Evaluation of Influence Factors on Crack Initiation of LTPP Resurfaced-Asphalt Pavements Using Parametric Survival Analysis
Publication: Journal of Performance of Constructed Facilities
Volume 28, Issue 2
Abstract
Survival model with Weibull hazard function was used to evaluate the influence of different factors on the crack initiation of resurfaced asphalt pavement. Data from Specific Pavement Study 5 experiments of the Long Term Pavement Performance (LTPP) program were used to conduct the analysis. The initiation time of four types of cracks including alligator (fatigue) crack, longitudinal crack on wheel path, non–wheel path longitudinal crack, and transverse crack was evaluated. Analyzed factors include overlay thickness, total pavement thickness, pretreatment pavement serviceability, traffic volume, freeze index, mixture [whether reclaimed asphalt pavement (RAP) is used], and whether milling is performed before overlay. It was found that traffic level was a significant factor for all four types of cracks. High traffic level accelerated the initiation of cracking. Thick overlay delayed the initiation of cracking except for the non–wheel path longitudinal crack, which is mainly caused by poor construction. Total pavement thickness only retarded the initiation of wheel path longitudinal cracking. Incorporating 30% RAP in the overlay accelerated the initiation of early-age fatigue cracking; however, it was not a significant cause for severe fatigue cracking. Severe freeze-thaw conditions accelerated the occurrence of non–wheel path longitudinal and transverse cracks; milling before overlay significantly retarded the occurrence of the two types of cracks.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The funding of this study was supported by the Tennessee DOT (TDOT) and the Federal Highway Administration (FHWA). This study used the data released by LTPP, which is funded and managed by the FHWA. The LTPP engineers are acknowledged for their assistance on data inquiry. The contents of this paper reflect the views of the authors, who are responsible for the facts and the accuracy of the data presented herein, and do not necessarily reflect the official views or policies of the TDOT or FHWA, nor do the contents constitute a standard, specification, or regulation.
References
Daleiden, F., Simpson, A., and Rauhut, J. B. (1998). “Rehabilitation performance trends: early observations from long-term pavement performance (LTPP) specific pavement studies (SPS).” Rep. FHWA-RD-97-099, Federal Highway Administration, U.S. DOT, McLean, VA.
Elkins, G. E., Schmalzer, P., Thompson, T., Simpson, A., and Ostrom, B. (2008) “Long-term pavement performance information management system pavement performance database user reference guide.” Report FHWA-RD-03-088, Federal Highway Administration, U.S. DOT, McLean, VA.
Eltahan, A. A., Daleiden, J. F., and Simpson, A. L. (1999). “Effectiveness of maintenance treatments of flexible pavements.” Transportation Research Record 1680, Transportation Research Board, Washington, DC, 18–25.
Hall, K. T., Correa, C. E., and Simpson, A. L. (2003). “Performance of flexible pavement rehabilitation treatments in the long-term pavement performance SPS-5 experiment.” Transportation Research Record 1823, Transportation Research Board, Washington, DC, 93–101.
Hanna, N., Tayabji, S. D., and Miller, J. S. (1994). SHRP-LTPP specific pavement studies: five-year report, Strategic Highway Research Program, National Research Council, Washington, DC.
Hong, F., Chen, D., and Mikhail, M. M. (2010). “Long-term performance evaluation of recycled asphalt pavement results from Texas.” Transportation Research Record 2180, Transportation Research Board, Washington, DC, 58–66.
Hong, F., Rosales-Herrera, V. I., and Prozzi, J. A. (2008). “Development of asphalt pavement transverse crack initiation models based on LTPP data.” Proc., Transportation Research Board 87th Annual Meeting, Transportation Research Board, Washington, DC.
Huang, Y. (1993). Pavement analysis and design, Prentice Hall, Englewood Cliffs, NJ, 113.
iENGINEERING Inc. (2011). “LTPP products online.” 〈http://www.ltpp-products.com/〉 (Aug. 1, 2010).
Loizos, A., and Karlaftis, M. G. (2005). “Prediction of pavement cracking initiation from in-service pavements.” Transportation Research Record 1940, Transportation Research Board, Washington, DC, 38–42.
LTPP [database]. (2010). Long-term pavement performance standard data release 24.0. Federal Highway Administration, U.S. DOT, McLean, VA.
McDaniel, R., and Nantung, T. (2009). “Designing Superpave mixes with locally reclaimed asphalt pavement: North central states jointly fund study.” Transportation Research News, Transportation Research Board, Washington, DC, 239, 28–30.
Miller, J. S., and Bellinger, W. Y. (2003). “Distress identification manual for the LTPP project.” Rep. FHWA-RD-03-031, Federal Highway Administration, U.S. DOT, McLean, VA.
Newcomb, D., Brown, E., and Epps, J. (2007). “Designing HMA mixtures with high RAP content: a practical guide.” Quality Improvement Series 124, National Asphalt Pavement Association, Lanham, MD.
Paterson, W. D. O., and Chester, A. D. (1986). “On predicting pavement surface distress with empirical models of failure times.” Transportation Research Record 1095, Transportation Research Board, Washington, DC, 45–56.
Pavia Systems, Inc. (2009). “Pavement interactive.” 〈http://www.pavementinteractive.org〉 (Aug. 1, 2010).
Prozzi, J. A., and Madanat, S. (2000). “Using duration models to analyze experimental pavement failure data.” Transportation Research Record 1699, Transportation Research Board, Washington, DC, 87–94.
Rauhut, J. B., Von Quintus, H. L., and Eltahan, A. (2000). “Performance of rehabilitated asphalt concrete pavements in LTPP experiments (data collected through February 1997).” Rep. FHWA-RD-00-029, Federal Highway Administration, U.S. DOT, McLean, VA.
SAS Institute. (2008). JMP statistics and graphics guide, release 8, SAS Institute Inc., Cary, NC.
Shin, H. C., and Madanat, S. (2003). “Development of a stochastic model of pavement distress initiation.” Proc. JSCE 744, 61–67.
Von Quintus, H. L., Simpson, A. L., and Eltahan, A. A. (2006). “Rehabilitation of asphalt concrete pavements: Initial evaluation of the SPS-5 experiment-final report.” Rep. No. FHWA-RD-01-168, Federal Highway Administration, U.S. DOT, McLean, VA.
Wang, Y., Mahboub, K., and Hancher, D. (2005). “Survival analysis of fatigue cracking for flexible pavements based on long-term pavement performance data.” J. Transp. Eng., 608–616.
Winfrey, R. (1969). Economic analysis for highways, International Textbook, Scranton, PA.
Information & Authors
Information
Published In
Copyright
© 2014 American Society of Civil Engineers.
History
Received: Nov 4, 2011
Accepted: Sep 26, 2012
Published online: Sep 28, 2012
Published in print: Apr 1, 2014
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.