Depletion of Antioxidants from a HDPE Geomembrane in a Composite Liner
Publication: Journal of Geotechnical and Geoenvironmental Engineering
Volume 134, Issue 1
Abstract
The results of two series of accelerated aging tests are reported. Both series of tests were conducted at temperatures of 85, 70, 55, and over a period of about . In the simulated liner series, the top of the geomembrane was covered with a geotextile (protection) layer that was exposed to simulated municipal solid waste (MSW) landfill leachate while the bottom of the geomembrane was in contact with a hydrated geosynthetic clay liner. In the immersion series, the geomembrane was immersed in the simulated MSW leachate, and hence, both sides were exposed to leachate. The results from oxidative induction time tests indicate that the antioxidant depletion is about 2.2–4.8 times faster for the leachate immersed geomembrane than for geomembrane in a composite liner. The higher rates are attributed to the higher extraction of antioxidants from two sides of the geomembrane immersed in leachate. The measured antioxidant depletion rates are extrapolated to a range of temperatures using Arrhenius modeling. At a liner temperature of , the calculated time for the depletion of antioxidants is about for a geomembrane in a composite liner compared to if it is simply immersed in leachate. These tests suggest that to obtain realistic estimates of geomembrane service life one needs data from tests that simulate the expected field conditions and that prediction based on immersion tests may underestimate the service life.
Get full access to this article
View all available purchase options and get full access to this article.
Acknowledgments
The research presented in this paper was funded by the Natural Science and Engineering Research Council of Canada (NSERC), Canada Foundation for Innovation (CFI), the Ontario Innovation Trust, the Centre for Research in Earth and Environmental Technologies (an Ontario Center of Excellence), the Ontario Ministry of Environment, and Terrafix Geosynthetics Inc. The writers are grateful to their industrial partners, Solmax International, Terrafix Geosynthetics Inc., Ontario Ministry of Environment, Gartner Lee Ltd., AMEC Earth and Environmental, Golder Associates Ltd., the CTT group, and especially to Terrafix Geosynthetics Inc. (Toronto, Canada) for providing the geosynthetics tested. Support from Dr. Henri P. Sangam in the initial stages of this project is gratefully acknowledged. The value of discussions with Dr. Grace Hsuan are also greatly appreciated.
References
ASTM. (2006a). “Standard test methods for laboratory compaction characteristics of soil using standard effort [ ].” D638-07e1, West Conshohocken, Pa.
ASTM. (2006b). “Standard test method for flow rates of thermoplastics by extrusion plastometer.” D1238-04c, West Conshohocken, Pa.
ASTM. (2006c). “Standard test method for density of plastics by the density gradient method.” D1505-03, West Conshohocken, Pa.
ASTM. (2006d). “Standard test method for carbon black content in olefin plastics.” D1603-06, West Conshohocken, Pa.
ASTM. (2006e). “Standard test method for oxidative-induction time of polyolefins by differential scanning calorimetry.” D3895-07, West Conshohocken, Pa.
ASTM. (2006f). “Standard test methods for water permeability of geotextiles by permittivity.” D4491-99a, West Conshohocken, Pa.
ASTM. (2006g). “Standard test method for grab breaking load and elongation of geotextiles.” D4632-04, West Conshohocken, Pa.
ASTM. (2006h). “Standard test method for determining apparent opening size of a geotextile.” D4751-04, West Conshohocken, Pa.
ASTM. (2006i). “Standard test method for determination of water (moisture) content of soil by direct heating.” D4959-07, West Conshohocken, Pa.
ASTM. (2006j). “Standard test methods for measurement of hydraulic conductivity of saturated porus material using a flexible wall permeameter.” D5080-00, West Conshohocken, Pa.
ASTM. (2006k). “Standard test method for determining apparent opening size of a geotextile.” D5199-06, West Conshohocken, Pa.
ASTM. (2006l). “Standard test method for measuring mass per unit area of geotextiles.” D5261-92/2003, West Conshohocken, Pa.
ASTM. (2006m). “Determining the coefficient of soil and geosynthetic or geosynthetic and geosynthetic friction by the direct shear method.” D5321-02, West Conshohocken, Pa.
ASTM. (2006n). “Standard test method for evaluation of stress crack resistance of polyolefin geomembranes using notched constant tensile load test.” D5397-07, West Conshohocken, Pa.
ASTM. (2006o). “Standard test method for oxidative induction time of polyolefin geosynthetics by high-pressure differential scanning calorimetry.” D5885-06, West Conshohocken, Pa.
ASTM. (2006p). “Standard test method for swell index of clay mineral component of geosynthetic clay liners.” D5890-06, West Conshohocken, Pa.
ASTM. (2006q). “Standard test method for measuring mass per unit area of geosynthetics liners.” D5993-99/2004, West Conshohocken, Pa.
ASTM. (2006r). “Standard test methods for particle-size analysis distribution (gradation) of soils using sieve analysis.” D6913-04e1, West Conshohocken, Pa.
ASTM. (2006s). “Standard test method for determining tensile properties of nonreinforced polyethylene and nonreinforced flexible polypropylene geomembranes.” D6693-04, West Conshohocken, Pa.
ASTM. (2006t). “Standard test method for melting and crystallization temperatures by thermal analysis.” E794-06, West Conshohocken, Pa.
Barroso, M., Touze-Foltz, N., von Maubeuge, K., and Pierson, P. (2006). “Laboratory investigation of flow rate through composite liners consisting of a geomembrane, a GCL and a soil liner.” Geotextiles Geomembranes, 24(3), 139–155.
Cartaud, F., Goblet, P., and Touze-Foltz, N. (2005a). “Numerical simulation of the flow in the interface of a composite bottom liner.” Geotextiles Geomembranes, 23(6), 513–533.
Cartaud, F., Touze-Foltz, N., and Duval, Y. (2005b). “Experimental investigation of the influence of a geotextile beneath the geomembrane in a composite liner on the leakage through a hole in the geomembrane.” Geotextiles Geomembranes, 23(2), 117–143.
Dörner, G., and Lang, R. W. (1998). “Influence of various stabilizer systems on the aging behavior of PE-ME-I. Hot water ageing compression molding plaques.” Polym. Degrad. Stab., 62, 421–430.
Eith, A. W., and Koerner, G. R. (1997). “Assessment of HDPE geomembrane performance in a municipal solid waste landfill double liner system after eight years of service.” Geotextiles Geomembranes, 15, 277–287.
Fay, J. J., and King, R. E. (1994). “Antioxidants for geosynthetic resins and applications.” Geosynthetic resins, formulations, and manufacturing, Y. G. Hsuan and R. M. Koerner, eds., Industrial Fabrics Association International, St. Paul, Minn., 77–96.
Flory, P. J., and Vrij, A. (1963). “Melting points of linear-chain homologs. The normal paraffin hydrocarbons.” J. Am. Chem. Soc., 85, 3548–3553.
Grassie, N., and Scott, G. (1985). Polymer degradation and stabilization, Cambridge University Press, New York.
Gulec, S. B., Edil, T. B., and Benson, C. H. (2004). “Effect of acidic mine drainage on the polymer properties of an HDPE geomembrane.” Geosynthet. Int., 11(2), 60–72.
Hamid, S. H., Maadhah, A. G., and Amin, M. B. (1992). “Weathering degradation of polyethylene.” Handbook of polymer degradation, S. H. Hamid, A. G. Maadhah, and M. B., Amin, eds., Marcel Dekker, New York, 219–259.
Hrapovic, L. (2001). “Laboratory study of intrinsic degradation of organic pollutants in compacted clayey soil.” Ph.D. dissertation, Dept. of Civil and Environmental Engineering, Univ. of Western Ontario, London, Ont., Canada.
Hsuan, Y. G., and Guan, Z. (1997). “Evaluation of the antioxidant behavior of polyethylene geomembranes using oxidative induction time tests.” Oxidative behavior of materials by thermal analytical techniques, ASTM STP1326, A. T. Riga and G. H. Patterson, eds., ASTM, Philadelphia, 76–90.
Hsuan, Y. G., and Koerner, R. M. (1995). “Long term durability of HDPE geomembrane: Part I—Depletion of antioxidant.” GRI Rep. 16, Geosynthetic Research Institute, Drexel Univ., Philadelphia.
Hsuan, Y. G., and Koerner, R. M. (1998). “Antioxidant depletion lifetime in high-density polyethylene geomembranes.” J. Geotech. Geoenviron. Eng., 124(6), 552–541.
Islam, M. Z., and Rowe, R. K. (2007). “Leachate composition and antixoxidant depletion from HDPE geomembranes.” Proc., Geosynthetics 2007 Conf. (CD-ROM), Washington D.C.
Karlsson, K., Smith, G. D., and Gedde, U. W. (1992). “Molecular structure, morphology, and antioxidant consumption in medium density polyethylene pipes in hot-water applications.” Polym. Eng. Sci., 32(10), 649–657.
Koerner, G. R., and Koerner, R. M. (2006). “Long-term temperature monitoring of geomembranes at dry and wet landfills.” Geotextiles Geomembranes, 24(1), 72–77.
Koerner, R. M. (1998). Designing with geosynthetics, 4th Ed., Prentice-Hall, Englewood Cliffs, N.J.
Koerner, R. M., Lord, A. E., and Hsuan, Y. H. (1992). “Arrhenius modeling to predict geosynthetics degradation.” Geotextiles Geomembranes, 11(2), 151–183.
Krushelnitzty, R. P. (2006). “Investigation of physical, temperature, and chemical effects on the short-term and long-term performance of high-density polyethylene pipe.” Ph.D. thesis, Queen’s Univ. Kingston, Ont., Canada.
Lutz, J. T., and Grossman, R. F. (2001). Polymer modifiers and additives, Marcel Dekker, New York.
Müller, W. W. (2007). HDPE geomembranes in geotechnics, Springer, Heidelberg, Germany.
Müller, W., and Jakob, I. (2003). “Oxidative resistance of high-density polyethylene geomembranes.” Polym. Degrad. Stab., 79, 161–172.
Osawa, Z., and Saito, T. (1978). “The effects of transition metal compounds on the thermal oxidative degradation of polypropylene in solution.” Stabilization and degradation of polymers. Advances in chemistry, Series, 169, American Chemical Society, Washington, D.C., 2897–2907.
Peacock, A. (2000). Handbook of plyethylene: Structures, properties, and application, Marcel Dekker, New York.
Rimal, S., Rowe, R. K., and Hansen, S. (2004). “Durability of geomembrane exposed to jet fuel A-1.” Proc., 57th Canadian Geotechnical Conf., Quebec City, 13–19.
Rowe, R. K. (2005). “Long-term performance of contaminant barrier systems.” Geotechnique, 55(9), 631–678.
Rowe, R. K., Quigley, R. M., Brachman, R. W. I., and Booker, J. R. (2004). Barrier systems for waste disposal facilities, 2nd Ed., E & FN Spon, London.
Salman, A., Elias, V., Juran, I., Lu, S., and Pearce, E. (1997). “Durability of geosynthetics based on accelerated laboratory testing.” Proc., Geosynthetics Conf., St. Paul, Minn., 217–234.
Sangam, H. P. (2001). “Performance of HDPE geomembrane liners in landfill applications.” Ph.D. thesis, Dept. of Civil and Environmental Engineering, Univ. of Western Ontario, Ont., Canada.
Sangam, H. P., and Rowe, R. K. (2002). “Effects of exposure conditions on the depletion of antioxidants from high-density polyethylene (HDPE) geomembranes.” Can. Geotech. J., 39, 1221–1230.
Shah, V. (2002). “Characterization and identification of plastics.” Handbook of materials selection, M. Kutz ed., Wiley, New York, 591–614.
Smith, G. D., Karlsson, K., and Gedde, U. W. (1992). “Modeling of antioxidant loss from polyolefins in hot-water applications. I: Model and application to medium density polyethylene pipes.” Polym. Eng. Sci., 32(10), 658–667.
Sung, W., and Nikolov, Z. L. (1992). “Accelerated degradation studies of starch-filled polyethylene films.” Ind. Eng. Chem. Res., 31, 2332–2339.
Thomas, R. W., and Ancelet, C. R. (1993). “The effect of temperature, pressure, and oven aging on the high-pressure oxidative induction time of different types of stabilizers.” Proc., of Geosynthetics Conf., Vancouver, Canada, 915–924.
Tikuisis, T., Lam, P., and Cossar, M. (1993). “High-pressure oxidative induction time analysis by differential scanning calorimetry MOC/MOA and COC/COA of geosynthetics.” GRI Conference Series, R. M. Koerner and Y. G. Hsuan, eds., Industrial Fabrics Association International, St. Paul, Minn., 191–201.
Tisinger, L. G., Peggs, I. D., and Haxo, H. E. (1991). “Chemical compatibility testing of geomembranes.” Geomembranes Identification and Performance Testing. Rilem Report, 4, A. Rollin and J. M. Rigo, eds., Chapman & Hall, New York, 268–307.
Touze-Foltz, N., Duquennoi, C., and Gaget, E. (2006). “Hydraulic and mechanical behavior of GCLs in contact with leachate as part of a composite liner.” Geotextiles Geomembranes, 24(3), 188–197.
Verdu, J. (1988). “Problèmes liés à la prédiction du comportement à long terme des matériaux polymères.” Durability of geotextiles, Rilem, Chapman & Hall, London, 161–185.
Viebke, J., Elble, E., Ifwarson, M., and Gedde, U. W. (1994). “Degradation of unstabilized medium-density polyethylene pipes in hot-water applications.” Polym. Eng. Sci., 34(17), 1354–1361.
Wisse, J. D. M., Broos, C. J. M., and Boels, W. H. (1990). “Evaluation of the life expectancy of polypropylene geotextiles used in bottom protection structures around the Ooster Schelde storm surge barrier: A case study.” Proc., 2nd Int. Conf. on Geotextiles, Vol. 1, Las Vegas, 283–288.
Yim, G., and Godin, M. (1993). “Long-term heat ageing stabilization study of polyethylene and its relationship with oxidative induction time (OIT).” Proc., Geosynthetics Conf., Vancouver, 803–815.
Information & Authors
Information
Published In
Copyright
© 2008 ASCE.
History
Received: Sep 29, 2006
Accepted: Feb 6, 2007
Published online: Jan 1, 2008
Published in print: Jan 2008
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.