Thermomechanical Properties of Epoxy Mortars
Publication: Journal of Materials in Civil Engineering
Volume 5, Issue 2
Abstract
Three epoxy mortar materials are subjected to failure tests in compression and split‐cylinder tension over a temperature range of −35°–200°F. The tests are completed using 76.22‐mm‐ (3‐in.) diameter, 152.4‐mm‐ (6‐in.‐)long cylinders and failed specimens are examined using a microscope. Axial and radial strains are measured during the compressive tests to determine the compressive modulus and Poisson's ratio. All three mortar materials exhibit an apparent linear relationship between ultimate compressive strength and temperature. The split‐cylinder tensile test results show that tensile strength varies linearly with temperature at temperatures below the glass transition region. The compressive modulus is found to increase with decreasing temperatures. The mode of failure also varies with temperature, and microscopic examination of fracture surfaces reveals that fracture occurs at the epoxy‐aggregate interface and within the epoxy itself. Brittle failure specimens show the formation of a powdery residue on the fracture face. The testing and examination suggests that temperature has a significant effect on the ultimate strength and behavior of epoxy mortars.
Get full access to this article
View all available purchase options and get full access to this article.
References
1.
Biswas, M. (1986). “Precast bridge deck design systems.” PCI J., 31, 40.
2.
Biswas, M., Ghattas, O., and Vladmirou, H. (1985). “Fatigue and freeze‐thaw resistance of epoxy mortar.” Transp. Res. Rec. 1041, 33.
3.
Eisenhut, W. O. (1985). “The significance of the glass transition temperature in the civil engineering use of epoxy adhesives.” Proc. Committee 548, Annual Conference, Transportation Research Board.
4.
Eyring, H. (1936). “Viscosity, plasticity, and diffusion as examples of absolute reaction rates.” J. Chemical Physics, 4, 283.
5.
Kelsey, R. G., and Biswas, M. (1987). “Static and repeated load tests of polymer mortar materials.” Transp. Res. Rec. 1113, 66.
6.
Lindholm, U. S., Yeakley, L. M., and Nagy, A. (1974). “The dynamic strength and fracture properties of dresser basalt.” Int. J. Rock Mech. Min. Sci. Geomech. Abstr., 11, 181.
7.
Nutt, W. O., and Staynes, B. (1987). “The next twenty‐five years.” The Production, Performance, and Potential of Polymers in Concrete, Proc. Fifth International Congress of Polymers in Concrete, 413.
Information & Authors
Information
Published In
Copyright
Copyright © 1993 American Society of Civil Engineers.
History
Received: Apr 11, 1989
Published online: May 1, 1993
Published in print: May 1993
Authors
Metrics & Citations
Metrics
Citations
Download citation
If you have the appropriate software installed, you can download article citation data to the citation manager of your choice. Simply select your manager software from the list below and click Download.