Anaerobic Biodegradation of Polyhydroxybutyrate in Municipal Sewage Sludge
Publication: Journal of Environmental Engineering
Volume 136, Issue 7
Abstract
Anaerobic biodegradation in sewage sludge of polyhydroxybutyrate (PHB) was investigated. Evolved gaseous carbon was measured to assess biodegradability according to ASTM D5210. Mass-loss experiments were performed to determine degradation kinetics. Changes in the polymer properties were investigated. The impact of a natural plasticizer [tributyl citrate (TBC)] on biodegradation was determined. Polylactic acid was also biodegraded for comparison. Melt-pressed plates of PHB (with thicknesses of 0.24, 0.5, 1.2, 3.5, and 5.0 mm) were biodegraded to investigate the relationship between initial mass:initial surface area ratios and decay rates. Scanning electron microscopy micrographs of degraded specimens were recorded for visual illustration of the degradation process. A relationship between initial mass:initial surface area and degradation rates indicates that the thickness and surface area of the material affect its degradation. The degradation rates were impacted by the sewage sludge activity. TBC additive hindered PHB’s rate of degradation. Thermal properties, molecular bonding, and molecular weight measured by differential scanning calorimetry, Fourier transform infrared, and size exclusion chromatography, respectively, were only slightly affected by biodegradation, indicating that recycling PHB will not affect its performance.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This work was made possible by The Consortium for Plant Biotechnology Research, Inc. (Agreement No. GO12026-224) and Metabolix, Inc. The writers wish to thank Cindy Henk for her help with the SEM photographs, Dr. Rafael Cueto for the molecular weight analysis, and Wanda LeBlanc for the WAXD analysis. Also, Ms. Rongman Cai worked on the initial analysis of the samples.
References
Abou-Zeid, D. M., Muller, R. J., and Deckwer, W. D. (2001). “Degradation of natural and synthetic polyesters under anaerobic conditions.” J. Biotechnol., 86(2), 113–126.
Abou-Zeid, D. -M., Müller, R. -J., and Deckwer, W. -D. (2004). “Biodegradation of aliphatic homopolyesters and aliphatic-aromatic copolyesters by anaerobic microorganisms.” Biomacromolecules, 5, 1687–1697.
An, Y., Dong, L., Mo, Z., Liu, T., and Feng, Z. (1998). “Non-isothermal crystallization kinetics of poly(β-hydroxybutyrate).” J. Polym. Sci., Part B: Polym. Phys., 36, 1305–1312.
ASTM International. (2000a). “Standard terminology relating to plastics.” ASTM D883-00, West Conshohocken, Pa.
ASTM International. (2000b). ”Standard test method for determining the anaerobic biodegradation of plastic materials in the presence of municipal sewage sludge.” ASTM D5210-92, West Conshohocken, Pa.
ASTM International. (2003). “Standard test method for transition temperatures and enthalpies of fusion and crystallization of polymers by differential scanning calorimetry.” ASTM D3418-03, West Conshohocken, Pa.
ASTM International. (2004). “Standard specification for compostable plastics.” ASTM D6400-04, West Conshohocken, Pa.
Barham, P. J., Keller, A., Otun, E. L., and Holmes, P. A. (1984). “Crystallization and morphology of a bacterial thermoplastic: Poly-3-hydroxybutyrate.” J. Mater. Sci., 19, 2781–2794.
Bonartseva, G. A., et al. (2003). “Aerobic and anaerobic microbial degradation of poly-β-hydroxybutyrate produced by Azotobacter chroococcum.” Appl. Biochem. Biotechnol., 109, 285–301.
Brandl, H., Bachofen, R., Mayer, J., and Wintermantel, E. (1995). “Degradation and applications of polyhydroxyalkanoates.” Can. J. Microbiol., 41, 143–153.
Brandl, H., and Püchner, P. (1992). “Biodegradation of plastic bottles made from ‘biopol’ in an aquatic ecosystem under in situ conditions.” Biodegradation, 2, 237–243.
Briese, B. H., Schmidt, B., and Jendrossek, D. (1994). “Pseudomonas lemoigne has five poly(hydroxyalkanoic acid) (PHA) depolymerase genes: A comparative study of bacterial and eukaryotic PHA depolymerases.” J. Environ. Polym. Degrad., 2, 75–87.
Budwill, K., Fedorak, P. M., and Page, W. J. (1992). “Methanogenic degradation of poly(3-hydroxyalkanoates).” Appl. Environ. Microbiol., 58, 1398–1401.
Chen, C., Cheung, M. K., and Yu, P. H. F. (2005). “Crystallization kinetics and melting behaviour of microbial poly(3-hydroxybutyrate-co-3-hydroxyhexanoate).” Polym. Int., 54, 1055–1064.
Day, M., Shaw, K., and Cooney, D. (1994). “Biodegradability: An assessment of commercial polymers according to the Canadian method for anaerobic conditions.” J. Environ. Polym. Degrad., 2, 121–127.
Degli-Innocenti, F., Tosin, M., and Bastioli, C. (1998). “Evaluation of the degradation of starch and cellulose under controlled composting conditions.” J. Environ. Polym. Degrad., 6(4), 197–202.
Doi, Y., Kanewasa, Y., and Kunioka, M. (1990). “Biodegradation of microbial copolyesters poly(3-hydroxybutyrate-co-3-hydroxybutyrate) and poly(3-hydroxybutyrate-co-4-hydroxybutyrate).” Macromolecules, 23, 26–31.
Freier, T., et al. (2002). “In vitro and in vivo degradation studies for development of a biodegradable patch based on poly(3–hydroxybutyrate).” Biomaterials, 23, 2649–2657.
Fritz, J., Link, U., and Braun, R. (2001). “Environmental impacts of biobased/biodegradable packaging.” Starch, 53, 105–109.
Gartiser, S., Wallrabenstein, M., and Stiene, G. (1998). “Assessment of several test methods for the determination of the anaerobic biodegradability of polymers.” J. Polym. Environ., 3, 159–173.
Gomez-Martinez, D., Partal, P., Martinez, I., and Gallegos, C. (2009). “Rheological behavior and physical properties of controlled-release gluten-based bioplastics.” Bioresour. Technol., 100, 1828–1832.
Imam, S. H., Chen, L., Gordon, S. H., Shogren, R. L., Weisleder, D., and Greene, R. V. (1998). “Biodegradation of injection molded starch-poly(3-hydroxybutyrate-co-3-hydroxyvalerate) blends in a natural compost environment.” J. Environ. Polym. Degrad., 6, 91–98.
Imam, S. H., Gordon, S. H., Shogren, R. L., and Greene, R. V. (1995). “Biodegradation of starch-poly( -hydroxybutyrate-co-valerate) composites in municipal activated sludge.” J. Polym. Environ., 3, 205–213.
Jendrossek, D., and Handrick, R. (2002). “Microbial degradation of polyhydroxyalkanoates.” Annu. Rev. Microbiol., 56, 403–432.
Kunioka, M., Ninomiya, F., and Funabashi, M. (2006). “Biodegradation of poly(lactic acid) powders proposed as the reference test materials for the international standard of biodegradation evaluation methods.” Polym. Degrad. Stab., 91, 1919–1928.
Labrecque, L. V., Kumar, R. A., Dave, V., Gross, R. A., and McCarthy, S. P. (1997). “Citrate esters as plasticizers for poly(lactic acid).” J. Appl. Polym. Sci., 66, 1507–1513.
Li, Z., Lin, H., Ishii, N., Chen, G. Q., and Inoue, Y. (2007). “Study of enzymatic degradation of microbial copolyesters consisting of 3-hydroxybutyrate and medium-chain-length 3-hydroxyalkanoates.” Polym. Degrad. Stab., 92, 1708–1714.
Luzier, W. D. (1992). “Materials derived from biomass/biodegradable materials.” Proc. Natl. Acad. Sci. U.S.A., 89, 839–842.
Mergaert, J., Anderson, C., Wouters, A., and Swings, J. (1994). “Microbial degradation of poly(3-hydroxybutyrate) and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) in compost.” J. Environ. Polym. Degrad., 2, 177–183.
Mezzanotte, V., Bertani, R., Degli-Innocenti, F., and Tosin, M. (2005). “Influence of inocula on the results of biodegradation tests.” Polym. Degrad. Stab., 87, 51–56.
Puechner, P., Mueller, W. -R., and Bardtke, D. (1995). “Assessing the biodegradation potential of polymers in screening and long-term test systems.” J. Environ. Polym. Degrad., 3, 133–143.
Reischwitz, A., Stoppok, E., and Klaus, B. (1998). “Anaerobic degradation of poly-3-hydroxybutyrate and poly-3-hydroxybutyrate-co-3-hydroxyvalerate.” Biodegradation, 8, 313–319.
Rutkowska, M. et al. (2008). “Environmental degradation of atactic poly[ -3-hydroxybutyrate] with natural PHBV in Baltic Seawater compost with activated sludge.” J. Polym. Environ., 16, 183–191.
Shin, P. K., Kim, M. H., and Kim, J. M. (1997). “Biodegradability of degradable plastics exposed to anaerobic digested sludge and simulated landfill conditions.” J. Environ. Polym. Degrad., 5, 33–39.
Sobkowicz, M. J., Feaver, J. L., and Dorgan, J. R. (2008). “Clean and green bioplastic composites: Comparison of calcium sulfate and carbon nanospheres in polylactide composites.” Clean, 36(8), 706–713.
Tercjak, A., Haponiuk, J. T., and Masiulanis, B. (2003). “Study of thermal property changes of biopol/polyamide 11 blends during biodegradation in compost.” J. Therm Anal. Calorim., 74, 605–608.
Waltz, E. (2008). “Do biomaterials really mean business?” Nat. Biotechnol., 26(8), 851–853.
Wang, Y.- S., Byrd, C. S., and Barlaz, M. A. (1994). “Anaerobic biodegradability of cellulose and hemicellulose in excavated refuse samples using a biochemical methane potential assay.” J. Ind. Microbiol., 13, 147–153.
Williams, S. F., and Peoples, O. P. (1996). “Biodegradable plastics from plants.” CHEMTECH, 26(9), 38–44.
Woolnough, C. A., Charlton, T., Yee, L. H., Sarris, M., and Foster, L. J. R. (2008). “Surface changes in polyhydroxyalkanoate films during biodegradation and biofouling.” Polym. Int., 57, 1042–1051.
Yu, J., and Chen, L. X. L. (2008). “The greenhouse gas emissions and fossil energy requirement of bioplastics from cradle to gate of a biomass refinery.” Environ. Sci. Technol., 42, 6961–6966.
Information & Authors
Information
Published In
Copyright
© 2010 ASCE.
History
Received: Jun 4, 2009
Accepted: Dec 2, 2009
Published online: Dec 4, 2009
Published in print: Jul 2010
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.