in this paper can assist pipe engineers and asset managers in developing a risk-informed and cost-effective strategy for better management of corrosion-affected metal pipelines.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
Financial support from Australian Research Council under DP140101547, LP150100413, and DP170102211 is gratefully acknowledged.
References
Ahammed, M., and Melchers, R. E. (1994). “Reliability of underground pipelines subject to corrosion.” J. Transp. Eng., 989–1002.
Ahammed, M., and Melchers, R. E. (1997). “Probabilistic analysis of underground pipelines subject to combined stresses and corrosion.” Eng. Struct., 19(12), 988–994.
Aliha, M. R. M., and Ayatollahi, M. R. (2007). “A fracture mechanics approach for analysing spiral weld pipes containing crack.” 1st Iranian Pipe and Pipeline Conf., Tehran, Iran.
Ayatollahi, M. R., and Khoramishad, H. (2010). “Stress intensity factors for an axially oriented internal crack embedded in a buried pipe.” Int. J. Press. Vessels Pip., 87(4), 165–169.
BSI (British Standards Institution). (2013). “Guide to methods for assessing the acceptability of flaws in metallic structures.” BS7910, London.
Camarinopoulos, L., Chatzoulis, A., Frontistou-Yannas, S., and Kallidromitis, V. (1999). “Assessment of the time-dependent structural reliability of buried water mains.” Reliab. Eng. Syst. Saf., 65(1), 41–53.
Chang, J., Xu, J.-Q., and Mutoh, Y. (2006). “A general mixed-mode brittle fracture criterion for cracked materials.” Eng. Fract. Mech., 73(9), 1249–1263.
De Silva, D., Moglia, M., Davis, P., and Burn, S. (2006). “Condition assessment to estimate failure rates in buried metallic pipelines.” J. Water Supply Res. Technol. AQUA, 55(3), 179–191.
Erdogan, F., and Sih, G. C., (1963). “On the crack extension in plates under plane loading and transverse shear.” J. Basic Eng., 85(4), 519–525.
Fu, G. Y., Yang, W., and Li, C. Q. (2017). “Elastic fracture toughness for ductile metal pipes with mixed mode fracture induced by inclined cracks.” Int. J. Press. Vessels Pip., in press.
Griggs, J., Gamboa, E., and Lavigne, O. (2015). “A review of modelling high pH stress corrosion cracking of high pressure gas pipelines.” Mater. Corros., 67(3), 251–263.
Ji, J., Robert, D. J., Zhang, C., Zhang, D., and Kodikara, J. (2017). “Probabilistic physical modelling of corroded cast iron pipes for lifetime prediction.” Struct. Saf., 64, 62–75.
Kucera, E., and Mattsson, E. (1987). “Atmospheric corrosion.” Corrosion mechanisms, F. Mansfeld, ed., Marcel Dekker, New York.
Li, C. Q., Fu, G. Y., and Yang, W. (2016). “Stress intensity factors for inclined external surface cracks in pressurised pipes.” Eng. Fract. Mech., 165, 72–86.
Li, C. Q., Lawanwisut, W., and Zheng, J. J. (2005). “Time-dependent reliability method to assess the serviceability of corrosion-affected concrete structures.” J. Struct. Eng., 1674–1680.
Li, C. Q., and Mahmoodian, M. (2013). “Risk based service life prediction of underground cast iron pipes subjected to corrosion.” Reliab. Eng. Syst. Saf., 119, 102–108.
Li, C. Q., and Melchers, R. E. (1993). “Outcrossings from convex polyhedrons for nonstationary Gaussian processes.” J. Eng. Mech., 2354–2361.
Mahmoodian, M., and Li, C. Q. (2016a). “Serviceability assessment and sensitivity analysis of cast iron water pipes under time dependent deterioration using stochastic approaches.” J. Water Supply Res. Technol. AQUA, 65(7), 530–540.
Mahmoodian, M., and Li, C. Q. (2016b). “Structural integrity of corrosion-affected cast iron water pipes using a reliability-based stochastic analysis method.” Struct. Infrastruct. Eng., 12(10), 1356–1363.
Makar, J. M. (2000). “A preliminary analysis of failures in grey cast iron water pipes.” Eng. Fail. Anal., 7(1), 43–53.
Marshall, P. (2001). The residual structural properties of cast iron pipes-structural and design criteria for linings for water mains, U.K. Water Industry Research, London.
Melchers, R. E. (1999). Structural reliability analysis and prediction, Wiley, Brisbane, Australia.
Moore, G. (2010). “Corrosion challenges—Urban water industry.” A report on the impact of failure of infrastructure assets through corrosion as a result of current practices and skilling in the Australian mainland urban water and Naval defence sectors, Australasian Corrosion Association, VIC, Australia.
National Water Commission Australia. (2009). “National performance rep. 2009–10.” Canberra, Australia.
Nowak, A. S., and Collins, K. R. (2012). Reliability of structures, CRC Press, New York.
Nuismer, R. J. (1975). “An energy release rate criterion for mixed mode fracture.” Int. J. Fract., 11(2), 245–250.
Papoulis, A., and Pillai, S. U. (2002). Probability, random variables and stochastic processes, McGraw-Hill Europe, New York.
Petersen, R. B., and Melchers, R. E. (2012). “Long-term corrosion of cast iron cement lined pipes.” Annual Conf. of the Australasian Corrosion Association 2012, Australasian Corrosion Association, VIC, Australia.
Predan, J., Močilnik, V., and Gubeljak, N. (2013). “Stress intensity factors for circumferential semi-elliptical surface cracks in a hollow cylinder subjected to pure torsion.” Eng. Fract. Mech., 105, 152–168.
Raghavachary, S., Rosenfield, A. R., and Hirth, J. P. (1990). “Mixed mode I/III fracture toughness of an experimental rotor steel.” Metall. Trans. A, 21(9), 2539–2545.
Rajani, B., et al. (2000). Investigation of grey cast iron water mains to develop a methodology for estimating service life, American Water Works Association Research Foundation, Denver.
Rice, S. O. (1944). “Mathematical analysis of random noise.” Bell Syst. Tech. J., 23(3), 282–332.
Rossum, J. R. (1969). “Prediction of pitting rates in ferrous metals from soil parameters.” J. Am. Water Works Assoc., 61(6), 305–310.
Sadiq, R., Rajani, B., and Kleiner, Y. (2004). “Probabilistic risk analysis of corrosion associated failures in cast iron water mains.” Reliab. Eng. Syst. Saf., 86(1), 1–10.
Shahani, A. R., and Habibi, S. E. (2007). “Stress intensity factors in a hollow cylinder containing a circumferential semi-elliptical crack subjected to combined loading.” Int. J. Fatigue, 29(1), 128–140.
Sheikh, A. K., Boah, J. K., and Hansen, D. A. (1990). “Statistical modeling of pitting corrosion and pipeline reliability.” Corrosion, 46(3), 190–197.
Sih, G. C., (1973). “Energy-density concept in fracture mechanics.” Eng. Fract. Mech., 5(4), 1037–1040.
Thoft-Christensen, P., and Sorensen, J. D. (1987). “Optimal strategy for inspection and repair of structural systems.” Civ. Eng. Syst., 4(2), 94–100.
Yamini, H., and Lence, B. J. (2010). “Probability of failure analysis due to internal corrosion in cast-iron pipes.” J. Infrastruct. Syst., 16(1), 73–80.
Information & Authors
Information
Published In
Copyright
©2017 American Society of Civil Engineers.
History
Received: Nov 13, 2016
Accepted: Aug 3, 2017
Published online: Dec 7, 2017
Published in print: Feb 1, 2018
Discussion open until: May 7, 2018
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.