Numerical Model for Minimizing Risk of Damage in Repair System
Publication: Journal of Materials in Civil Engineering
Volume 13, Issue 2
Abstract
New cement-based repair overlays are subject to restraint and eigenstresses that can lead to crack formation and delamination. The origin of this complex state of stresses is found in the dimensional instability of the new coating. Drying shrinkage, autogeneous shrinkage, and temperature gradients are the most important loads acting on the system. In most cases the design of such coating systems is carried out in an empirical way. In this paper a new approach based on a numerical model is proposed to determine the relevant key parameters for the design of repair systems. By means of this model time-dependent moisture distributions and crack evolution in a drying concrete repair system can be simulated in a realistic way. Crack formation and delamination is described, with the smeared and discrete crack models, applying nonlinear fracture mechanics. The relevant material parameters influencing shrinkage cracking and delamination are identified by means of a sensitivity analysis. Finally, this approach is applied to analyze in a rational way the repair measures on a concrete bridge. This study primarily aimed to decide which repair material is more suitable with respect to shrinkage-induced damage and consequently which one provides the highest durability for the rehabilitated structure.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Bazant, Z. P. ( 1988). “Material models for structural analysis.” Mathematical modelling of creep and shrinkage of concrete, Z. P. Bazant, ed., Wiley, New York.
2.
Bazant, Z. P., and Oh, B. H. ( 1983). “Crack band theory for fracture of concrete.” Mat. and Struct., Paris, 16, 155–172.
3.
DIANA Users' manual—Release 6.1. (1996). Diana Analysis BV, Delft, The Netherlands.
4.
Emmons, P. H., McDonald, J. E., and Vaysburd, A. M. ( 1993). “Some compatibility problems in repair of concrete structures—A fresh look.” Proc., 3rd Int. Colloquium on Mat. Sci. and Restoration, Vol. 1, Expert Verlag, 836–857.
5.
Hillerborg, A., Modéer, M., and Petersson, P. E. ( 1976). “Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements.” Cement and Concrete Res., 6, 773–782.
6.
Martinola, G. ( 1998). “Entwicklung zuverlässiger zementgebundener Beschichtungen auf Beton, KTI Project (1994–1998).” Internal Rep. IBWK-ETHZ, Swiss Federal Institute of Technology, Zürich, Switzerland (in German).
7.
Martinola, G., and Sadouki, H. ( 1998). “Combined experimental and numerical study to assess shrinkage cracking of cement-based materials.” Int. J. for Restoration of Build. and Monuments, Freiburg, Germany, 4(5), 479–506.
8.
Martinola, G., Sadouki, H., and Wittmann, F. H. ( 1996). “Numerisches Modell zur Beschreibung der Eigenspannungen und der Rissbildung in Beschichtungssystemen.” Proc., 4th Int. Colloquium on Mat. Sci. and Restoration, Vol. 1, Aedificatio Verlag, Freiburg, Germany, 393–407 (in German).
9.
Martinola, G., Sadouki, H., and Wittmann, F. H. ( 1997). “Fissuration et délamination d'une couche de réparation appliquée sur un élément de béton.” Proc., 15th Rencontres Universitaires de Génie Civil: Expérimentation et Calcul, EC. 97, Vol. 2, 267–276 (in French).
10.
Martinola, G., Trausch, J. L., and Sadouki, H. ( 1997). “The ring test for optimizing low shrinkage concrete.” Proc., RILEM-WTA-Seminar on High Perf. of Cement-Based Mat. WTA-Rep. Ser. No. 15, 173–194.
11.
Roelfstra, P. E., and Wittmann, F. H. ( 1986). “Numerical method to link strain softening with failure of concrete.” Fracture toughness and fracture energy of concrete, F. H. Wittmann, ed., Elsevier Science, Amsterdam, 163–175.
12.
Rots, J. G. ( 1988). “Computational modeling of concrete fracture.” PhD thesis, Delft University of Technology, Delft, The Netherlands.
13.
Sadouki, H., and van Mier, J. G. M. ( 1997). “Simulation of hygral crack growth in concrete repair systems.” Mat. and Struct., Paris, 30, 518–526.
14.
Shah, S. P., Karaguler, M. E., and Sarigaphuti, M. ( 1992). “Effects of shrinkager-reducing admixtures on restrained shrinkage cracking of concrete.” ACI Mat. J., 89, 289–295.
15.
Trausch, J. L., and Wittmann, F. H. ( 1996). “Einfluss der Grenzfläche auf das Haftvermögen zementgebundener Beschichtungen.” Proc., 4th Int. Colloquium on Mat. Sci. and Restoration, Vol. 1, Aedificatio Verlag, Freiburg, Germany, 409–424 (in German).
16.
Wittmann, F. H. ( 1998). “Application of fracture mechanics to optimize repair systems and protective coatings for reinforced concrete structures.” Proc., FRAMCOS-3, Fracture Mech. of Concrete Struct., Vol. 3, Aedificatio Publishers, Freiburg, Germany, 1707–1714.
17.
Wittmann, F. H., and Müller, T. ( 1994). “Adherence and fracture energy.” Adherence of young on old concrete, Aedificatio Publishers, Freiburg, Germany, 97–106.
18.
Wittmann, X., Sadouki, H., and Wittmann, F. H. ( 1989). “Numerical evaluation of drying test data.” Proc., 10th Int. Conf. on Struct. Mech. in Reactor Technol., Vol. Q, 71–79.
Information & Authors
Information
Published In
History
Received: Jun 18, 1999
Published online: Apr 1, 2001
Published in print: Apr 2001
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.