Biogenic and Chemical Sulfuric Acid Corrosion of Mortars
Publication: Journal of Materials in Civil Engineering
Volume 11, Issue 4
Abstract
The biogenic corrosion of mortars by sulfuric acid-producing bacteria was simulated in a controlled breeding chamber. Calcium aluminate cement (CAC) as well as portland and blended portland cement mortars were tested. Growth conditions for bacteria were optimized in a way that accelerated the naturally occurring corrosion (worst case) by a factor of at least 24. After 12 months of incubation in the chamber the samples being tested could be clearly classified according to their resistance properties. CAC mortars were found to resist microbiologically induced corrosion significantly better than portland and blended portland cement mortars. Measurement of the amount of biogenic sulfuric acid on CAC and portland and blended portland cement mortars demonstrated a higher amount of acid on the latter. The more effective resistance of CAC mortars was explained by the higher neutralization capacity due to their chemical composition and the smaller production of biogenic acid. Chemical immersion tests in sulfuric acid at pH 2 also revealed better resistance properties for the CAC mortars. But the mortars could not be distinguished as well as in the biological test because the samples were all exposed to the same concentration of acid. It is concluded that predictions concerning the long-term behavior of mortars used in sewerage networks are only reliable on the basis of the biogenic simulation experiment because the different metabolic activities of sulfuric acid-producing bacteria inhabiting different materials should be taken into account. Chemical corrosion tests tended to overestimate the resistance properties of portland and blast furnace cement mortars.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Aldred, M. I., and Eagles, B. G. (1982). “Hydrogen sulphide corrosion of the Bagdad trunk sewerage system.” Water Pollution Control, London, 81, 80–96.
2.
Espinosa, B., Letourneux, R., and Marcdargent, S. (1996). “Acid attack of hydraulic cementbound materials: Corrosion kinetics and neutralisation capacity.” Proc., 13th Int. Corrosion Congr., Vol. 4, Australasian Corrosion Association, Clayton, Vic., 1–10.
3.
Gilchrist, F. M. C. (1953). “Microbiological studies of the corrosion of concrete sewers by sulphuric acid producing bacteria.” The South African industrial chemist, Johannesburg, South Africa, 11, 214–215.
4.
Jackson, L. G., and Studzinski, G. P. (1968). “Autoradiographic studies of the effects of inhibitors of protein synthesis on RNA synthesis in HeLa cells.” Experimental Cell Res., 52, 408–418.
5.
Maxson, T. E. (1972). “Cast-in place plastic lining protects corrosion zone in concrete sewer pipe used in Memphis Tennessee.” The American City, 87, 46–47.
6.
Milde, K., Sand, W., Wolff, W., and Bock, E. (1983). “Thiobacilli of the corroded concrete walls of the Hamburg sewer system.” J. Gen. Microbiology, London, 129, 1327–1333.
7.
Miller, F. H., Barron, W. T., and Goffigon, E. K. ( 1965). “Hydrogen sulfide can be a problem in sewers . . . The Hampton Roads Sanitation District has studied its effects and developed counter measures.” Water Works and Wastes Engrg., 45–49.
8.
Parker, C. D. (1945). “The corrosion of concrete: 2. The function of Thiobacillus concretivorus (nov. Spec.) in the corrosion of concrete exposed to atmosphere containing hydrogen sulphide.” Aust. J. Exp. Biol. and Med. Sci., 23, 91–98.
9.
Rao, G. S., and Berger, L. R. (1970). “Basis of pyruvate inhibition in Thiobacillus thiooxidans.” J. Bacteriol. Soc., 102, 462–466.
10.
Sand, W. (1987). “Importance of hydrogen sulfide, thiosulfate, and methylmercaptan for growth of thiobacilli during simulation of concrete corrosion.” Appl. Envir. Microbiology, 53, 1645–1648.
11.
Sand, W., and Bock, E. (1984). “Concrete corrosion in the Hamburg sewer system.” Envir. Technol. Letters, 5, 517–528.
12.
Sand, W., Dumas, T., and Marcdargent, S. ( 1992). “Accelerated biogenic sulfuric-acid corrosion test for evaluating the performance of calcium aluminate-based concrete in sewage applications.” ASTM Spec. Tech. Publ., 94, Vol. STP1232—Microbiologically influenced corrosion testing, ASTM, West Conshohocken, Pa., 234–249.
13.
Yoshida, N., Morinaga, T., and Murooka, Y. (1993). “Characterization and identification of bacterial strains isolated from corroded concrete in the accumulation stratum and their resistance levels to heavy metals.” J. Fermentation and Bioengineering, Osaka, Japan, 76, 400–402.
Information & Authors
Information
Published In
Journal of Materials in Civil Engineering
Volume 11 • Issue 4 • November 1999
Pages: 340 - 344
History
Received: Jan 12, 1998
Published online: Nov 1, 1999
Published in print: Nov 1999
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.