Prediction of Concrete Crack Width under Combined Reinforcement Corrosion and Applied Load
Publication: Journal of Engineering Mechanics
Volume 137, Issue 11
Abstract
As a global problem for reinforced concrete structures located in a chloride and/or carbon dioxide–laden environment, reinforcing steel corrosion in concrete costs approximately $100 billion per annum worldwide for maintenance and repairs. The continual demands for greater load for infrastructure exacerbate the problem. This paper attempts to examine the whole process of longitudinal cracking in concrete structures under the combined effect of reinforcement corrosion and applied load. A model for residual stiffness of cracked concrete is derived using the concept of fracture energy. It is found that the corrosion rate is the most important single factor that affects both the time-to-surface cracking and crack width growth. The paper concludes that the developed model is one of very few theoretical models that can predict with reasonable accuracy the crack width on the surface of reinforced concrete structures under such a combined effect. The developed model can be used as a tool to assess the serviceability of corrosion-affected concrete infrastructure. Timely repairs have the potential to prolong the service life of reinforced concrete structures.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
Financial support from the Royal Academy of Engineering, UK, with GRA UNSPECIFIED10177/93, the Engineering and Physical Sciences Research Council (EPSRC), UK, with EPSRC-GBEP/I032150/1 and the Univ. of Greenwich Scholarship for the second writer is gratefully acknowledged.
References
American Concrete Institute (ACI) Committee 365. (2002). “Service life prediction—state-of-the-art report.” ACI365.1R-00, American Concrete Institute, Farmington Hills, MI, 44.
Alonso, C., Andrade, C., Rodriguez, J., and Diez, J. M. (1998). “Factors controlling cracking of concrete affected by reinforcement corrosion.” Mater. Struct., 31(8), 435–441.
Andrade, C., Molina, F. J., and Alonso, C. (1993). “Cover cracking as a function of rebar corrosion: part I—experiment test.” Mater. Struct., 26, 453–464.
Bažant, Z. P. (1979). “Physical model for steel corrosion in concrete sea structures—theory.” J. Struct. Div., ASCE, 105(ST6), 1137–1153.
Bažant, Z. P., and Jirasek, M. (2002). “Nonlocal integral formulations of plasticity and damage: survey and progress.” J. Eng. Mech., 128(11), 1119–1149.
Bažant, Z. P., and Planas, J. (1998). Fracture and size effect in concrete and other quasibrittle materials, CRC, 640.
Bhargava, K., Ghosh, A. K., Mori, Y., and Ramanujam, S. (2006). “Model for cover cracking due to rebar corrosion in RC structures.” Eng. Struct., 28, 1093–1109.
Broomfield, J. (1997). Corrosion of steel in concrete: understanding, investigating and repair, E&FN Spon, London, 264.
Chen, Z. J. (2004). “Effect of reinforcement corrosion on the serviceability of reinforced concrete structures.” M.Sc. thesis, Dept. of Civil Engineering, Univ. of Dundee, UK, 168.
Chen, D., and Mahadevan, S. (2007). “Chloride-induced reinforcement corrosion and concrete cracking simulation.” Cem. Concr. Compos., 30, 227–238.
Colotti, V., and Spadea, G. (2004). “An analytical model for crack control in reinforced concrete elements under combined forces.” Cem. Concr. Compos., 27(4), 503–514.
Coronelli, D. (2002). “Corrosion cracking and bond strength modeling for corroded bars in reinforced concrete.” ACI Struct. J., 99(3), 267–276.
Dagher, H. J., and Kulendran, S. (1992). “Finite element modeling of corrosion damage in concrete structures.” ACI Struct. J., 89(6), 699–708.
El Maaddawy, T., and Soudki, K. (2007). “A model for prediction of time from corrosion initiation to corrosion cracking.” Cem. Concr. Compos., 29(3), 168–175.
Fenner, R. T. (1989). Mechanics of solids, Blackwell Scientific, Oxford, 648.
Gopalaratnam, V. S., and Shah, S. P. (1985). “Softening response of plain concrete in direct tension.” J. Am. Concr. Inst., 62(3), 310–323.
Goto, Y. (1971). “Cracks formed in concrete around deformed tension bars.” J. Am. Concr. Inst., 68(4), 244–251.
James, G. (1993). Advanced modern engineering mathematics, Addison-Wesley, Wokingham, UK, 901.
Lekhnitskii, S. G. (1963). Theory of elasticity of an anisotropic elastic body, Holden-Day, San Francisco, 404.
Li, C. Q. 2003. “Life cycle modeling of corrosion-affected concrete structures—propagation.” J. Struct. Eng., 129(6), 753–761.
Liu, Y., and Weyers, R. E. (1998). “Modeling the time-to-corrosion cracking in chloride contaminated reinforced concrete structures.” ACI Mater. J., 95(6), 675–681.
Molina, F. J., Alonso, C., and Andrade, C. (1993). “Cover cracking as a function of rebar corrosion: part 2—numerical model.” Mater. Struct., 26, 532–548.
Otsuki, N., Miyazato, S., Diola, N. B., and Suzuki, H. (2000). “Influences of bending crack and water-cement ratio on chloride-induced corrosion of main reinforcing bars and stirrups.” ACI Mater. J., 97(4), 454–465.
Pantazopoulou, S. J., and Papoulia, K. D. (2001). “Modeling cover-cracking due to reinforcement corrosion in RC structures.” J. Eng. Mech., 127(4), 342–351.
Schiessl, P. (1988). “Corrosion of steel in concrete.” Report of the TC60-CSC RILEM, Chapman and Hall, London, 204.
Shah, S. P., Swartz, S. E., and Ouyang, C. S. (1995). Fracture mechanics of concrete: applications of fracture mechanics to concrete, rock and other quasi-brittle materials, Wiley-IEEE, 552.
Sheng, J. M., Wang, Z. Z., and Jiang, J. J. (1991). Finite element methods for reinforced concrete and limit analysis of plates and shells, Tsinghua Univ., Beijing, 510.
Tepfers, R. (1979). “Cracking of concrete cover along anchored deformed reinforcing bars.” Mag. Concr. Res., 31(106), 3–12.
Thoft-Christensen, P. (2001). “Corrosion crack based assessment of the life-cycle reliability of concrete structures.” Structural safety and reliability (CD-ROM), R. B. Corotis, G. I. Schueller, and M. Shinozuka, eds., A. A. Balkema, Lisse, Netherlands, 290.
Timoshenko, S. P., and Goodier, J. N. (1970). Theory of Elasticity, McGraw-Hill, New York, 400.
Ueda, T., Sato, Y., Kakuta, Y., and Kameya, H. (1998). “Analytical study on concrete cover cracking due to reinforcement corrosion.” Proc., 2nd Int. Conf. on Concrete Under Severe Conditions, CONSEC’98, Tromsø, Norway, 678–687.
Vu, K. A. T., and Stewart, M. G. (2002). “Spatial variability of structural deterioration and service life prediction of reinforced concrete bridges.” Proc., Int. Conf. on Bridge Maintenance, Safety and Management (CD-ROM), IABMAS, Barcelona.
Xu, G., Wei, J., Zhang, K., and Zhou, X. (2007). “A calculation model for corrosion cracking in RC structures.” J. China Univ. Geosci., 18(18), 85–89.
Yuzer, N., Akoz, F., and Kabay, N. (2007). “Prediction of time to crack initiation in reinforced concrete exposed to chloride.” Constr. Build. Mater., 22, 1100–1107.
Information & Authors
Information
Published In
Copyright
© 2011 American Society of Civil Engineers.
History
Received: Oct 16, 2008
Accepted: Jun 22, 2011
Published online: Jun 24, 2011
Published in print: Nov 1, 2011
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.