Proposed Method to Reduce Magnesium Chloride Deicer Damage to Pervious Concrete
Publication: Journal of Cold Regions Engineering
Volume 35, Issue 3
Abstract
This technical note tests the efficacy of a carbonate-laden water treatment on pervious concrete to increase its resistance to magnesium chloride (MgCl2) attack. A treatment method and an example of the method application are described. The method consists of applying MgCl2 deicer onto pervious concrete specimens for 17 weeks, but some specimens are treated prior to the deicer applications and some are not. All specimens are then subjected to compressive strength tests and to optical microscopy, for visual analysis of the interfacial transition zone. In the example given, the time frames between casting and treating or applying deicer varied, and although inconclusive, results indicated that the treatment might be more effective if more curing is allowed prior to treatment.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The authors thank Dr. Nicholas Brake, Dr. Saeid Hosseini, Natalie Lopez, Jarod Jantz, and Lamar University.
References
ACI (American Concrete Institute). 2010. Report on pervious concrete 522R-10. ACI Committee 522. Farmington Hills, MI: ACI.
ASTM. 2012. Standard test method for density and void content of hardened pervious concrete. ASTM C1754/C1754M-12. West Conshohocken, PA: ASTM.
ASTM. 2018. Standard test method for compressive strength of cylindrical concrete specimens. ASTM C39/C39M-18. West Conshohocken, PA: ASTM.
Chen, Y., K. Wang, X. Wang, and W. Zhou. 2013. “Strength, fracture and fatigue of pervious concrete.” Constr. Build. Mater. 42: 97–104. https://doi.org/10.1016/j.conbuildmat.2013.01.006.
Haselbach, L. 2017. Evaluation of the effects of deicer chemical methodologies on pervious concrete & development of a deicer chemical testing method for pervious concrete. Silver Spring, MD: Ready Mixed Concrete Research & Education Foundation.
Haselbach, L. M., and J. N. Thomle. 2014. “An alternative mechanism for accelerated carbon sequestration in concrete.” Sustainable Cities Soc. 12: 25–30. https://doi.org/10.1016/j.scs.2014.01.001.
ISO. 2016. Testing methods for pervious concrete—Part 1: Infiltration rate. ISO 17785-1 2016. Geneva: ISO.
Meininger, R. C. 1988. “No-Fines pervious concrete for paving.” Concr. Int. 10 (8): 20–27.
Neithalath, N. 2004. “Development and characterization of acoustically efficient cementitious materials.” Ph.D. thesis, Dept. of Civil Engineering, Purdue Univ.
Ross, M., L. Haselbach, T. Sendele, and N. Almeida. 2018. “Magnesium chloride deicer chemical effects on pervious concrete.” Environ. Eng. Sci. 35 (11): 1165–1172. https://doi.org/10.1089/ees.2018.0144.
Stumm, W., and J. Morgan. 1996. Aquatic chemistry. New York: John Wiley & Sons.
Thomle, J., and L. Haselbach. 2011. “The declining pH of waters exfiltrated through pervious concrete.” Spec. Publ. Am. Concr. Inst. 282: 1–12.
Information & Authors
Information
Published In
Copyright
© 2021 American Society of Civil Engineers.
History
Received: Dec 3, 2019
Accepted: Mar 25, 2021
Published online: May 26, 2021
Published in print: Sep 1, 2021
Discussion open until: Oct 26, 2021
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.