Characterization of Emulsion Wax Curing Agent as Bond-Breaker Medium in Jointed Concrete Pavement
Publication: Journal of Performance of Constructed Facilities
Volume 23, Issue 6
Abstract
Bond-breaker media have been used with success to reduce and minimize undesirable cracks reflecting from cement-treated or lean-concrete subbases (LCSs). The common bond-breaking media include (1) emulsion slurry seal; (2) 30 to 60-mm-thin asphalt concrete; (3) one or two applications of wax-based curing compounds; (4) one or two layers of polyethylene sheets; and (5) geotextile. The cost differences among different bond-breaking media are significant for a highway project over 200 km long. Different types of tests (British pendulum friction, push off, pullout, and torsion) were performed to determine the cost-effectiveness of bond-breaking media. It was found that the bond stress had been reduced by approximately 90% when either emulsion wax curing compound (EWCC) or emulsion slurry seal was used. The results from the British pendulum, push-off, pullout, torsion, and cost analyses indicate that EWCC is the most cost-effective bond-breaker medium. Based on the observations from the laboratory testing and field trial section, the EWCC application rate was selected at . As evident from the push-off and torsion test results, the effectiveness of the EWCC as a bond-breaker medium decreased with time. Thus, a second application of EWCC is required if the LCS base has been exposed to the environment for more than 14 days. The 216-km project was successfully constructed with EWCC. It resulted in a more than $7 million savings by using EWCC instead of emulsion slurry seal. No distress or cracking has been observed after the section was opened to traffic for more than 1 year.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
This research is supported by the key project “Study on key technical issues on the project of upgrading the first-rate highway in the mountainous areas,” the section of Guangdong Transportation, the Transportation Department of Guangdong Province [Grant No. UNSPECIFIED(2007)1010].
References
AASHTO. (2005). “Standard specification for liquid membrane-forming compounds for curing concrete.” AASHTO M 148-05, Washington, D.C.
American Concrete Pavement Association (ACPA). (1991). TB011P, Skokie, Ill.
Ao, X., Zhou, Z., and Li, Q. (2004). “Comparison of performance of various interfaces between cement concrete slab and different subbases.” Highways & Automotive Applications (in Chinese), (3), 39–41.
ASTM. (2003a). “Standard test method for liquid membrane-forming compounds for curing concretes.” C309, West Conshohocken, Pa.
ASTM. (2003b). “Standard test method for measuring surface frictional properties using the British pendulum tester.” E303, West Conshohocken, Pa.
ASTM. (2004). “Standard test method for tensile strength of concrete surfaces and the bond strength or tensile strength of concrete repair and overlay materials by direct tension (torsion method).” C1583, West Conshohocken, Pa.
ASTM. (2007). “Standard specification for liquid membrane-forming compounds for curing concrete.” C309, West Conshohocken, Pa.
Chen, D. -H., and Won, M. (2008). “Field performance monitoring of repair treatments on joint concrete pavements.” J. Test. Eval., 36(2), 119–127.
Hall, K., et al. (2007). “Long-life concrete pavements in Europe and Canada.” Rep. No. FHWA-PL-07-027, Federal Highway Administration (FHWA), Washington, D.C.
Heath, A. C., and Roesler, J. R. (1999). “Shrinkage and thermal cracking of fast setting hydraulic cement concrete pavements in Palmdale, California.” ⟨http://www.its.berkeley.edu/pavementresearch/PDF/Shrinkage%20and%20Therm%20Crack.pdf⟩ (May 2008).
Okamoto, P. A., et al. (1994). “Guidelines for timing contraction joint sawing and earliest loading for concrete pavements.” Final Rep. No. FHWA-RD-91-079, Federal Highway Administration (FHWA), Washington, D.C.
Suh, Y. C., Lee, S. W., and Kang, M. S. (2002). “Evaluation of subbase friction for typical Korean concrete pavement.” Transportation Research Record. 1809, Transportation Research Board, Washington, D.C., 66–73, ⟨http://www.pavement.com/Concrete_Pavement/Technical/FATQ/Construction/Cracking.asp⟩ (April 2009).
Tarr, S. M., Okamoto, P. A., Sheehan, M. J., and Packard, R. G. (1999). “Bond interaction between concrete pavement and lean concrete base.” Transportation Research Record. 1668, Transportation Research Board, Washington, D.C., 9–17.
Taylor, P., Kosmatka, S., and Voigt, G. (2007). “Integrated materials and construction practices for concrete pavement: A state-of-the-practice manual.” Rep. No. FHWA HIF-07-004, Federal Highway Administration (FHWA), Washington, D.C.
Voigt, G. V. (2002). “Early cracking of concrete pavement—Causes and repairs.” American Concrete Pavement Association, ⟨http://www.airtech.tc.faa.gov/naptf/att07/2002%20TRACK%20P.pdf/P-68.pdf⟩ (May 2008).
Wesevich, J. W., McCullough, B. F., and Burns, N. H. (1987). “Stabilized subbase friction study for concrete pavements.” Research Rep. No. 459-1, Center for Transportation Research, University of Texas at Austin, Washington, D.C.
Information & Authors
Information
Published In
Copyright
© 2009 ASCE.
History
Received: May 9, 2008
Accepted: Apr 9, 2009
Published online: Apr 22, 2009
Published in print: Dec 2009
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.