Effects of Crack Width and Permeability on Moisture-Induced Damage of Pavements
Publication: Journal of Materials in Civil Engineering
Volume 16, Issue 3
Abstract
The purpose of this study was to evaluate the pavement distress associated with moisture and cracks. A feedback-controlled test was developed to generate a crack with a controlled width in asphalt concrete specimens. Three different mixtures, i.e., dense graded, stone mastic asphalt (SMA), and porous asphalt (PA), were tested for moisture-induced damage aggravated by cracking and high void contents. An exponential relationship was found to exist between permeability and air voids. The intrusion of water can be greatly reduced when the asphalt mixture is properly compacted to an air void level of 7% or less. As water penetrated into the mixtures, PA and SMA coated by a thicker asphalt film showed more resistance to water damage than the dense mixture by a thinner one. The test results indicated that voids in these three types of mixtures could be categorized as impervious, semieffective, and effective, respectively. The corresponding permeability was found to be or higher, to and or lower, respectively. When cracks became wider than 0.2 cm, the indirect tensile strength of all three mixtures reduced significantly in the presence of water. The effect of cracks on a pavement was similar to an increase in voids in a mixture regarding water damage. A pavement showing 0.2 cm cracking is recommended to have immediate maintenance. The present research may provide insight into establishing criteria for a durable asphalt pavement.
Get full access to this article
View all available purchase options and get full access to this article.
References
Aldea, C., Shah, S. P., and Karr, A.(1999). “Permeability of cracked concrete.” Mater. Struct., 32(3), 370–376.
Asphalt Institute (AI). (1998). Construction of hot mix asphalt pavements, Manual Series No. 22, 2nd Ed., AI, KY.
Brown, E. R., and Cooley, L. A. (1999). “Designing Stone Matrix Asphalt Mixtures for Rut-Resistant Pavements.” National Cooperative Highway Research Program, NCHRP Rep. No. 425, Transportation Research Board, Washington, D.C.
Busching, H. W., Corley, G. C., Burail, J. L., Amirkhanian, S. N., and Alewine, J. M. (1985). “A statewide program to identify and prevent stripping damage.” ASTM STP 899, American Society for Testing and Materials, Philadelphia, 1–21.
Chen, J. S., and Lin, K. Y.(2002). “Evaluation of an accelerated pavement testing facility and development of its load equivalence factors.” J. Test. Eval., 30(2), 103–109.
Choubane, B., Page, G. C., and Mussleman, G. A. (1999). “Investigation of water permeability of coarse graded superpave pavements.” Rep. No. FL/DOT/SMO/97-416, Florida Department of Transportation, Fla.
Cooley, L. A., Brown, E. R., and Maghsoodloo, S. (2001). “Development of critical field permeability and pavement density values for coarse-graded superpave pavements.” NCAT Rep. No. 2001–3, National Center for Asphalt Technology, Auburn Univ. Ala.
Davies, R. M., and Sorenson, J.(2000). “Pavement preservation: Preserving our investment in highways.” Public Roads, 63(2), 63–69.
Hall, K. D., and Williams, S. G. (2000). “Effects of specimen configuration and compaction method on rutting and stripping behavior in asphalt concrete wheel-tracking tests.” Transportation Research Board 79th Annual Meeting (CD-ROM), Transportation Research Board, Washington, D.C.
Huang, B., Mohammad, L. N., Ragavendra, A., and Abadi, C.(1999). “Fundamentals of permeability in asphalt mixtures.” J. Assoc. Asphalt Paving Technol., 68, 479–500.
Japan Association of Pavement Engineering (JAPE). (2001). Guideline for drainage pavements, 2nd Ed., JAPE, Tokyo (in Japanese).
Kandhal, P. S., Lubold, C. W., and Roberts, F. L.(1989). “Water damage to asphalt overlays: Case histories.” J. Assoc. Asphalt Paving Technol., 58, 40–76.
Kennedy, T. W., Roberts, F. L., and Lee, K. W. (1983). “Evaluation of moisture effects on asphalt concrete mixtures.” Transportation Research Record 911, Transportation Research Board, Washington, D.C., 134–143.
Kim, O. K., Bell, C. A., and Hicks, R. G. (1985). “The effect of moisture on the performance of asphalt mixtures.” ASTM STP 899, American Society for Testing and Materials, Philadelphia, 51–72.
Lottman, R. P. (1974). “Laboratory test system for prediction of asphalt concrete moisture damage.” Transportation Research Record 515, Transportation Research Board, Washington, D.C., 18–26.
Lottman, R. P. (1978). “Predicting moisture-induced damage to asphalt concrete.” NCHRP Rep. No. l92, Transportation Research Board, National Research Council, Washington, D.C.
Ministry of Transport and Communication (MOTC). (1998). “Relationship between pavement distress and asphalt cement.” Rep. No. MOTC-STA-89-018, MOTC, Taiwan, Taipei.
Parr, W. K. (1958). “Field observation of the behavior of bituminous pavements as influenced by moisture.” ASTM STP 240, American Society for Testing and Materials, Philadelphia, 3–16.
Plancher, H., Dorrence, S. M., and Peterson, J. C.(1977). “Identification of chemical type in asphalt strongly absorbed at the asphalt-aggregate interface and their relative displacement by water,” J. Assoc. Asphalt Paving Technol., 46, 151–175.
Shatnawi, S. R., and Kirk, J. V. (1993). “Premature asphalt concrete pavement distress caused by moisture-induced damage.” Transportation Research Record 1417, Transportation Research Board, Washington, D.C., 168–177.
Stroup-Gardiner, M., Newcomb, D.E., Crow, B., Kussman, W., and Wegman, D. (1996). “Moisture Sensitivity in Asphalt Concrete Mixtures.” Research Rep. No. 96-04, Minnesota Department of Transportation, Minn.
Stuart, K. D. (1990). “Moisture damage in asphalt mixture-A state of the art report.” Rep. No. FHWA-RD-90-019, Federal Highway Administration, Va.
Taylor, M. A., and Khosla, N. P. (1983). “Stripping of asphalt pavements: State of the art.” Transportation Research Record 911, Transportation Research Board, Washington, D.C., 150–158.
Terrel, R. L., and Al-Swailmi, S. (1994). “Water sensitivity of asphalt–aggregate mixes,” Rep. No. SHRP-A-403, Strategic Highway Research Program, Washington, D.C.
Wang, K., Jansen, D., Shah, S. P., and Karr, A.(1997). “Permeability study of cracked concrete.” Cem. Concr. Res., 27(4), 381–393.
Information & Authors
Information
Published In
Copyright
Copyright © 2004 American Society of Civil Engineers.
History
Received: Jun 6, 2002
Accepted: Jun 17, 2003
Published online: May 14, 2004
Published in print: Jun 2004
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.