Corrosion of Reinforcement in Relation to Presence of Defects at the Interface between Steel and Concrete
Publication: Journal of Materials in Civil Engineering
Volume 17, Issue 4
Abstract
In this study, steel-concrete interface defects were analyzed in order to define their potential to induce corrosion. Various types of steel-concrete interface defects were classified into two main groups: macrodefects and microdefects. Gaps formed beneath horizontal reinforcement as a result of bleeding and settlement of fresh concrete were analyzed for macrodefects. Microdefects presented no signs that could be identified by visual inspection and resulted not only from controlled pull-out of the steel bar but also from bleeding and settlement (but without the production of macrodefects as found with gap formation). Apart from interface defects, cover concrete porosity was defined as an intrinsic defect. The effect of these defects on reinforcement corrosion was investigated. Macrodefects have a direct effect on corrosion, whereas microdefects have no significant effect on corrosion. Where the level of intrinsic defects was high, these had a greater effect on corrosion than interface macrodefects. The behaviors of conventional and self-compacting concrete (SCC) were compared. SCC was found to have better interface quality.
Get full access to this article
View all available purchase options and get full access to this article.
References
Andrade, C., and Alonso, C. (1996). “Corrosion rate monitoring in the laboratory and on-site.” Constr. Build. Mater., 10(5), 315–328.
Arya, C., and Xu, Y. (1995). “Effect of cement type on chloride binding and corrosion of steel in concrete.” Cem. Concr. Res., 25(4), 893–902.
Cao, H. T., and Sirivivatnanon, V. (1991). “Corrosion of steel in concrete with and without silica fume.” Cem. Concr. Res., 21(2–3), 316–324.
Cao, J., and Chung, D. D. L. (2001). “Degradation of the bond between concrete and steel under cyclic shear loading, monitored by contact electrical measurement.” Cem. Concr. Res., 31, 669–671.
Castel, A., François, R., and Arliguie, G. (2000). “Factors other than chloride level influencing corrosion rate of reinforcement.” Proc., CANMET/ACI Durability of Concrete, V. M. Malhotra, ed., American Concrete Institute, Detroit, 629–644.
Gjorv, O. E., Monteiro, P. J. M., and Mehta, P. K. (1990). “Effect of condensed silica fume on the steel-concrete bond.” ACI Mater. J., 87(6), 573–580.
Glass, G. K., Reddy, B., and Buenfeld, N. R. (2000). “Corrosion inhibition in concrete arising from its acid neutralization capacity.” Corros. Sci., 42, 1587–1598.
Hamad, B. S., and Itani, M. S. (1998). “Bond strength of reinforcement in high-performance concrete: The role of silica fume, casting position, and superplasticizer dosage.” ACI Mater. J., 95(5), 499–511.
Khayat, K. H. (1998a). “Viscosity-enhancing admixtures for cement-based materials—an overview.” Cem. Concr. Compos., 20, 171–188.
Khayat, K. H. (1998b). “Use of viscosity-modifying admixture to reduce top-bar effect of anchored bars cast with fluid concrete.” ACI Mater. J., 95(2), 158–167.
Khayat, K. H. (1999). “Workability, testing, and performance of self-consolidating concrete.” ACI Mater. J., 96, 346–353.
Khayat, K. H., Vachon, M., and Lanctot, M. C. (1997). “Use of blended silica fume in commercial concrete mixtures.” ACI Mater. J., 94(3), 119–131.
Kosmatka, S. H. (1994). “Bleeding, significance of tests, and properties of concrete and concrete making material.” Proc., Special Publication STP 169 C, ASTM, West Conshohocken, Pa., 88–111.
Lambert, P. L., Page, C. L., and Vassie, P. R. W. (1991). “Investigations of reinforcement corrosion. 2: Electrochemical monitoring of steel in chloride-contaminated concrete.” Mater. Struct., 24, 351–358.
Lorentz, T., and French, C. (1995). “Corrosion of reinforcing steel in concrete: Effects of materials, mix composition, and cracking.” ACI Mater. J., 92(2), 181–190.
Millard, S. G., Law, D., Bungey J. H., and Cairns, J. (2001). “Environmental influences on linear polarization corrosion rate in reinforced concrete.” NDT & E Int., 34, 409–417.
Mohammed, T. U., and Hamada, H. (2001). “Discussion of ‘Chloride threshold values to depassivate reinforcing bars embedded in a standardized OPC mortar,’ by C. Alonso, C. Andrade, M. Castellote, and P. Castro.” Cem. Concr. Res., 31, 835–838.
Mohammed, T. U., Otsuki, N., Hamada, H., and Yamaji, T. (2002). “Chloride-induced corrosion of steeel bars in concrete with presence of gap at the steel-concrete interface.” ACI Mater. J., 99(2), 149–156.
Mohammed, T. U., Otsuki, N., and Hisada, M. (1999). “Corrosion of steel bars with respect to orientation in concrete.” ACI Mater. J., 96(2), 154–159.
Nilsson, L. O., Poulsen, E., Sandberg, P., Sørensen, H. E., and Klinghoffer, O. (1996). “Chloride penetration into concrete state of art.” HETEK Rep. No. 53, Danish Road Directorate, Copenhagen, Denmark.
Page, C. L. (1975). “Mechanism of corrosion protection in reinforced concrete marine structures.” Nature (London), 258(11), 514–515.
Page, C. L., Al Khalaf, M. N., and Ritchie, A. G. B. (1978). “Steel/mortar interfaces: Mechanical characteristics and electrocapillarity.” Cem. Concr. Res., 8, 481–490.
Page, C. L., and Treadaway, K. W. J. (1982). “Aspects of the electrochemistry of steel in concrete.” Nature (London), 297, 109–115.
Page, C. L., and Vennesland, Ø. (1983). “Pore solution composition and chloride binding capacity of silica-fume cement pastes.” Mater. Struct., 16(91), 19–25.
Petrov, N. (1998). “Etude des propriétés d’un béton autonivelant in situ et de leurs influences sur l’interface béton-armature.” MS thesis, Université de Sherbrooke, Sherbrooke, Canada.
Suryavanshi, A. K., Scantlebury, J. D., and Lyon, S. B. (1988). “Corrosion of reinforcement steel embedded in high water-cement ration concrete contaminated with chloride.” Cem. Concr. Compos., 20, 263–281.
Yonezawa, T., Ashworth, V., and Procter, R. P. M. (1988). “Pore solution composition and chloride effects on the corrosion of steel in concrete.” Corros. Eng., 44(7), 489–499.
Information & Authors
Information
Published In
Copyright
© 2005 ASCE.
History
Received: Jan 9, 2004
Accepted: Sep 7, 2004
Published online: Aug 1, 2005
Published in print: Aug 2005
Notes
Note. Associate Editor: Jason Weiss
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.