Bond Durability of FRP Bars Embedded in Fiber-Reinforced Concrete
Publication: Journal of Composites for Construction
Volume 16, Issue 4
Abstract
A research program was initiated to develop a nonferrous reinforcement system for concrete bridge decks using continuous fiber-reinforced polymer (FRP) bars and discrete, randomly distributed polypropylene fibers. This hybrid system may eliminate problems related to corrosion of steel reinforcement while providing requisite strength, stiffness, and desired ductility, which are shortcomings of the FRP reinforcing system in plain concrete. This paper presents the results of a part of this research program [i.e., the long-term bond behaviors of this FRP/fiber-reinforced concrete (FRC) hybrid system]. Bond durability for the FRP/plain concrete system that served as a reference is also reported. Test results indicated that ultimate and design bond strength experienced noticeable degradation when exposed to combined environmental conditioning, including freeze-thaw cycles, high temperature (60°C), and deicing salt solution. Test results showed that bond durability significantly improved owing to the restriction of the concrete crack by the addition of polypropylene fibers. The larger specimens with thicker concrete cover and relatively smaller direct exposed area to the solution of sodium chloride (NaCl) showed better bond durability. Comparing glass FRP specimens with carbon FRP specimens, it was found that bond degradation was tightly correlated to the degradation of FRP bars.
Get full access to this article
View all available purchase options and get full access to this article.
References
American Concrete Institute (ACI). (2006). “Guide for the design and construction of concrete reinforced with FRP bars.” ACI 440.1R-06, Farmington Hills, MI.
American Concrete Institute (ACI). (2008a). “Guide to durable concrete.” ACI 201.2R-08, Farmington Hills, MI.
American Concrete Institute (ACI). (2008b). “Building code requirements for structural concrete and commentary.” ACI 318-08, Farmington Hills, MI.
Balazs, G. L., and Borosnyoi, A. (2001). “Long-term behavior of FRP.” Proc., Int. Workshop Composites in Construction: A Reality, ASCE, Reston, VA.
Bank, L. C., Gentry, T. R., and Barkatt, A. (1995). “Accelerated test methods to determine the long-term behavior of FRP composite structures: Environmental effects.” J. Reinf. Plast. Compos.JRPCDW, 14(6), 559–587.
Bank, L. C., Puterman, M., and Katz, A. (1998). “The effect of material degradation on bond properties of fiber reinforced plastic reinforcing bars in concrete.” ACI Mater. J.AMAJEF, 95(3), 232–243.
Ceroni, F., Cosenza, E., Gaetano, M., and Pecce, M. (2006). “Durability issues of FRP rebars in reinforced concrete members.” Cem. Concr. Compos.CCOCEG, 28(10), 857–868.
Chen, Y., Davalos, J. F., Ray, I., and Kim, H. Y. (2007). “Accelerated aging tests for evaluations of durability performance of FRP reinforcing bars for concrete structures.” Compos. Struct.COMSE2, 78(1), 101–111.
Davalos, J. F., Chen, Y., and Ray, I. (2008). “Effect of FRP bar degradation on interface bond with high strength concrete.” Cem. Concr. Compos.CCOCEG, 30(8), 722–730.
Ferguson, P. M., Breen, J. E., and Thompson, J. N. (1965). “Pullout tests on high strength reinforcing bars.” J. Am. Concr. Inst.JACIAX, 62(8), 933–950.
Galati, N., Nanni, A., Dharani, L. R., Focacci, F., and Antonietta, M. (2006). “Thermal effects on bond between FRP rebars and concrete.” Composites, Part ACASMFJ, 37(8), 1223–1230.
Gylltoft, K., Cederwall, K., Elfgren, L., and Nilsson, L. (1982). “Bond failure in reinforcement concrete under monotonic and cyclic loading: A fracture mechanics approach.” Fatigue of Concrete Structures, SP-75, American Concrete Institute, Detroit, 269–287.
Katz, A., Berman, N., and Bank, L. C. (1999). “Effect of high temperature on bond strength of FRP.” J. Compos. Constr.JCCOF2, 3(2), 73–81.
Kim, H. Y., Park, Y. H., You, Y. J., and Moon, C. K. (2008). “Short-term durability test for GFRP rods under various environmental conditions.” Compos. Struct.COMSE2, 83(1), 37–47.
Mashima, M., and Iwamoto, K. (1993). “Bond characteristics of FRP rod and concrete after freezing and thawing deterioration.” Fiber-Reinforced-Plastic Reinforcement for Concrete Structures—International Symposium, SP 138, American Concrete Institute, Detroit, 51–70.
Mathey, R. G., and Watstein, D. (1961). “Investigation of bond in beam and pull-out specimens with high-yield-strength deformed bars.” J. Am. Concr. Inst.JACIAX, 57(3), 1071–1090.
Micelli, F., and Nanni, A. (2004). “Durability of FRP rods for concrete structures.” Constr. Build. Mater.CBUMEZ, 18(7), 491–503.
RILEM. (1994). “RC6: Bond test for reinforcing steel. 1. Pull-out test.” RILEM Technical Recommendations for the Testing and Use of Construction Materials, 7-II-128, E & FN Spon, Oxfordshire, UK, 102–105.
Robert, M., and Benmokrane, B. (2010). “Effect of aging on bond of GFRP bars embedded in concrete.” Cem. Concr. Compos.CCOCEG, 32(6), 461–467.
Schutte, C. L. (1994). “Environmental durability of glass-fiber composites.” Mater. Sci. Eng.MSCEAA, 13(7), 265–324.
Sekijima, K., Otsuka, Y., and Konno, T. (1999). “Durability of fiber reinforced polymer reinforcement embedded in concrete.” 4th Int. Symp. on Fiber Reinforced Polymer Reinforced Concrete Structures, SP-188, American Concrete Institute, Farmington Hills, MI, 501–513.
Tannous, F. E., and Saadatmanesh, H. (1998). “Environmental effects on the mechanical properties of E-Glass FRP rebars.” ACI Mater. J.AMAJEF, 95(2), 87–100.
Uomoto, T., and Nishimura, T. (1999). “Deterioration of aramid, glass, and carbon fibers due to alkali, acid, and water in different temperatures.” 4th Int. Symp. on Fiber Reinforced Polymer for Reinforced Concrete Structures, SP-188, American Concrete Institute, Farmington Hills, MI, 515–522.
Wang, H., and Belarbi, A. (2010). “Static and fatigue bond characteristics of FRP rebars embedded in fiber-reinforced concrete.” J. Compos. Mater.JCOMBI, 44(13), 1605–1622.
Wang, H., and Belarbi, A. (2011). “Ductility characteristics of fiber-reinforced-concrete beams reinforced with FRP rebars.” Constr. Build. Mater.CBUMEZ, 25(5), 2391–2401.
Information & Authors
Information
Published In
Copyright
© 2012. American Society of Civil Engineers.
History
Received: Jul 13, 2011
Accepted: Dec 8, 2011
Published online: Dec 10, 2011
Published in print: Aug 1, 2012
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.