Investigation of Corrosion Damage and Repair System in a Concrete Jetty Structure
Publication: Journal of Performance of Constructed Facilities
Volume 24, Issue 4
Abstract
This paper presents the diagnostic investigation of a reinforced concrete jetty after 15 years of service. The main cause of the deterioration was reinforcement corrosion, which initiated within few years after the completion of the jetty structure. The structure underwent major corrosion rehabilitation after 7 years of service. Despite the use of high-strength concrete in the construction of the jetty structure, inadequate cover thickness for reinforced concrete elements intensified corrosion rate and caused early age corrosion problems to reappear. Other contributing factors included high salinity of the seawater by simultaneous action of climatic factors such as exposure to high relative humidity and air temperature. After the initial repair work, a new investigative procedure was carried out to reevaluate the repaired and surrounding unrepaired areas. Results indicate that the deterioration progressed even in concrete elements that were undamaged during the first step of the investigation. No sign of steel corrosion appeared on repaired areas; but shrinkage cracking and incipient corrosion around repaired areas were indications of dimensional and electrochemical incompatibility between repair concrete and substrate. The repair strategy was reevaluated through the repair index method proposed by Andrade and Izquierdo. The results showed that the patching repair method was more suitable and feasible in comparison with other techniques.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The writers would like to acknowledge “Persian Mining and Metal Industries Special Zones (P.G.S.E.Z)” Company for financial support and “Construction Materials Institute (CMI)” at the University of Tehran for technical support.
References
Aïtcin, P. C. (1998). “High-performance concrete.” Modern concrete technology series, E & FN Spon, London.
Al-Bahar, S., Attiogbe, E. M., and Kamal, H. (1998). “Investigation of corrosion damage in reinforced concrete structure in Kuwait.” ACI Mater. J., 95(3), 226–231.
Al-Khaiat, H., and Haque, M. N. (1997). “Carbonation of some coastal concrete structures in Kuwait.” ACI Mater. J., 94(6), 602–607.
Alonso, C., Andrade, C., Castellote, M., and Castro, P. (2000). “Chloride threshold values to depassivate reinforcing bars embedded in a standardized OPC mortar.” Cem. Concr. Res., 30(7), 1047–1055.
American Concrete Institute (ACI) Committee. (2005a). “Building code requirements for structural concrete (ACI 318-05) and commentary (318R-05).” ACI 318, Farmington Hills, Mich.
American Concrete Institute (ACI) Committee. (2005b). “Code requirements for environmental engineering concrete structures (ACI 350-01) and commentary (ACI 350R-01).” ACI 350, Farmington Hills, Mich.
Andrade, C., and Izquierdo, D. (2005). “Benchmarking through an algorithm of repair methods of reinforcement corrosion: The repair index method.” Cem. Concr. Compos., 27(6), 727–733.
Ann, K. Y., and Song, H. (2007). “Chloride threshold level for corrosion of steel in concrete.” Corros. Sci., 49(11), 4113–4133.
Bertolini, L., Gastaldi, M., Pedeferri, M., and Redaelli, E. (2002). “Prevention of steel corrosion in concrete exposed to seawater with submerged sacrificial anodes.” Corros. Sci., 44(7), 1497–1513.
British Standard Institution. (1997). “Structural use of concrete—Code of practice for design and construction.” BS 8110-1, London.
Brown, M. D., Smith, C. A., Sellers, J. G., Folliard, K. J., and Breen, J. E. (2007). “Use of alternative materials to reduce shrinkage cracking in bridge decks.” ACI Mater. J., 104(6), 629–637.
Building and Housing Research Center. (2005). “National code of practice for concrete durability in the Persian Gulf and Omman Sea (in Farsi).” BHRC-PN-S428, Ministry of Housing and Urban Development, Tehran, Iran.
Castro, P., Moreno, E. I., and Genescá, J. (2000a). “Influence of marine micro-climate on carbonation of reinforced concrete buildings.” Cem. Concr. Res., 30(10), 1565–1571.
Castro, P., Sanjuán, M. A., and Genescá, J. (2000b). “Carbonation of concretes in the Mexican Gulf.” Build. Environment, 35(2), 145–149.
“Climatic statistics.” (2008). I. R. of Iran Meteorological Organization (Monthly and Annual), ⟨http://www.irimo.ir/english/statistics/index.asp⟩ (Feb. 2008).
Construction Materials Institute (CMI). (2007). “Diagnostic assessment of corrosion damage of Charlie 1&2 Jetty Structure in Bandar Abbas Port with aim of designing a repair method (in Farsi).” CMI8708304, Univ. of Tehran, Iran.
Costa, A., and Appleton, J. (2002). “Case studies of concrete deterioration in a marine environment in Portugal.” Cem. Concr. Compos., 24(1), 169–179.
Cusson, D., Qian, S., and Hoogeveen, T. (2006). “Field performance of concrete repair systems on highway bridge.” ACI Mater. J., 103(5), 366–373.
Elsener, B. (2001). “Half-cell potential mapping to assess repair work on RC structures.” Constr. Build. Mater., 15(2–3), 133–139.
Emmons, E. H., Vaysburd, A. M., and McDonald, J. E. (1993). “A rational approach to durable concrete repairs.” Concr Inrern, 15(9), 40–45.
Fookes, P. G., Simm, J. D., and Barr, J. M. (1986). “Marine concrete performance in different climatic environments.” Proc., Int. Conf. on Concrete in the Marine Environment, The Concrete Society, London.
Golam Ali, M. (1993). “Cathodic protection current accelerates the alkali-silica reaction.” ACI Mater. J., 90(3), 247–252.
Guettala, A., and Abibsi, A. (2006). “Corrosion degradation and repair of a concrete bridge.” Mater. Struct., 39(4), 471–478.
Marseguerra, M., and Zio, E. (2000). “Optimizing maintenance and repair policies via a combination of genetic algorithms and Monte Carlo simulation.” Reliab. Eng. Syst. Saf., 68(1), 69–83.
Momayez, A., Ehsani, M. R., Rajaie, H., and Ramezanianpour, A. (2005). “Cylindrical specimen for measuring shrinkage in repaired concrete members.” Constr. Build. Mater., 19(2), 107–116.
Novokshchenov, V. (1995). “Deterioration of reinforced concrete in the marine industrial environment of the Gulf-A case study.” Mater. Struct., 28(7), 392–400.
Pargar, F., Layssi, H., and Shekarchi, M. (2007). “Investigation of chloride threshold value in an old concrete structure.” Proc., 5th Int. Conf. on Concrete under Severe Conditions: Environment and Loading (CONSEC’07) Tours, Laboratoire central des ponts et chaussées (LCPC), France.
Raupach, M. (2006). “Patch repairs on reinforced concrete structures—Model investigations on the required size and practical consequences.” Cem. Concr. Compos., 28(8), 679–684.
Shekarchi, M., Moradi-Marani, F., and Pargar, F. (2009). “Corrosion damage of a reinforced concrete jetty structure in the Persian Gulf: A case study.” Struct. Infrastruct. Eng., in press.
Vaysburd, A. M., and Emmons, P. H. (2000). “How to make today’s repairs durable for tomorrow—Corrosion protection in concrete repair.” Constr. Build. Mater., 14(4), 189–197.
Zhang, J., and Lounis, Z. (2006). “Sensitivity analysis of simplified diffusion-based corrosion initiation model of concrete structures exposed to chlorides.” Cem. Concr. Res., 36(7), 1312–1323.
Information & Authors
Information
Published In
Copyright
© 2010 ASCE.
History
Received: Aug 26, 2008
Accepted: Dec 23, 2009
Published online: Dec 29, 2009
Published in print: Aug 2010
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.