Optimum Percentage of Fly Ash Reinforcement in Vinyl Ester Composites
Publication: Journal of Materials in Civil Engineering
Volume 22, Issue 1
Abstract
The previous work of another group of researchers found that the modulus of tension, flexural, and compression increased with increasing percentage by volume of fly ash. They also documented that the viscosity of the composite increased exponentially with increasing percentage by volume of the filler. The viscosity increased sharply when the percentage by volume of reinforcer is between 35 and 50%. They failed to mention the highest percentage by weight of fly ash that could be added to the resin to get the highest mechanical properties while still ensuring that the composite could be cast into molds with ease. This project attempts to find out the optimum percentage by weight of cement hollow spheres (SLG) in vinyl ester resin as far as yield strength, tensile strength, Young’s modulus, and Poisson’s ratio of the composite are taken into account. The research found that 33% by weight of filler is a favorable and convenient percentage by weight of SLG to use because up to this percentage by weight of reinforcement, the mechanical properties like modulus of tension are increasing with the increase in percentage by weight of filler while at the same time the viscosity is not high enough to prevent ease of casting the composite into molds.
Get full access to this article
View all available purchase options and get full access to this article.
References
Astrom, B. T. (1997). Manufacturing of polymer composites, Chapman & Hall, London, 74–83.
Australian Standard. (2001). “Determination of tensile properties of plastic materials—Test conditions for moulding and extrusion plastics.” Australian standard 1145.2.
Calister, W. D. (2003). Material science and engineering: An introduction, 6th Ed., Wiley, New York, 121–122.
Davey, S. W., Heldt, T., Van Erp, G., and Ayers, S. R. (2005). “Vinylester/cenosphere composite materials for civil and structural engineering.” FRP International, 2(3), 2–5.
John, V. B. (1990). Engineering materials, Macmillan, New York, 209.
Kota, V. (2006). “Young’s modulus of vinyl ester composites cured by microwave irradiation.” MS thesis, Univ. of Southern Queensland, Australia.
Ku, H. (2003). “Curing vinyl ester particle reinforced composites using microwaves.” J. Compos. Mater., 37(22), 2027–2042.
Reinforced plastics durability. (1999). G. Pritchard, ed., Woodhead Publishing Ltd., U.K., 282–293.
Information & Authors
Information
Published In
Copyright
© 2010 ASCE.
History
Received: Nov 9, 2006
Accepted: Aug 14, 2009
Published online: Dec 15, 2009
Published in print: Jan 2010
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.